A kind of energy storage seam welding welding method of metal wire mesh

A wire mesh and welding method technology, which is applied in energy storage discharge welding, welding equipment, welding power supply, etc., can solve the problems of scrapped parts, easy burn-through, and less than 50% pass rate, so as to improve welding efficiency and avoid Welding burn-through and burns, the effect of improving productivity

Active Publication Date: 2021-02-19
AECC AVIATION POWER CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In actual work, it is found that using the energy storage welding welding method for welding is very prone to burn-through during the positioning welding and welding process of parts, which will lead to a large number of scrapped parts, and the pass rate is less than 50%.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of energy storage seam welding welding method of metal wire mesh

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0027] In order to enable those skilled in the art to better understand the solutions of the present invention, the following will clearly and completely describe the technical solutions in the embodiments of the present invention in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments are only It is an embodiment of a part of the present invention, but not all embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts shall fall within the protection scope of the present invention.

[0028] It should be noted that the terms "first" and "second" in the description and claims of the present invention and the above drawings are used to distinguish similar objects, but not necessarily used to describe a specific sequence or sequence. It is to be understood that the data so used are interchangeable under appropriate ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a welding method for energy storage seam welding of wire mesh, which comprises step 1: cleaning the parts to be welded, selecting a test piece to carry out positioning welding trial welding, energy storage seam welding trial welding and tearing test, and determining the positioning welding Welding parameters and welding parameters of energy storage seam welding; step 2: assemble the parts to be welded and check whether the overlap is qualified, and then perform tack welding on the parts to be welded with qualified overlap according to the welding parameters of tack welding; step 3: put The parts to be welded after tack welding are performed energy storage seam welding according to the welding parameters of energy storage seam welding. Energy storage positioning welding and energy storage seam welding are carried out through the process route and process parameters determined by the process test of the present invention. The welding quality is reliable, the appearance of the weld seam is beautiful, a large number of welding burn-through and burn phenomena are avoided, and the qualified rate of parts is less than 50%. % has increased to more than 90%, and the welding efficiency has increased by 3 times.

Description

technical field [0001] The invention belongs to the field of welding technology, and relates to an energy storage seam welding method for wire mesh. Background technique [0002] The current fuel nozzle adopts a two-stage oil filter, and the filter screen of the auxiliary oil filter adopts an ultra-thin wire mesh welded structure. The wire mesh weaving method is flat mesh weaving square hole mesh, the precision grade is A grade, the basic size of the mesh and the diameter of the wire are very small, both within the range of a few tenths of a millimeter. [0003] The welding method of this part is energy storage lap seam welding. The lap width, the diameter of the welded part, the width of the weld, and the length of the weld are all at the millimeter level. At the same time, because the thickness of the part is very thin, it is only 0.1mm. In actual work, it is found that using the energy storage welding welding method for welding is very prone to burn-through during the po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B23K11/08B23K11/00B23K11/26B23K11/36
CPCB23K11/00B23K11/002B23K11/08B23K11/26B23K11/36
Inventor 周卫涛申健邢泽生胡斌苟浩洲邵志宏赵海任建勇
Owner AECC AVIATION POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap