A kind of carbon/carbon composite honeycomb and preparation method thereof

A carbon composite material and honeycomb technology, which is applied in ceramic products, other household appliances, household appliances, etc., can solve the problems of unfavorable lightweight requirements in the aerospace field, poor thermal stability, etc., and achieve excellent densification process adaptability and densification cycle The effect of short and simple process

Active Publication Date: 2021-07-13
AEROSPACE RES INST OF MATERIAL & PROCESSING TECH +1
View PDF30 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, carbon / carbon composite blocks, carbon / silicon carbide composite blocks or carbon fiber reinforced resin-based honeycombs are usually used in the domestic aerospace field as the supporting structure of precision instruments to maintain good stability; due to carbon / carbon composite block or carbon / silicon carbide composite block are all solid structures, which is not conducive to the lightweight requirements of the aerospace field; the carbon fiber reinforced resin-based honeycomb thermal expansion system is about 10 -4 magnitude, poor thermal stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of carbon/carbon composite honeycomb and preparation method thereof
  • A kind of carbon/carbon composite honeycomb and preparation method thereof
  • A kind of carbon/carbon composite honeycomb and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The embodiment of the present invention also provides a method for preparing a carbon / carbon composite material honeycomb, comprising the following steps:

[0040] Step 1, preparing a carbon fiber reinforced body of a honeycomb structure, in which the L direction has continuous carbon fibers, and the W direction also has continuous carbon fibers;

[0041] Specifically, in the embodiment of the present invention, the L-direction and W-direction of the carbon fiber reinforced body honeycomb structure can be realized to have continuous fibers by splicing and sewing carbon cloth, specifically, as figure 2 As shown, first cut the carbon cloth m into a predetermined shape according to the size of the honeycomb design and mark the position that needs to be stitched. Insert the mandrel at the seam, and release the mold after solidifying the dimension shape, you can get the following figure 2 The honeycomb structure shown;

[0042] The carbon matrix includes resin carbon forme...

Embodiment 1

[0053] This embodiment provides a carbon / carbon composite material honeycomb for satellites with an outline size of 200mm×200mm×80mm, a honeycomb cell side length of 5mm, and a honeycomb wall thickness of 0.8mm. The preparation method includes:

[0054] 1) Use general-purpose T300-3K polyacrylonitrile-based carbon fiber to weave to an area density of 240g / cm 3 Plain carbon cloth, warp and weft density 6 threads / cm×6 threads / cm. Then cut the carbon cloth into carbon cloth blocks of a certain specification according to the expanded size of the honeycomb wall; during the cutting process, the warp yarn direction is 0°, rotate counterclockwise to form +45° carbon cloth, and rotate clockwise to form -45° carbon cloth.

[0055] 2) Lay the carbon cloth blocks in step 1) according to the designed layering sequence, and arrange the adjacent carbon cloths in the order of +45 / -45 layering; stitch the carbon cloths in pairs, and stitch the spacing in the thickness direction of the honeyco...

Embodiment 2

[0061] This embodiment provides a carbon / carbon composite material honeycomb with an outline size of 400mm×400mm×80mm, a honeycomb cell side length of 5mm, and a honeycomb wall thickness of 0.8mm. The preparation method includes:

[0062] 1) Use general-purpose T300-3K polyacrylonitrile-based carbon fiber to weave to an area density of 240g / cm 3 Plain carbon cloth, warp and weft density 6 threads / cm×6 threads / cm. Then cut the carbon cloth into carbon cloth blocks of a certain specification according to the expanded size of the honeycomb wall; during the cutting process, the warp yarn direction is 0°, rotate counterclockwise to form +45° carbon cloth, and rotate clockwise to form -45° carbon cloth.

[0063] 2) Lay the carbon cloth blocks in step 1) according to the designed layering sequence, and arrange the adjacent carbon cloths in the order of +45 / -45 layering; stitch the carbon cloths in pairs, and stitch the spacing in the thickness direction of the honeycomb 4mm, the st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flat compressive strengthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

A carbon / carbon composite material honeycomb and a preparation method thereof belong to the technical field of carbon / carbon composite materials. The carbon / carbon composite material honeycomb includes a carbon fiber reinforcement and a carbon matrix covering the surface of the carbon fiber reinforcement, wherein the carbon fiber reinforcement is a honeycomb structure, and the honeycomb structure has continuous carbon fibers in the L direction, and the W direction Also has continuous carbon fiber. The carbon / carbon composite material honeycomb of the present invention has excellent thermal stability and mechanical properties, and meets the lightweight requirements of the aerospace field; the main performance parameters of the honeycomb meet the requirements of flat compressive strength ≥ 8MPa, flat compressive modulus ≥ 900MPa, and L-direction shear strength ≥6.7MPa, L-direction shear modulus ≥1500MPa, W-direction shear strength ≥4.5MPa, W-direction shear modulus ≥730MPa, thermal expansion coefficient 0~0.2×10 ‑6 / K.

Description

technical field [0001] This patent relates to a low-density, high-stability, high-strength integral carbon / carbon composite material honeycomb for a high-precision observation platform, which belongs to the technical field of carbon / carbon composite materials. Background technique [0002] Traditional composite materials for spacecraft structures generally only require high specific strength, high specific modulus, etc., and do not have high requirements for dimensional stability. However, in the field of research and development of composite material structures for high-precision spacecraft such as satellites, composite materials with high stability, light weight, and high strength are an important development direction. Advanced countries have begun to study zero-expansion, high-stability composite material structures for spacecraft, which are mainly used for supporting structures of optical instruments such as space telescopes, supporting bases for gravity gradiometers, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/83C04B35/622C04B38/00C04B35/84
CPCC04B35/622C04B35/83C04B38/0009C04B2235/96C04B38/0067
Inventor 张中伟刘宇峰许正辉李同起俸翔
Owner AEROSPACE RES INST OF MATERIAL & PROCESSING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More