Halogen-free flame retardant and resin alloy containing the halogen-free flame retardant

A flame retardant and halogen compound technology, which is applied in the field of halogen-free flame retardants and resin alloys containing the halogen-free flame retardants, can solve the problems of inability to meet the flame retardant grade, the influence of mechanical properties, and the small amount of addition.

Active Publication Date: 2018-07-13
励凯宏
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in order to improve the flame retardant level of the resin, more flame retardants are usually added to the resin composition to meet the requirements for the flame retardant level. However, as the amount of flame retardant added increases, the mechanical properties of the resin composition will decrease. Affected, but the amount added is too small to meet the requirements of the flame retardant grade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Halogen-free flame retardant and resin alloy containing the halogen-free flame retardant

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The invention provides a resin alloy, which is composed of the following components: 40 parts by weight of polycarbonate resin, 24 parts by weight of acrylonitrile-butadiene-styrene copolymer, 13 parts by weight of halogen-free flame retardant, 8 parts by weight of Compatibility agent and 3.6 parts by weight processing aid; Described compatibilizer is made up of following components: 42 parts by weight diene oligomers, 12 parts by weight maleic anhydride and 9 parts by weight acrylic acid; Described diene oligomers are made of 2 parts by weight of butadiene oligomers with an average relative molecular mass of 600-2000 g / mol, 3 parts by weight of pentadiene oligomers with an average relative molecular mass of 1200-3000 g / mol and 5 parts by weight of relative Molecular mass is the hexadiene oligomer composition of 2400-3600g / mol; Described processing aid comprises antioxidant, lubricant and release agent, and described antioxidant is made of 1.6 parts by weight of citric a...

Embodiment 2

[0022] The invention provides a resin alloy, which is composed of the following components: 43 parts by weight of polycarbonate resin, 20 parts by weight of acrylonitrile-butadiene-styrene copolymer, 21 parts by weight of halogen-free flame retardant, 6 parts by weight of Compatibility agent and 2.4 parts by weight processing aid; Described compatibilizer is made up of following components: 34 parts by weight diene oligomers, 16 parts by weight maleic anhydride and 3 parts by weight acrylic acid; Described diene oligomers are made of 1 part by weight of a butadiene oligomer with an average relative molecular mass of 600-2000 g / mol, 2 parts by weight of a pentadiene oligomer with an average relative molecular mass of 1200-3000 g / mol and 4 parts by weight of a relative The composition of hexadiene oligomers with a molecular mass of 2400-3600 g / mol; the composition of the processing aid is the same as that of the processing aid in Example 1.

[0023] Wherein, the halogen-free fla...

Embodiment 3

[0026] The invention provides a polyphenylene ether resin alloy, which is composed of the following components: 48 parts by weight of polycarbonate resin, 26 parts by weight of acrylonitrile-butadiene-styrene copolymer, 6 parts by weight of halogen-free flame retardant, 9 parts by weight Parts by weight compatibilizer and 2 parts by weight processing aid; Described compatibilizer is made up of following components: 48 parts by weight diene oligomers, 8 parts by weight maleic anhydride and 11 parts by weight acrylic acid; Described diene low The polymer consists of 3 parts by weight of a butadiene oligomer with an average relative molecular mass of 600-2000g / mol, 3 parts by weight of a pentadiene oligomer with an average relative molecular mass of 1200-3000g / mol and 3 parts by weight The composition of hexadiene oligomers with a weight-average relative molecular mass of 2400-3600 g / mol; the composition of the processing aid is the same as that of the processing aid in Example 1....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a halogen-free flame retardant and a resin alloy containing the halogen-free flame retardant, wherein the halogen-free flame retardant is composed of the following components in parts by weight: 1-10 parts by weight of carbon nano-tube nano-particles, 10-20 parts by weight of carboxylated carbon nano-tube nano-particles, 5-10 parts by weight of metal oxide mixture, 20-40 parts by weight of expandable graphite nano-particles and 15-30 parts by weight of phosphorus-containing halogen-free compounds. According to the halogen-free flame retardant disclosed by the invention,the flame retardancy grade of the resin is improved, and the mechanical property of the resin alloy is not reduced or not greatly reduced.

Description

technical field [0001] The invention relates to the field of resin alloys, in particular to a halogen-free flame retardant and a resin alloy containing the halogen-free flame retardant. Background technique [0002] When a fire occurs, halogen-containing flame-retardant materials will produce a large amount of smoke and toxic corrosive hydrogen halide gas during the flame-retardant process, causing secondary hazards. The new flame retardant system has a small amount of smoke when burning, and does not produce toxic and corrosive gases. Halogen-free flame retardant additives are mainly phosphorus compounds and metal hydroxides. These two types of compounds do not volatilize or produce corrosive gases when burned, and are called pollution-free flame retardants. In addition, there are several new types of halogen-free flame retardants such as silicon-based flame retardants and nitrogen-based flame retardants. These new halogen-free flame retardants have become new products th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L55/02C08K13/04C08K7/24C08K3/22C08K5/521
CPCC08K2003/222C08K2003/2227C08K2003/2241C08K2201/011C08K2201/014C08L69/00C08L2201/02C08L2201/22C08L55/02C08K13/04C08K7/24C08K3/22C08K5/521
Inventor 黄玉青
Owner 励凯宏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap