A battery electrolyte and a lithium ion battery containing the electrolyte

An electrolyte and battery technology, which is applied in the field of lithium-ion batteries, can solve the problems of reducing the constant current charging ratio and capacity of the battery, consuming hydrofluoric acid, and increasing the internal resistance of the battery, so as to improve high-temperature cycle performance and high-temperature cycle performance , the effect of suppressing flatulence

Active Publication Date: 2019-01-04
HEFEI GUOXUAN HIGH TECH POWER ENERGY
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of acid anhydride additives also significantly increases the internal resistance of the battery, reduces the constant current charging ratio and capacity of the battery, and is not conducive to the improvement of the energy density of the battery.
The silane additives can cooperate with hydrofluoric acid, consume hydrofluoric acid, and block the continuous occurrence of subsequent side reactions, so they have better functions of removing water and acid, thereby improving the cycle performance of the battery, but the silane additives There is no obvious improvement effect on the problem of flatulence of the battery at high temperature

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A battery electrolyte and a lithium ion battery containing the electrolyte
  • A battery electrolyte and a lithium ion battery containing the electrolyte
  • A battery electrolyte and a lithium ion battery containing the electrolyte

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] In a glove box filled with argon, based on the total mass of the battery electrolyte, the mass fraction of 12.0% LiPF was weighed 6 Dissolved in an organic solvent with a mass fraction of 87%, wherein the organic solvent is a mixed solvent of ethylene carbonate: diethyl carbonate: ethyl methyl carbonate=3:2:5 (w / w / w), and then The film-forming additive ethylene carbonate with a mass fraction of 0.5% and the additive A with a mass fraction of 0.5% were added thereto, and the electrolyte solution 1 was obtained after stirring evenly.

Embodiment 2

[0030] In a glove box filled with argon, based on the total mass of the battery electrolyte, the mass fraction of 12.0% LiPF was weighed 6 Dissolved in an organic solvent with a mass fraction of 87%, wherein the organic solvent is a mixed solvent of ethylene carbonate: diethyl carbonate: ethyl methyl carbonate=3:2:5 (w / w / w), and then The film-forming additive ethylene carbonate with a mass fraction of 0.5% and the additive B with a mass fraction of 0.5% were added thereto, and the electrolyte solution 2 was obtained after stirring evenly.

Embodiment 3

[0032] In a glove box filled with argon, based on the total mass of the battery electrolyte, the mass fraction of 12.0% LiPF was weighed 6 Dissolved in an organic solvent with a mass fraction of 87%, wherein the organic solvent is a mixed solvent of ethylene carbonate: diethyl carbonate: ethyl methyl carbonate=3:2:5 (w / w / w), and then Add film-forming additive ethylene carbonate with a mass fraction of 0.5% and additive C with a mass fraction of 0.5% to it, and stir to obtain electrolyte 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A battery electrolyte A lithium ion battery containing the electrolyte is also disclosed, As that acid anhydride derivative additive is added into the battery electrolyte, At the same time, the acid anhydride derivative additive contains O, N, Si, F and has good compatibility with the positive and negative electrode materials when it is used as the electrolyte additive, which can effectively inhibit the gas expansion of the battery and improve the high-temperature cycling performance of the battery.

Description

technical field [0001] The invention belongs to the technical field of lithium ion batteries, in particular to a battery electrolyte, and also to a lithium ion battery containing the electrolyte. Background technique [0002] Since Sony commercialized lithium-ion batteries in 1991, they have been widely used in electronic products such as mobile phones, cameras and notebook computers due to their advantages of high energy density, long cycle life and low environmental pollution. With the rapid development of the field of new energy vehicles, people have put forward higher requirements for the safety performance and energy density of lithium-ion batteries. However, under high temperature and high pressure, the battery's flatulence and rapid degradation of cycle performance severely limit its wider use. . [0003] In order to solve the gas problem of batteries, acid anhydride additives are widely used. This is because the acid anhydride additive can neutralize the alkalinity...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0567H01M10/0525
CPCH01M10/0525H01M10/0567H01M2300/0025Y02E60/10
Inventor 刘娟娟俞金萍沈剑梁大宇
Owner HEFEI GUOXUAN HIGH TECH POWER ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products