A kind of preparation method of uniform structure tnm alloy forging billet

A technology with uniform structure and forging billet, which is applied in metal processing equipment, manufacturing tools, heating/cooling equipment, etc., can solve the problems of rough structure of forging billet, high forging temperature, increase of forging billet preparation cost, etc., and achieve low forging temperature. , Improve the uniformity of the organization and avoid the effect of cracking

Active Publication Date: 2020-11-03
NORTHWESTERN POLYTECHNICAL UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the literature search that although TiAl alloy forging blanks with uniform structure have been obtained by forging, the forging temperature is relatively high, which will not only increase the preparation cost of forging blanks, but also make the structure of forging blanks coarser.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of uniform structure tnm alloy forging billet
  • A kind of preparation method of uniform structure tnm alloy forging billet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment is a method for preparing a TNM alloy forging billet with uniform structure.

[0035] The nominal composition of the TNM alloy described in this implementation example is Ti-43Al-4Nb-1Mo-0.2B, the composition is atomic percentage, and the size of the ingot used is Φ73×99 mm.

[0036] The specific process of this embodiment is as follows:

[0037] The first step is preparation before forging. The ingot to be die-cast is a cylindrical sample, and the surface of the ingot to be die-cast is polished to ensure that the surface quality is good and free of defects. Ultrasonic flaw detection is used to confirm that there is no crack inside the ingot, and the surface of the ingot is evenly coated with Y 2 o 3 slurry to avoid surface oxidation of the ingot. After the coating is air-dried, the ingot to be die-cast is wrapped. The sheath is composed of a hollow cylindrical sleeve and two end caps. The material of the sheath is stainless steel with a thickness o...

Embodiment 2

[0052] This embodiment is a method for preparing a TNM alloy forging billet with uniform structure.

[0053] The nominal composition of the TNM alloy described in this implementation example is Ti-43Al-4Nb-1Mo-0.2B, the composition is atomic percentage, and the size of the ingot used is Φ73×99 mm.

[0054] The specific process described in this embodiment is as follows:

[0055] The first step is preparation before forging. The ingot to be die-cast is a cylindrical sample, and the surface of the ingot to be die-cast is polished to ensure that the surface quality is good and free of defects. Ultrasonic flaw detection is used to confirm that there is no crack inside the ingot, and the surface of the ingot is evenly coated with Y 2 o 3 slurry to avoid surface oxidation of the ingot. After the coating is air-dried, the ingot to be die-cast is wrapped. The sheath is composed of a hollow cylindrical sleeve and two end caps. The material of the sheath is stainless steel with a t...

Embodiment 3

[0070] This embodiment is a method for preparing a TNM alloy forging billet with uniform structure.

[0071] The nominal composition of the TNM alloy described in this implementation example is Ti-43Al-4Nb-1Mo-0.2B, the composition is atomic percentage, and the size of the ingot used is Φ73×99 mm.

[0072] The specific process described in this embodiment is as follows:

[0073] The first step is preparation before forging. The ingot to be die-cast is a cylindrical sample, and the surface of the ingot to be die-cast is polished to ensure that the surface quality is good and free of defects. Ultrasonic flaw detection is used to confirm that there is no crack inside the ingot, and the surface of the ingot is evenly coated with Y 2 o 3 slurry to avoid surface oxidation of the ingot. After the coating is air-dried, the ingot to be die-cast is wrapped. The sheath is composed of a hollow cylindrical sleeve and two end caps. The material of the sheath is stainless steel with a t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for a TNM alloy forging blank with the uniform structure. A small-amount and high-frequency forging method is adopted so as to avoid the cracking phenomenon in the TNM alloy forging process; and meanwhile, heat preservation is conducted for the enough time among passes, the sub-dynamic recrystallization phenomenon in the process of heat treatment afterforging is fully utilized, therefore, the uniformity of the structures of all portions of the forging blank is improved, and the TNM alloy forging blank with the fine and uniform structure is obtained. According to the preparation method for the TNM alloy forging blank with the uniform structure, non-isothermal forging is adopted, the forging temperature is low, and the economic benefit can be effectively increased; and in addition, deformation parameters and heat treatment parameters of all the passes are same, and operation is easy.

Description

technical field [0001] The invention relates to the field of intermetallic compound forging and heat treatment, in particular to a method for preparing a TNM alloy forging billet with uniform structure. Background technique [0002] TiAl alloy is a multi-phase alloy, and its structure is often composed of body-centered cubic (BCC), face-centered cubic (FCC), hexagonal close-packed (HCP) and other crystal structure phases, and the phase transformation process is relatively complicated. Moreover, TiAl alloy has the characteristics of low density, high specific strength, and good creep resistance. Its service temperature is 700-850 ° C. It is a light-weight high-temperature structure that is applied to the upper limit of the service temperature of titanium alloys and the lower limit of service temperatures of high-temperature alloys. metallic material. Therefore, TiAl not only has great research value in theory, but also has great potential in industrial application. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21J5/00B21J1/06B21K29/00C22F1/18
Inventor 李金山唐斌向林薛祥义寇宏超王军王毅孙智刚
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com