A kind of antibacterial magnesium alloy

An antibacterial magnesium and alloy technology, applied in the field of magnesium alloy biomedical material preparation, to achieve the effect of avoiding cell or tissue infection, high purity, and uniform composition and tissue

Active Publication Date: 2021-01-01
NORTHEASTERN UNIV LIAONING
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Magnesium and magnesium alloys have great potential and advantages as a new class of medical implant materials, but the research on the antibacterial properties of magnesium alloys needs further exploration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial magnesium alloy
  • A kind of antibacterial magnesium alloy
  • A kind of antibacterial magnesium alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0038] The chemical composition of an antibacterial magnesium alloy is: Zn: 5-6wt.%, Zr: 0.3-0.9wt.%, Ag: 1.5-15.0wt.%, Cu: 2.0-4.0wt.%, the balance It is Mg and unavoidable impurities.

[0039] A kind of preparation method of antibacterial magnesium alloy, concrete steps are as follows:

[0040] Step 1, weigh:

[0041] As shown in table 1, take industrial pure magnesium, industrial pure zinc, Mg-Zn-Zr master alloy, Mg-Cu master alloy, Mg-Ag master alloy according to the chemical composition ratio of novel antibacterial magnesium alloy;

[0042] Step 2, preheating, (a), (b) in no order:

[0043] (a) Place the weighed industrial pure magnesium, industrial pure zinc, Mg-Zn-Zr master alloy, Mg-Cu master alloy, and Mg-Ag master alloy in a vacuum drying oven, dry and preheat at 200°C for 20min,

[0044] (b) Place the weighed industrially pure zinc in a vacuum oven, dry and preheat at 120°C for 20 minutes;

[0045] Step 3, smelting:

[0046] Industrial pure magnesium is smelted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses antibacterial magnesium alloy, and belongs to the field of preparation of magnesium alloy biomedical materials. The magnesium alloy comprises the following chemical componentsin percentage by weight: 5 to 6 wt.% of Zn, 0.3 to 0.9 wt.% of Zr, 1.5 to 15.0 wt.% of Ag, 2.0 to 4.0 wt.% of Cu, and the balance of Mg and inevitable impurities. The magnesium alloy has higher strength and corrosion resistance on the promise of maintaining good biocompatibility and biodegradability. Through the optimization of component design of the magnesium alloy and adding of Ag and Cu elements, the magnesium alloy gives antibacterial activity to magnesium alloy implantable devices, effectively avoids the occurrence of infection of peripheral cell or tissue of an implant, and obviously improves the success rate and prognosis effect of implantation treatment.

Description

technical field [0001] The invention belongs to the field of magnesium alloy biomedical material preparation, in particular to an antibacterial magnesium alloy. Background technique [0002] With the continuous development of high-tech science and technology, because of the good mechanical properties, good biocompatibility and degradability of magnesium alloy, it is more and more favored by the biomedical field, especially for the manufacture of internal implants. aroused widespread concern. Magnesium alloy is a high-performance light-weight structural material made of magnesium. Its specific gravity is similar to that of plastic, and its rigidity and strength are no less than aluminum. It has strong shock resistance, anti-electromagnetic, thermal conductivity, and electrical conductivity. create pollution. Using magnesium alloy as raw material to produce implants has many advantages. For example, the density of magnesium is about 1.74g / cm3, which is equivalent to the bone...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/04C22C1/03C22C1/06C22F1/06
CPCC22C1/03C22C1/06C22C23/04C22F1/06
Inventor 铁镝任浩博颜路飞管仁国李洪超赵阳
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap