Polyurethane-based self-healing material and preparation method thereof

A composite material and polyurethane technology, applied in the field of polyurethane-based self-healing materials and their preparation, can solve the problems of difficult expansion of material application, difficulty of self-healing materials with mechanical properties and self-healing effects, etc., to increase mechanical properties performance effect

Active Publication Date: 2020-12-01
SUZHOU UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the self-healing materials obtained by these methods are usually difficult to have both high mechanical properties and excellent self-healing effects, so that the application of materials is difficult to expand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane-based self-healing material and preparation method thereof
  • Polyurethane-based self-healing material and preparation method thereof
  • Polyurethane-based self-healing material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 2

[0060] The synthesis of embodiment 1 diaminodiphenylalkyl diselenide

[0061] Take 1.23g of selenone, 1.00g of 4-aminobenzylamine and 40ml of tetrahydrofuran in a 100ml round bottom flask, stir well, and react at 40°C for 2 hours to obtain diaminodiphenylalkyl diselenide.

[0062] The reaction scheme is as follows:

[0063]

[0064] figure 1 , figure 2 The result of NMR characterization of the synthesized diaminodiphenylalkyl diselenide shows that diaminodiphenylalkyl diselenide was successfully obtained in this example.

Embodiment 2

[0065] The end group modification reaction of embodiment 2 polypropylene glycol

[0066] 1) End group modification of dihydroxypolypropylene glycol (Mn=2000g / mol)

[0067] Get 30g of dihydroxypolypropylene glycol (Shanghai McLean Biochemical Technology Co., Ltd., PPG-2000, number 2, Mn=2000g / mol) and place in a 500ml reaction bottle equipped with a mechanical stirrer, heat at 80°C for 4 hours and pump gas, dehumidify the reaction system. When the humidity of the system is less than 20%, lower the temperature to 70°C, add 6.66g of isophorone diisocyanate (No. 1) and 50mmp of catalyst dibutyltin dilaurate (DBTDL) into the reaction flask, and react in tetrahydrofuran for 60 minutes , to obtain a diisocyanate-terminated prepolymer (No. 4), and carry out infrared tracking on the whole reaction process.

[0068] The reaction scheme is as follows:

[0069]

[0070] 2) Trihydroxypolypropylene glycol (Mn=3000g / mol) end group modification

[0071] Get 30g trihydroxypolypropylene ...

Embodiment 3

[0075] The film-forming synthesis of embodiment 3 self-healing materials

[0076] Taking the molar ratio of diisocyanate-terminated prepolymer and triisocyanate-terminated prepolymer as 1:1 as an example, the preparation method of the polyurethane-based self-healing material of the present invention is as follows:

[0077] In a polytetrafluoroethylene mold, add 4 g of diisocyanate-terminated prepolymer (2 mmol, code 4), 6 g of triisocyanate-terminated prepolymer (2 mmol, code 5) and diaminodiphenylalkyl diselenide in sequence A tetrahydrofuran (20-40mL) solution of ether (2.23g, No. 9) was stirred rapidly, dried in vacuum, solvent removed, and reacted at 60°C for 24h to obtain a polyurethane-based self-healing material (No. 10 / 11). Infrared tracking of the entire reaction process.

[0078] The reaction scheme is as follows Figure 5 As shown, among the substances numbered 10 and 11 in the figure, only the specific structural formula of a part of the repeating unit is provide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of a polyurethane-based self-healing material. The preparation method comprises the following steps: reacting dihydroxypolypropylene glycol and trihydroxypolypropylene glycol with IPDI at 50-80 DEG C respectively to obtain a first isocyanate-terminated polyurethane prepolymer and a second isocyanate-terminated polyurethane prepolymer respectively; uniformly mixing the first polyurethane prepolymer, the second polyurethane prepolymer and diaminodiphenylalkyl diselenide, then reacting at 50-70 DEG C to obtain the polyurethane-based self-healing material. The invention further provides the polyurethane-based self-healing material prepared by the preparation method. the polyurethane-based self-healing material adopts a structural formula as follows: FORMULA. By virtue of rapid and efficient exchange between Se-Se dynamic covalent bonds, a material capable of achieving 100% healing efficiency in a short time and at room temperature is prepared;in addition, a urea group is also introduced into the material, so that mechanical properties of the material are improved.

Description

technical field [0001] The invention relates to the technical field of material preparation, in particular to a polyurethane-based self-healing material and a preparation method thereof. Background technique [0002] In the 1980s, Jud and others proposed the concept of self-healing materials, that is, using the self-sensing ability of materials to respond to micro-cracks in materials, and then trigger self-healing to restore their mechanical properties and prolong their service life. At present, self-healing materials have been applied in many fields such as aerospace, electronics, and construction. As a new class of self-healing materials, polymer-based self-healing materials have received much attention from the scientific community, and many research progresses have been made. [0003] Due to the influence of thermal, mechanical and chemical factors, polymer materials will produce cracks during application, which will affect their service life and mechanical properties. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/12C08G18/32C08L75/08
CPCC08G18/12C08G18/4812C08G18/4825C08G18/4829C08G18/6685C08L75/08C08G18/3897
Inventor 朱健钱玉清李娜潘向强朱秀林
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap