Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Multi-effect toothpaste containing tremolite mineral elements

A technology of mineral elements and tremolite, applied in dentistry, medical science, oral care, etc., can solve the problems of dental diseases and oral diseases with ineffective effects, toothpaste damage to teeth, waste of resources, etc., and achieve the effect of preventing bacterial growth

Inactive Publication Date: 2018-02-06
广州市西瑶玉池科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Mining tremolite ore will inevitably produce a large amount of scraps, and tremolite scraps still contain active ingredients or elements that can be used, discarding tremolite scraps will cause a waste of resources
[0005] Chinese patent application (CN200610047542.X) discloses a natural jade mineral toothpaste, comprising the following components: magnesium oxide MgO, silicon dioxide SiO 2 , calcium oxide CaO, crystal water H 2 O and selenium, zinc, nickel, copper, cobalt, manganese and other trace elements composed of Xiuyu or serpentine jade or Hetian jade, Nanyang jade fine powder; this toothpaste uses natural jade health care function to replace the conventional toothpaste The abrasives, bactericides, and preservatives are safe and non-toxic, and will not produce any adverse side effects. Long-term use not only has a good cleaning and nursing effect on teeth and oral cavity, but also prevents and treats various dental diseases and oral diseases. At the same time, it can effectively provide inorganic Trace elements and mineral nutrition; but the particle size of this toothpaste jade powder is 1nm ~ 1mm, too large particle size in toothpaste is likely to damage teeth and gums, and the effect of preventing and treating various dental diseases and oral diseases is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multi-effect toothpaste containing tremolite mineral elements
  • Multi-effect toothpaste containing tremolite mineral elements
  • Multi-effect toothpaste containing tremolite mineral elements

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A multi-effect toothpaste containing tremolite mineral elements, which is composed of the following materials in parts by weight: 1 part of sodium lauryl sulfate, 0.1 part of sodium carboxymethylcellulose, 0.05 part of xanthan gum, 1 part of spices, saccharin 0.05 parts of sodium, 15 parts of glycerin, 0.05 parts of methyl paraben, 0.1 parts of allantoin, 10 parts of tremolite mineral powder, 0.2 parts of strontium carbonate, 1 part of silicon dioxide, 5 parts of calcium carbonate, glucose oxidase 0.05 parts, sodium phytate 2 parts, calcium pyrophosphate 15 parts, deionized water 50 parts.

[0021] The preparation method of the described tremolite ore powder is as follows: (1) take the leftovers of tremolite ore and grind them through a 100-mesh sieve to obtain a powder with a particle size not greater than 150 μm; (2) superfine the powder obtained in step (1) Finely pulverize to obtain a powder with a particle size not greater than 50 μm, which is tremolite ore powder....

Embodiment 2

[0025] A multi-effect toothpaste containing tremolite mineral elements, which is composed of the following substances in parts by weight: 3 parts of sodium lauryl sulfate, 0.3 parts of sodium carboxymethylcellulose, 0.15 parts of xanthan gum, 2 parts of spices, saccharin 0.2 parts of sodium, 30 parts of glycerin, 0.3 parts of methyl paraben, 0.3 parts of allantoin, 20 parts of tremolite mineral powder, 0.5 parts of strontium carbonate, 7 parts of silicon dioxide, 10 parts of calcium carbonate, glucose oxidase 0.1 parts, sodium phytate 5 parts, calcium pyrophosphate 30 parts, deionized water 30 parts.

[0026] The preparation method of the described tremolite ore powder is as follows: (1) take the leftovers of tremolite ore and grind them through a 100-mesh sieve to obtain a powder with a particle size not greater than 150 μm; (2) superfine the powder obtained in step (1) Finely pulverize to obtain a powder with a particle size not greater than 50 μm, which is tremolite ore pow...

Embodiment 3

[0030] A multi-effect toothpaste containing tremolite mineral elements, which is composed of the following materials in parts by weight: 1 part of sodium lauryl sulfate, 0.1 part of sodium carboxymethylcellulose, 0.05 part of xanthan gum, 1 part of spices, saccharin 0.05 parts of sodium, 15 parts of glycerin, 0.05 parts of methyl paraben, 0.1 parts of allantoin, 10 parts of tremolite mineral powder, 0.2 parts of strontium carbonate, 1 part of silicon dioxide, 5 parts of calcium carbonate, glucose oxidase 0.05 parts, sodium phytate 2 parts, calcium pyrophosphate 15 parts, deionized water 30 parts.

[0031] The preparation method of the described tremolite ore powder is as follows: (1) take the leftovers of tremolite ore and grind them through a 100-mesh sieve to obtain a powder with a particle size not greater than 150 μm; (2) superfine the powder obtained in step (1) Finely pulverize to obtain a powder with a particle size not greater than 50 μm, which is tremolite ore powder....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses multi-effect toothpaste containing tremolite mineral elements. The multi-effect toothpaste contains the following components: lauryl sodium sulfate, sodium carboxymethylcellulose, xanthan gum, saccharin sodium salt, methyl p-hydroxybenzoate, allantoin, tremolite mineral powder, strontium carbonate, silicon dioxide, calcium carbonate, glucose oxidase, sodium phytate, calciumpyrophosphate and deionized water. According to the multi-effect toothpaste, tremolite leftovers are secondarily utilized, and have a good inhibition effect on streptococcus mutans and porphyromonasgingivalis, and the toothpaste has an antiallergic effect; the dental plaque bacteria can be eliminated, the generation of tooth stains can be prevented, glucose attached to teeth can be removed, thebreeding of the bacteria can be prevented, teeth can be well protected, and the teeth can be well whitened after the toothpaste is used for a long time.

Description

technical field [0001] The invention relates to the field of daily chemical products, in particular to a multi-effect toothpaste containing tremolite mineral elements. Background technique [0002] Toothpaste has already become a necessity in people's daily life. With the continuous improvement of living standards, toothpaste has developed from a common tooth-cleaning type to a curative effect type, and even to a multi-effect type. At present, the additives added in multi-effect toothpaste are mostly peroxide compounds, solvent compounds or high friction value compounds, or several or more types of compounds are added at the same time. Peroxide compounds have obvious pleiotropic effects, but this type of compound is extremely unstable, and the ratio performance with other components of toothpaste is poor, which affects its use effect, and peroxide is used in the oral cavity, its safety Sex is restricted. Solvent-based additives such as polyethylene glycol have a certain ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/73A61K8/66A61K8/49A61K8/29A61K8/27A61K8/26A61K8/19A61K8/24A61K8/25A61Q11/00A61P31/02
CPCA61K8/731A61K8/19A61K8/24A61K8/25A61K8/26A61K8/27A61K8/29A61K8/4946A61K8/66A61Q11/00
Inventor 不公告发明人
Owner 广州市西瑶玉池科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com