Bamboo carbon fiber fly-knitted vamp

A bamboo charcoal fiber and flying weaving technology, which is applied in the field of bamboo charcoal fiber flying weaving shoe uppers, can solve the problems of discomfort, airtightness, unhealthy, etc., and achieve the effect of comfortable wearing, good air permeability and cool wearing

Inactive Publication Date: 2019-05-10
东莞市喜宝体育用品科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The common practice of flying woven shoes produced by ordinary high-elasticity and low-elasticity shoe materials in the current market will lead to: 1. Airtight; 2. Unhealthy; 3. Not environmentally friendly; 4. Uncomfortable; Psychology and Physiology of Consumers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo carbon fiber fly-knitted vamp
  • Bamboo carbon fiber fly-knitted vamp
  • Bamboo carbon fiber fly-knitted vamp

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A bamboo charcoal fiber flying woven shoe upper is woven from bamboo charcoal fiber.

[0026] Wherein, the bamboo charcoal fiber is SORONA fiber.

[0027] Wherein, the fly-woven shoe upper is coated with a waterproof and breathable coating, and the waterproof and breathable coating is coated with a water-based UV coating, and the water-based UV coating includes the following raw materials in parts by weight:

[0028]

[0029]

[0030] Wherein, the polyurethane nanofiber is prepared by the following method:

[0031] A. Mix 25 parts by weight of castor oil, 6 parts by weight of glycerin and 0.2 parts by weight of triethanolamine, heat up to 210° C. for alcoholysis reaction for 2.5 hours, cool to obtain alcoholylated castor oil;

[0032] B. Mix alcoholyzed castor oil, 55 parts by weight of isophorone diisocyanate and 100 parts by weight of N,N-dimethylacetamide, heat up to 60° C. and react for 2.5 hours to obtain a spinning solution;

[0033] C. Electrospinning the...

Embodiment 2

[0042] A bamboo charcoal fiber flying woven shoe upper is woven from bamboo charcoal fiber.

[0043] Wherein, the bamboo charcoal fiber is SORONA fiber.

[0044] Wherein, the flying woven shoe upper is coated with a waterproof and breathable coating, and the waterproof and breathable coating is coated with a water-based UV coating, and the water-based UV coating includes the following raw materials in parts by weight:

[0045]

[0046]

[0047] Wherein, the polyurethane nanofiber is prepared by the following method:

[0048] A. Mix 20 parts by weight of castor oil, 4 parts by weight of glycerin and 0.1 parts by weight of triethanolamine, heat up to 200° C. for alcoholysis reaction for 2 hours, and cool to obtain alcoholylated castor oil;

[0049] B. Mix alcoholyzed castor oil, 50 parts by weight of isophorone diisocyanate and 100 parts by weight of N,N-dimethylacetamide, heat up to 50° C. and react for 2 hours to obtain a spinning solution;

[0050] C. Electrospinning ...

Embodiment 3

[0059] A bamboo charcoal fiber flying woven shoe upper is woven from bamboo charcoal fiber.

[0060] Wherein, the bamboo charcoal fiber is SORONA fiber.

[0061] Wherein, the flying woven shoe upper is coated with a waterproof and breathable coating, and the waterproof and breathable coating is coated with a water-based UV coating, and the water-based UV coating includes the following raw materials in parts by weight:

[0062]

[0063] Wherein, the polyurethane nanofiber is prepared by the following method:

[0064] A. Mix 30 parts by weight of castor oil, 8 parts by weight of glycerin and 0.3 parts by weight of triethanolamine, heat up to 220° C. for alcoholysis reaction for 3 hours, and cool to obtain alcoholylated castor oil;

[0065] B. Mix alcoholyzed castor oil, 60 parts by weight of isophorone diisocyanate and 100 parts by weight of N,N-dimethylacetamide, heat up to 70° C. and react for 3 hours to obtain a spinning solution;

[0066] C. Electrospinning the spinning s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of fly-knitted vamps and particularly relates to a bamboo carbon fiber fly-knitted vamp knitted by virtue of bamboo carbon fibers. The bamboo carbon fibershave the characteristics of good air permeability, instant water-absorbing property, relatively strong wear resistance, winter warmness, summer coolness and the like, further have a series of functional characteristics of natural antibacterial property, bacteriostatic property, mite removal property, deodorization property and ultraviolet resistance and are applied to the fly-knitted vamps, the fly-knitted vamps can be dry, comfortable, air-permeable, healthy and odor-free when being worn in outdoor hot weather, are cool and comfortable when being worn in winter, are warm in winter and cool in summer and can meet the mental and wearing comfortable feels of customers. The fly-knitted vamps have great market superiorities and breakthrough effects.

Description

technical field [0001] The invention relates to the technical field of fly-woven shoe uppers, in particular to a bamboo charcoal fiber fly-woven shoe upper. Background technique [0002] The common practice of flying woven shoes produced by ordinary high-elasticity and low-elasticity shoe materials in the current market will lead to: 1. Airtight; 2. Unhealthy; 3. Not environmentally friendly; 4. Uncomfortable; Psychology and physiology of consumers. For example, a flying woven upper can have the characteristics of moisture absorption and perspiration, antibacterial and antibacterial, deodorizing, anti-ultraviolet, warm in winter and cool in summer, green and environmental protection, and can directly or indirectly participate in its physiological functions, which is beneficial to health and can satisfy customers. Psychological and physical needs, that will be a breakthrough in the development of Feizhi shoe materials, and it will be a huge breakthrough in the market. Cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/04D01F6/70
Inventor 吴惠冲罗泽满陈敏
Owner 东莞市喜宝体育用品科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap