Method for reinforcing conductive carbon paper, and hydrolysis-resistant conductive carbon paper prepared therethrough

A technology of strengthening treatment and conductive carbon, which is used in fiber raw material treatment, synthetic cellulose/non-cellulose material pulp/paper, papermaking, etc. The effect of high bonding strength, increased tear strength and improved tear strength

Active Publication Date: 2019-02-01
贵州朝日供暖科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problems that the existing conductive paper has improved tear strength, but poor water resistance and low moisture absorption, it is not conducive to use on the ground or in a humid environment, the service life is reduced, and the conductive performance is affected. A conductive paper is provided. Strengthening treatment method of carbon paper and hydrolysis-resistant conductive carbon paper prepared therefrom

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: a kind of strengthening treatment method of conductive carbon paper, comprises the steps:

[0019] (1) Preparation of conductive paper by wet forming: Fully disperse pure wood pulp and carbon fiber with 15% weight of pure wood pulp in water, copy it into paper, dry to obtain conductive paper, and control the resistance of the conductive paper to 15Ω / m 2 ;

[0020] (2) Preparation of polyvinyl alcohol latex: 55 parts of polyvinyl alcohol as the main binder, 8 parts of sodium dichromate as a curing agent, 10 parts of rosin and 10 parts of gelatin as a thickener, 10 parts of glycerin as a softener, 2 1 part formaldehyde is used as antiseptic, adds clear water 1000g, is prepared into polyvinyl alcohol latex;

[0021] (3) Reinforced conductive carbon paper: The polyvinyl alcohol latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:1, and then the mixed glue solution is sprayed on the conductive paper prepared in step (1) , le...

Embodiment 2

[0027] Embodiment 2: a kind of strengthening treatment method of conductive carbon paper, comprises the steps:

[0028] (1) Preparation of conductive paper by wet forming: Fully disperse pure wood pulp and carbon fiber with 10% weight of pure wood pulp in water, copy it into paper, dry to obtain conductive paper, and control the resistance of the conductive paper to 50Ω / m 2 ;

[0029] (2) Preparation of polyvinyl alcohol latex: 50 parts of polyvinyl alcohol as the main adhesive, 5 parts of sodium dichromate as a curing agent, 5 parts of rosin and 5 parts of gelatin as a thickener, 20 parts of glycerin as a softener, 1 1 part formaldehyde is used as antiseptic, adds clear water 1000g, is prepared into polyvinyl alcohol latex;

[0030] (3) Enhanced conductive carbon paper: The polyvinyl alcohol latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:5, and then the mixed glue solution is sprayed on the conductive paper prepared in step (1) , let ...

Embodiment 3

[0035] Embodiment 3: a kind of strengthening treatment method of conductive carbon paper, comprises the steps:

[0036] (1) Preparation of conductive paper by wet forming: fully disperse pure wood pulp and carbon fiber with a weight of 2.5% of pure wood pulp in water, copy it into paper, and dry it to obtain conductive paper. Control the resistance of the conductive paper to 100Ω / m 2 ;

[0037] (2) Preparation of polyvinyl alcohol latex: 60 parts of polyvinyl alcohol as the main adhesive, 20 parts of sodium dichromate as a curing agent, 15 parts of rosin and 15 parts of gelatin as a thickener, 30 parts of glycerin as a softener, 3 1 part formaldehyde is used as antiseptic, adds clear water 1000g, is prepared into polyvinyl alcohol latex;

[0038] (3) Enhanced conductive carbon paper: The polyvinyl alcohol latex prepared in step (2) is mixed with water evenly according to the glue ratio of 1:10, and then the mixed glue solution is sprayed on the conductive paper prepared in st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of conductive material manufacturing, and provides a method for reinforcing conductive carbon paper, and a hydrolysis-resistant conductive carbon paper prepared therethrough in order to solve a problem that poor waterproof property and low moisture absorption property of existing conductive papers even having improved tear strength are bad for the use of the existing conductive papers on the ground or in a humid environment, shorten the life and affect the electrical conduction property. The method comprises the following steps: wet molding of a conductive paper, preparation of a polyvinyl alcohol latex, and reinforcing the polyvinyl alcohol latex with the conductive paper. The temperature of the conductive carbon paper can be easily controlled,the temperature resistance is improved, the lowest temperature reaches 50 DEG C or above, and the application field of the conductive carbon paper is broadened. The improvement of the hydrolysis resistance of the conductive paper makes the product have the advantages of good waterproof property, good flame retardant property and small occupied space and realize large-area low temperature radiantheat. The paper can be wound freely, can be easily pasted and compounded on a wall and a flat utensil, and is compounded in a wood floor to form a self-heating composite floor, is moisture-proof and waterproof, and can be used in a water immersion or humid environment.

Description

technical field [0001] The invention belongs to the technical field of conductive material production, and in particular relates to a method for strengthening conductive carbon paper and the prepared hydrolysis-resistant conductive carbon paper. Background technique [0002] Conductive paper is a kind of conductive functional paper, which can be widely used in anti-static packaging, electromagnetic shielding, surface heating, heat-resistant and flame-retardant, new energy, electrochemistry, biomedicine and other materials. Carbon fiber conductive paper is obtained by fully dispersing carbon fiber and other fibers or powder materials in a solvent, and drying them into paper. In order to make the fibers interweave more fully, organic compounds such as polyvinyl alcohol, polyimide or styrene-butadiene latex and cationic reinforcing agents are usually added to increase the bonding force between fibers; The content can also be adjusted within a wide range. Carbon fiber conducti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/20D21H13/50
CPCD21H13/50D21H19/20
Inventor 程学礼何建宇
Owner 贵州朝日供暖科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com