Waterproof, fireproof, and insect-proof plant fiber and moulding technology thereof

A technology of plant fiber and fireproof fiber, which is applied in the field of plant fiber, can solve the problems of plant fiber performance failure, etc., and achieve the effects of reducing poor heat preservation, simple process, and strong water resistance

Active Publication Date: 2019-11-29
安徽润邦环保科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, with the development of my country's building materials field, people have higher and higher requirements for the waterproof, fireproof and moth-proof properties of plant fibers. When plant fibers are used in an environment with rich water content, the surface of existing plant fibers will produce Humidity, after a long period of humidity, the plant fiber will have performance failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof, fireproof, and insect-proof plant fiber and moulding technology thereof
  • Waterproof, fireproof, and insect-proof plant fiber and moulding technology thereof
  • Waterproof, fireproof, and insect-proof plant fiber and moulding technology thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0050] A kind of glutinous rice-starch binder, adopts following method to prepare:

[0051] (1) Ingredients: in parts by weight, weigh 45 parts of cooked glutinous rice pulp, 25 parts of starch, 15 parts of slaked lime and 10 parts of vitrified microbeads;

[0052] (2) Add vitrified microbeads to the cooked glutinous rice slurry, and stir evenly;

[0053] (3) Continue to add starch and slaked lime, stir until the viscosity of the glutinous rice-starch binder is 20000mpa·s, set aside.

preparation example 2

[0055] A kind of glutinous rice-starch binder, adopts following method to prepare:

[0056] (1) Ingredients: in parts by weight, weigh 48 parts of cooked glutinous rice pulp, 28 parts of starch, 23 parts of slaked lime and 11 parts of vitrified microbeads;

[0057] (2) Add vitrified microbeads to the cooked glutinous rice slurry, and stir evenly;

[0058] (3) Continue to add starch and slaked lime, stir until the viscosity of the glutinous rice-starch binder is about 30000mpa·s, set aside.

preparation example 3

[0060] A kind of glutinous rice-starch binder, adopts following method to prepare:

[0061] (1) Ingredients: in parts by weight, weigh 50 parts of cooked glutinous rice pulp, 30 parts of starch, 30 parts of slaked lime and 12 parts of vitrified microbeads;

[0062] (2) Add vitrified microbeads to the cooked glutinous rice slurry, and stir evenly;

[0063] (3) Continue to add starch and slaked lime, stir until the viscosity of the glutinous rice-starch binder is 40000mpa·s, set aside.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterproof, fireproof, and insect-proof plant fiber and a moulding technology thereof, and belongs to the technical field of construction filling materials. The plant fibercomprises following components in parts by weight: 50 to 60 parts of wheat straws, 10 to 20 parts of peanut shell powder, 5 to 20 parts of a glutinous rice-starch binder, 20 to 22 parts of calcium hydroxide, 3 to 10 parts of paraffin waterproof powder, and 1 to 5 parts of fireproof fibers. Wheat straws and peanut shell powder are taken as the basic materials and are subjected to an antiseptic treatment; the glutinous rice-starch binder and paraffin waterproof powder are compounded so as to firmly bind the wheat straws, peanut shell powder, and other filling materials together; a water repellent layer is formed on the surface of the plant fiber, thus the surface of the plant fiber will not be wetted; moreover, fireproof fibers are added, and the provided plant fiber is resistant to water, fire, and insects.

Description

technical field [0001] The invention relates to the technical field of plant fibers, in particular to a waterproof, fireproof and insect-resistant plant fiber and a molding process thereof. Background technique [0002] Plant fiber is made of rice husk, rice straw, wheat straw, corn stalk, cotton stalk, wood chips, bamboo chips and other crop straw or other plant stalks, first made into 10-200 mesh plant fiber powder, and then mixed with other The raw material is made into plant fiber. [0003] The Chinese patent application publication number CN106046824A discloses a plant fiber product and a preparation method thereof, which is made of raw materials comprising the following components: (a) konjac flour adhesive; (b) plant fiber powder, which includes bamboo leaves ; The mixture slurry containing raw materials and water is loaded into a mold, and the mixture slurry is hot-pressed, and the plant fiber product prepared by this method has excellent strength, excellent toughne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/28C04B111/20C04B111/28C04B111/27
CPCC04B26/28C04B2111/20C04B2111/28C04B2111/2092C04B2111/27C04B24/36C04B22/064C04B18/24C04B14/42C04B14/386
Inventor 谢思松邵蒙影
Owner 安徽润邦环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com