High-performance storage battery negative electrode lead paste for renewable energy storage and preparation method thereof

A renewable energy, negative lead paste technology, applied in battery electrodes, circuits, electrical components, etc., can solve the problems of negative plate vulcanization, battery failure, etc., to improve the service life, improve the conversion environment, and improve the effect of charging receiving capacity.

Inactive Publication Date: 2019-07-30
ZHAOQING LEOCH BATTERY TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The outdoor communication battery is a kind of battery. Due to the use environment, the outdoor communica

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The present invention proposes a high-performance storage battery negative lead paste for renewable energy storage. The formula of its raw materials by weight is as follows: lead powder: 81-82 parts, 1.325 density dilute sulfuric acid: 8-9.5 parts, deionized water: 7.3-8.5 parts , sodium carboxymethyl cellulose: 3-5 parts, barium sulfate: 0.15-0.25 parts, sodium lignosulfonate: 0.12-0.22 parts, humic acid: 0.2-0.35 parts, carbon black: 0.1-0.2 parts, short fiber : 0.07-0.12 parts, graphene: 0.002-0.005 parts.

[0019] The present invention also provides a preparation method of a high-performance battery negative electrode paste for renewable energy storage, comprising the following steps:

[0020] S1. Weigh lead powder, barium sulfate, sodium lignin sulfonate, humic acid, carbon black and short fibers in proportion, and use a paste mixing machine to mix and stir for 4 minutes, and during the stirring process, it is necessary to ensure that its speed is at 300 Between -...

Embodiment 2

[0027] The present invention proposes a high-performance storage battery negative lead paste for renewable energy storage. The formula of its raw materials by weight is as follows: lead powder: 81.5 parts, 1.325 density dilute sulfuric acid: 8.8 parts, 8 parts of deionized water, sodium carboxymethyl cellulose : 4 parts, barium sulfate: 0.2 parts, sodium lignosulfonate: 0.18 parts, humic acid: 0.28 parts, carbon black: 0.15 parts, short fiber: 0.1 parts, graphene: 0.0035 parts.

[0028] The present invention also provides a preparation method of a high-performance battery negative electrode paste for renewable energy storage, comprising the following steps:

[0029] S1. Weigh lead powder, barium sulfate, sodium lignin sulfonate, humic acid, carbon black and short fibers in proportion, and use a paste mixing machine to mix and stir for 4 minutes, and during the stirring process, it is necessary to ensure that its speed is at 300 Between -500 rev / min, it is necessary to check th...

Embodiment 3

[0036] The present invention proposes a high-performance storage battery negative lead paste for renewable energy storage. The formula of its raw materials by weight is as follows: lead powder: 81-82 parts, 1.325 density dilute sulfuric acid: 8-9.5 parts, deionized water: 7.3-8.5 parts , sodium carboxymethyl cellulose: 3-5 parts, barium sulfate: 0.15-0.25 parts, sodium lignosulfonate: 0.12-0.22 parts, humic acid: 0.2-0.35 parts, carbon black: 0.1-0.2 parts, short fiber : 0.07-0.12 parts, graphene: 0.002-0.005 parts.

[0037] The present invention also provides a preparation method of a high-performance battery negative electrode paste for renewable energy storage, comprising the following steps:

[0038] S1. Weigh lead powder, barium sulfate, sodium lignin sulfonate, humic acid, carbon black and short fibers in proportion, and use a paste mixing machine to mix and stir for 4 minutes, and during the stirring process, it is necessary to ensure that its speed is at 300 Between -...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance storage battery negative electrode lead paste for renewable energy storage, which comprises the following raw materials by weight: 81-82 parts of lead powder, 8-9.5 parts of 1.325 density dilute sulfuric acid, 7.3-8.5 parts of deionized water; 3-5 parts of sodium carboxymethylcellulose, 0.15-0.25 parts of barium sulfate, 0.12-0.22 parts of sodium lignosulphonate, 0.2-0.35 parts of humic acid, 0.1-0.2 parts of carbon black, 0.07-0.12 parts of short-staple, 0.002-0.005 parts of graphite alkene. The invention also provides a preparation method of the high-performance storage battery negative electrode lead paste for renewable energy storage. According to the invention, the charging receiving capacity of the negative plate is improved by adding graphene, the negative plate conversion environment is improved, and the problem that the negative plate cannot be converted due to the generation of coarse lead sulfate crystal particles on the surface ofthe negative plate is avoided, so that the service life of the battery is prolonged, the development requirement is met, and the negative plate is suitable for large-scale popularization.

Description

technical field [0001] The invention relates to the technical field of battery preparation, in particular to a high-performance battery negative lead paste for renewable energy storage and a preparation method thereof. Background technique [0002] A storage battery is a device that directly converts chemical energy into electrical energy. It is a battery designed to be rechargeable. It is recharged through a reversible chemical reaction. It usually refers to a lead-acid battery, which is a type of battery. , belonging to the secondary battery. Its working principle: when charging, the external electric energy is used to regenerate the internal active material, the electric energy is stored as chemical energy, and the chemical energy is converted into electric energy output again when it needs to be discharged. [0003] The outdoor communication battery is one of the batteries. Due to the use environment, the outdoor communication battery will have the problem of vulcanizat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/57H01M4/62
CPCH01M4/57H01M4/628Y02E60/10
Inventor 赵周辉
Owner ZHAOQING LEOCH BATTERY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap