One-dimensional coordination polymer with phase matching SHG performance and synthetic method thereof

A technology of coordination polymer and synthesis method, which is applied in the field of matching performance second-order nonlinear material coordination polymer and second-order nonlinear material, which can solve the requirements that cannot meet the needs of practical applications, mismatch, and practical application of composite materials. Limitations and other issues, to achieve the effect of good application prospects, strong application significance, and excellent SHG performance

Active Publication Date: 2019-09-20
ANHUI UNIVERSITY OF ARCHITECTURE
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] With the research and development of nonlinear optical materials, new nonlinear materials emerge in endlessly, but many materials have the disadvantage of mismatching second-order nonlinear (SHG) performance, which has great influence on the practical application of composite materials. limitations, cannot meet the needs of practical applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-dimensional coordination polymer with phase matching SHG performance and synthetic method thereof
  • One-dimensional coordination polymer with phase matching SHG performance and synthetic method thereof
  • One-dimensional coordination polymer with phase matching SHG performance and synthetic method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0054] The present invention discloses a method for synthesizing a one-dimensional coordination polymer with matching SHG properties, specifically, comprising the following steps:

[0055] (1) dissolving γ-dpdpt in a solvent to obtain a γ-dpdpt solution;

[0056] (2) dissolving the zinc salt in a solvent to obtain a zinc salt solution;

[0057] (3) Put the γ-dpdpt solution on the bottom of the test tube, drop methanol into it as a transition layer, and then drop the zinc salt solution into it as the upper layer;

[0058] (4) The test tube was left to stand for two weeks, and a rod-shaped single crystal appeared, and the solvent was removed by suction filtration, and dried in the air to obtain a Zn(II) coordination polymer;

[0059] Zinc salt is ZnCl 2 , ZnBr 2 , ZnI 2 one of

[0060] The solvent is at least one of water, ethanol, methanol, acetonitrile, chloroform, chloroform, ethyl acetate, tetrahydrofuran and dimethylformamide.

Embodiment 1

[0063] (1) Dissolve 0.0504g (0.010mmol) γ-dpdpt in a mixed solvent of 6 mL chloroform and 1 mL methanol to obtain a γ-dpdpt solution;

[0064] (2) 0.0136g (0.010mmol) of ZnCl 2 Dissolve in 10mL methanol to get ZnCl 2 solution;

[0065] (3) Put the γ-dpdpt solution on the bottom of the test tube, drop 3mL of methanol as a transition layer, and then add ZnCl 2 The solution is dripped into it as the upper layer;

[0066] (4) The test tube was left to stand for two weeks at 25 degrees Celsius, and an orange rod-shaped single crystal appeared. The solvent was removed by suction filtration, and dried in the air to obtain 0.067 g of an orange solid, with a yield of 78.2%.

Embodiment 2

[0068] (1) Dissolve 0.0504g (0.010mmol) γ-dpdpt in a mixed solvent of 6 mL chloroform and 1 mL methanol to obtain a γ-dpdpt solution;

[0069] (2) 0.0136g (0.010mmol) of ZnCl 2 Dissolve in 10mL methanol to get ZnCl 2 solution;

[0070] (3) Put the γ-dpdpt solution on the bottom of the test tube, drop 3mL of methanol as a transition layer, and then add ZnCl 2 The solution is dripped into it as the upper layer;

[0071] (4) The test tube was left standing for two weeks at 30 degrees Celsius, and an orange rod-shaped single crystal appeared. The solvent was removed by suction filtration, and dried in the air to obtain 0.075 g of an orange solid with a yield of 87.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an one-dimensional coordination polymer with phase matching SHG performance and a synthetic method thereof, and relates to the field of second-order nonlinear materials. Positions of powder X-ray diffraction peaks of the coordination polymer material are as follows: 6.76 degree + / -0.50 degree, 8.77 degree + / -0.50 degree, 10.15 degree + / -0.50 degree, 10.30 degree + / -0.50 degree, 11.43 degree + / -0.50 degree, 13.44 degree + / -0.50 degree, 13.81 degree + / -0.50 degree, 16.04 degree + / -0.50 degree and other specific peak values. A 2[theta] angle range is between 5 degree and 35 degree. The coordination polymer provided by the invention has excellent SHG performance and phase matching performance. The phase matching performance has a stronger significance for applications of the second-order nonlinear materials, which makes the polymer have a wider application range and a good application prospect.

Description

technical field [0001] The invention belongs to the field of second-order nonlinear materials with phase-matching properties, and specifically relates to the field of coordination polymers of second-order nonlinear materials with phase-matching properties. Background technique [0002] Nonlinear optics is a branch of modern optics, which studies the nonlinear phenomena and applications of media under the action of strong coherent light. The study of nonlinear optics is of great significance to the development of laser technology, spectroscopy, and material structure analysis. Applications of nonlinear optics range from technical fields to research fields. For example: using various nonlinear crystals to make electro-optical switches and realize laser modulation. The tuning of laser frequency is realized by optical parametric oscillation. Combined with frequency doubling and frequency mixing technology, it can be tuned in a wide range from mid-infrared to vacuum ultraviole...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G83/00
CPCC08G83/008
Inventor 张俊
Owner ANHUI UNIVERSITY OF ARCHITECTURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products