A method for changing the glossiness of film surface
A technology of surface gloss and gloss, applied in the direction of coating, etc., can solve the problems of troublesome way of adjusting the formula and the decline of film performance.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0013] A method for changing the surface gloss of a film. The film is prepared by a casting process. In the operation step of casting a film, a silicone pressure roller is added before the active casting roller, and the distance between the silicone pressure roller and the active casting roller is 2mm, when the air pressure is 0.2MPa, the glossiness of the film is 15; when the air pressure is 0.2MPa, and the distance between the silicone pressure roller and the active casting roller is 4mm, the glossiness of the film is 25.
Embodiment 2
[0015] A method for changing the surface gloss of a film. The film is prepared by a casting process. In the operation step of casting a film, a silicone pressure roller is added before the active casting roller, and the distance between the silicone pressure roller and the active casting roller is 2mm, when the air pressure is 0.1MPa, the glossiness of the film is 10; when the air pressure is 0.2MPa, and the distance between the silicone pressure roller and the active casting roller is 3mm, the glossiness of the film is 20.
Embodiment 3
[0017] A method for changing the surface gloss of a film. The film is prepared by a casting process. In the operation step of casting a film, a silicone pressure roller is added before the active casting roller, and the distance between the silicone pressure roller and the active casting roller is 2mm, the air pressure is 0.4MPa, and the gloss of the film is 18; when the air pressure is 0.3MPa, and the distance between the silicone pressure roller and the active casting roller is 4mm, the gloss of the film is 28.
[0018] The formula of the casting film that following embodiment adopts is made up of the component of following parts by weight: 35 parts of polyterephthalic acid-adipate-butylene glycol ester, 8 parts of polytetrafluoroethylene, 1 part of montmorillonite .
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com