A kind of moisture absorption and perspiration polyester fiber and preparation method thereof

A polyester fiber, moisture wicking technology, applied in the fiber field, can solve problems such as unfavorable moisture export

Active Publication Date: 2020-10-30
深圳市宏翔新材料发展有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the grooves of general special-shaped cross-section fibers are on the same side, which is not conducive to the export of moisture, and its moisture-conducting efficiency needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of moisture absorption and perspiration polyester fiber and preparation method thereof
  • A kind of moisture absorption and perspiration polyester fiber and preparation method thereof
  • A kind of moisture absorption and perspiration polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A kind of preparation method of moisture-wicking polyester fiber, according to FDY process, after the mass ratio is 55:45 CDP melt (intrinsic viscosity is 0.58dL / g) and PBT melt (intrinsic viscosity is 1dL / g) are distributed , after extruding from the spinneret holes on the same spinneret to obtain FDY filaments, perform relaxation heat treatment to obtain moisture-absorbing and sweat-wicking polyester fibers;

[0048] The spinneret holes on the spinneret are shaped spinneret hole, The shape is composed of a horizontal line and two vertical lines perpendicular to it; the width of a horizontal line and the two vertical lines are the same; the length of the two vertical lines is the same, and the ratio of the length of the two vertical lines to the length of the horizontal line is 4:5 ; The ratio of the length to width of two vertical lines is 6:1; the distance between two vertical lines is 50% of the length of a horizontal line; Midpoint; said distribution refers to ...

Embodiment 2

[0055] A method for preparing moisture-wicking polyester fiber, according to the FDY process, the mass ratio is 55:45 CDP melt (intrinsic viscosity is 0.6dL / g) and PBT melt (intrinsic viscosity is 1.2dL / g) are distributed Finally, after extruding from the spinneret holes on the same spinneret to obtain FDY filaments, perform relaxation heat treatment to obtain moisture-absorbing and sweat-wicking polyester fibers;

[0056] The spinneret hole is shaped spinneret hole, The shape is composed of a horizontal line and two vertical lines perpendicular to it; the width of a horizontal line and the two vertical lines are the same; the length of the two vertical lines is the same, and the ratio of the length of the two vertical lines to the length of the horizontal line is 6:5 ; The ratio of the length and width of two vertical lines is 8:1; the distance between two vertical lines is 65% of the length of a horizontal line; Midpoint; said distribution refers to controlling the CDP m...

Embodiment 3

[0063] A method for preparing moisture-wicking polyester fiber, according to the FDY process, the mass ratio is 55:45 CDP melt (intrinsic viscosity is 0.58dL / g) and PBT melt (intrinsic viscosity is 1.09dL / g) are distributed Finally, after extruding from the spinneret holes on the same spinneret to obtain FDY filaments, perform relaxation heat treatment to obtain moisture-absorbing and sweat-wicking polyester fibers;

[0064] The spinneret hole is shaped spinneret hole, The shape is composed of a horizontal line and two vertical lines perpendicular to it; the width of a horizontal line and the two vertical lines are the same; the length of the two vertical lines is the same, and the ratio of the length of the two vertical lines to the length of the horizontal line is 5:5 ; The ratio of the length and width of two vertical lines is 8:1; the distance between two vertical lines is 65% of the length of a horizontal line; Midpoint; said distribution refers to controlling the CDP...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
heightaaaaaaaaaa
Basis weightaaaaaaaaaa
Login to View More

Abstract

The invention relates to moisture absorption and sweat releasing polyester fibres and a preparation method thereof. According to a FDY process, a CDP melt and a PBT melt are distributed and extruded from spinneret holes on the same spinneret plate, so that FDY filaments are obtained; then, heat treatment without tension is carried out, so that moisture absorption and sweat releasing polyester fibres are obtained; the spinneret holes are shaped as shown in the specification; the shape as shown in the specification is composed of a transverse line and two vertical lines vertically connected withthe transverse line; the transverse line and the two vertical lines are same in width; the two vertical lines are same in length; the length ratio of the vertical line to the transverse line is (4-6):5; the length-to-width ratio of the two vertical lines is (6-8):1; the distance between the two vertical lines is 50-70% of the length of the transverse line; the midpoint of the connecting line of intersection points of the two vertical lines and the transverse line is the midpoint of the transverse line; distribution is that the CDP melt is controlled to flow through the transverse line and thePBT melt is controlled to flow through the two vertical lines at the same time; the finally prepared moisture absorption and sweat releasing polyester fibres have twisted form; the structure is easyfor water output; and the moisture absorption and sweat releasing performance is good.

Description

technical field [0001] The invention belongs to the field of fiber technology, and relates to a moisture-absorbing and sweat-wicking polyester fiber and a preparation method thereof. Background technique [0002] At present, domestic chemical fibers mainly use polyester filaments as raw materials, and the cross-section of chemical fibers is round or similar to round. Due to the poor hygroscopicity of polyester itself, it feels stuffy, airtight, and lacks comfort when worn, so it is in urgent need of improvement. At present, the more commonly used method is to design it as a shaped fiber with moisture permeability. [0003] Special-shaped fibers are generally prepared by specially designed and manufactured special-shaped spinnerets through special spinning processes, which is also the most commonly used method for producing special-shaped fibers at home and abroad. Producers can produce shaped fibers with any cross-sectional shape by improving and optimizing the processing t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/253D01D5/30D01D5/22
CPCD01D5/22D01D5/253D01D5/30
Inventor 王显峰
Owner 深圳市宏翔新材料发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com