High-and-low-temperature-resistant wire harness sheathing material of new energy automobile and preparation method of high-and-low-temperature-resistant wire harness sheathing material

A new energy vehicle, high and low temperature resistant technology, applied in the direction of plastic/resin/wax insulators, organic insulators, electrical components, etc., can solve the problems of weak high and low temperature resistance, poor stability, easy aging of wire harness protective sleeves, etc., to achieve material The effect of excellent performance and stable material performance

Inactive Publication Date: 2018-10-26
WUHU EXCELLENCE WIRE HARNESS SYST
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing wire harness protective cover is easy to age, has weak high and low temperature resi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-and-low-temperature-resistant wire harness sheathing material of new energy automobile and preparation method of high-and-low-temperature-resistant wire harness sheathing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A new energy vehicle high and low temperature resistant wire harness sheath material, which is composed of the following raw materials in parts by weight: 40 parts of thermosetting liquid polyimide pure resin, 32 parts of EVA resin, 12 parts of polytetrafluoroethylene, and temperature-resistant compound modification 5 parts of agent, 8 parts of superfine activated calcium carbonate, 4 parts of diisononyl phthalate, 3 parts of lubricant, 0.7 part of antioxidant; Wherein, the preparation steps of temperature-resistant composite modifier are as follows:

[0015] In parts by weight, weigh 3 parts of sodium lignosulfonate, 4 parts of Al 2 o 3 / Mo 5 Si 3 Composite powder, 1.5 parts of expanded graphite, 7 parts of ultra-high molecular weight polyethylene and 6 parts of silane coupling agent KH-570 are placed in a grinder for 5 hours and then taken out, and then the taken out mixture is placed in a vacuum drying oven at 80°C Drying under high temperature for 10 hours to obt...

Embodiment 2

[0022] A new energy vehicle high and low temperature resistant wire harness sheath material, which is composed of the following raw materials in parts by weight: 45 parts of thermosetting liquid polyimide pure resin, 32 parts of EVA resin, 13 parts of polytetrafluoroethylene, and temperature-resistant compound modification 6 parts of agent, 8 parts of superfine activated calcium carbonate, 4 parts of diisononyl phthalate, 4 parts of lubricant, 0.9 part of antioxidant; Wherein, the preparation steps of temperature-resistant composite modifier are as follows:

[0023] In parts by weight, weigh 3 parts of sodium lignosulfonate, 4 parts of Al 2 o 3 / Mo 5 Si 3 Composite powder, 1.5 parts of expanded graphite, 7 parts of ultra-high molecular weight polyethylene and 6 parts of silane coupling agent KH-570 are placed in a grinder for 5 hours and then taken out, and then the taken out mixture is placed in a vacuum drying oven at 80°C Drying under high temperature for 10 hours to obt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of wire harness sheathing materials, and particularly discloses a high-and-low-temperature-resistant wire harness sheathing material of a new energy automobile. Thehigh-and-low-temperature-resistant wire harness sheathing material of the new energy automobile comprises the following components: 30-45 parts of thermosetting liquid polyimide pure resin, 20-35 parts of EVA resin, 10-15 parts of polytetrafluoroethylene, 4-6 parts of a temperature-resistant compound modifying agent, 6-10 parts of ultra-fine activated calcium carbonate, 3-5 parts of diisononyl phthalate, 2-4 parts of a lubricating agent and 0.5-0.9 part of an antioxidant. The thermosetting liquid polyimide pure resin, the EVA resin and the like are used as matrixes, the matrixes have properties of weather resistance, temperature resistance, wear resistance, corrosion resistance and the like, and then are compounded with the temperature-resistant compound modifying agent and the like, and thus, the properties (such as wear resistance, impact resistance, weather resistance, temperature resistance and corrosion resistance) of the prepared material are excellent.

Description

technical field [0001] The invention belongs to the field of new energy automobile spare parts, and in particular relates to a new energy automobile high and low temperature resistant wire harness sheath material and a preparation method thereof. Background technique [0002] The automobile wiring harness is the main body of the automobile circuit network, and there is no automobile circuit without the wiring harness. The wire harness refers to the contact terminal (connector) punched from copper and the wire and cable after crimping, and then plastic insulator or metal shell on the outside, and then bundled with wire harness to form a connected circuit component. The wire harness industry chain includes wire and cable, connectors, processing equipment, wire harness manufacturing and downstream application industries. Wire harnesses are widely used and can be used in automobiles, household appliances, computers and communication equipment, and various electronic instruments ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L79/08C08L23/08C08L27/18C08L97/00C08L23/06C08L83/04C08K13/06C08K9/06C08K7/24C08K3/22C08K3/26C08K5/12H01B3/30
CPCC08K2003/2227C08K2003/265C08L79/08C08L2201/08C08L2203/202C08L2205/035C08L2207/068H01B3/302C08L23/0853C08L27/18C08L97/005C08L23/06C08L83/04C08K13/06C08K9/06C08K7/24C08K3/22C08K3/26C08K5/12
Inventor 嵇存雄
Owner WUHU EXCELLENCE WIRE HARNESS SYST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap