Aluminum alloy deoiling and dewaxing powder and preparing method thereof

An aluminum alloy and wax powder technology, applied in the field of metal surface treatment, can solve the problems of poor rust resistance, easy rust of metal parts, corrosion of workpieces, etc., and achieve the effect of excellent lubricity

Inactive Publication Date: 2020-04-10
HUBEI DE MEI TECH
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used organic solvents cannot completely remove polishing wax, especially the polishing materials such as metal oxides and carbides on it cannot be effectively cleaned; and chlorine-containing solvents are not only highly toxic, but also tend to hydrolyze. The workpiece will be corroded; at the same time, chemical and electrochemical methods for wax and degreasing must use strong acid or alkali, which will corrode metal, so it is not suitable for cleaning
[0003] In addition, although various wax removers currently on the market can clean the polishing wax and grease on the metal surface to a certain extent, due to the defects in their components, content and process, the rust resistance is very poor, and the metal products after cleaning The parts are easy to rust, and the product has a lot of foam, which is dangerous to use and poor cleaning efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy deoiling and dewaxing powder and preparing method thereof
  • Aluminum alloy deoiling and dewaxing powder and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] An aluminum alloy degreasing and dewaxing powder is made from the following raw materials in parts by weight:

[0050] Borax 69%

[0051] Sodium Oleate 7.8%

[0052] Sodium Laurate 7.8%

[0053] Sodium lignosulfonate 3%

[0054] Surfactant 1.7%

[0055] Emulsifier 3.7%

[0056] Ethylene glycol monobutyl ether 2%

[0057] Macrogol 5%.

[0058] Preferably, the surfactant is A-260 type low foam surfactant.

[0059] Preferably, the emulsifier is a TMN-10 emulsifier.

[0060] Preferably, the polyethylene glycol has a molecular weight of 2000.

[0061] A preparation method of aluminum alloy degreasing and dewaxing powder, comprising the following steps:

[0062] S1: Add borax, sodium oleate and sodium laurate in corresponding parts by weight to a mixer to disperse, mix and stir for 3 minutes to form a mixed solution A;

[0063] S2: add surfactant, emulsifier and ethylene glycol monobutyl ether in corresponding parts by weight to the mixer to disperse, mix and stir f...

Embodiment 2

[0070] The preparation method of an aluminum alloy degreasing and waxing powder in this embodiment is the same as that in Embodiment 1, and will not be repeated here.

[0071] In this embodiment, an aluminum alloy degreasing and waxing powder is made from the following raw materials in parts by weight:

[0072] Borax 65%

[0073] Sodium Oleate 5%

[0074] Sodium Laurate 6%

[0075] Sodium lignosulfonate 1%

[0076] Surfactant 1%

[0077] Emulsifier 3%

[0078] Ethylene glycol monobutyl ether 1%

[0079] Macrogol 4%.

[0080] Preferably, the surfactant is A-260 type low foam surfactant.

[0081] Preferably, the emulsifier is a TMN-10 emulsifier.

[0082] Preferably, the polyethylene glycol has a molecular weight of 2000.

Embodiment 3

[0084] The preparation method of an aluminum alloy degreasing and waxing powder in this embodiment is the same as that in Embodiment 1, and will not be repeated here.

[0085] In this embodiment, an aluminum alloy degreasing and waxing powder is made from the following raw materials in parts by weight:

[0086] Borax 70%

[0087] Sodium Oleate 8%

[0088] Sodium Laurate 8%

[0089] Sodium lignosulfonate 3%

[0090] Surfactant 2%

[0091] Emulsifier 5%

[0092] Ethylene glycol monobutyl ether 2%

[0093] Polyethylene glycol 6%.

[0094] Preferably, the surfactant is A-260 type low foam surfactant.

[0095] Preferably, the emulsifier is a TMN-10 emulsifier.

[0096] Preferably, the polyethylene glycol has a molecular weight of 2000.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of metal surface treatment, in particular to aluminum alloy deoiling and dewaxing powder and a preparing method thereof. The aluminum alloy deoiling and dewaxing powder is prepared from, by weight, 65-70% of borax, 5-8% of sodium oleate, 6-8% of sodium laurate, 1-3% of sodium lignin sulfonate, 1-2% of a surfactant, 3-5% of an emulsifying agent, 1-2% of ethylene glycol monobutylether and 4-6% of polyethylene glycol. The aluminum alloy deoiling and dewaxing powder can effectively remove oil and wax dirt attached to the surface of an aluminum alloy product; andthe aluminum alloy deoiling and dewaxing powder is not limited by temperature control, does not need to be cleaned up at a high temperature, and can remove polishing wax, grinding wax, grease, oil stains, dust and other dirt on the surface of the aluminum alloy product at a normal temperature.

Description

technical field [0001] The invention relates to the field of metal surface treatment, in particular to an aluminum alloy degreasing and waxing powder and a preparation method thereof. Background technique [0002] After the metal workpiece is polished with polishing wax, the wax scale remains on the workpiece by mechanical adsorption, intermolecular adsorption and electrostatic adsorption. The main components of polishing wax are mineral oil, animal and vegetable oil, paraffin, natural wax, resin, stearic acid and abrasives. At present, the methods of wax removal, degreasing and degreasing of metal mainly include the following categories: organic solvent method, chemical method, electrochemical method and water-based cleaning agent method. Commonly used organic solvents cannot completely remove polishing wax, especially the polishing materials such as metal oxides and carbides on it cannot be effectively cleaned; and chlorine-containing solvents are not only highly toxic, b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G5/00
CPCC23G5/00
Inventor 瞿德勤
Owner HUBEI DE MEI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap