Preparation method and application of biomass honeycomb semicoke loaded nickel-iron nanoparticle catalyst

A granular catalyst and nanoparticle technology, applied in the direction of catalyst activation/preparation, physical/chemical process catalyst, metal/metal oxide/metal hydroxide catalyst, etc., can solve the problems of a large amount of smoke, tar generation, waste of energy, etc. , to reduce pollution, increase specific surface area and pore volume, and reduce preparation cost

Active Publication Date: 2020-06-09
CHINA UNIV OF MINING & TECH
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In the production process of modern society, a large amount of waste biomass will be produced. Composting and incineration are mainly used for the treatment of waste biomass, but this method will generate a lot of smoke and waste energy.
At this stage, various thermochemical technologies (such as pyrolysis and gasification) convert biomass into high-value products, but in this process, the key problem of tar is inevitably generated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of biomass honeycomb semicoke loaded nickel-iron nanoparticle catalyst
  • Preparation method and application of biomass honeycomb semicoke loaded nickel-iron nanoparticle catalyst
  • Preparation method and application of biomass honeycomb semicoke loaded nickel-iron nanoparticle catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The raw material of Sargassum algae was washed with deionized water, dried at 105°C for 48 hours, crushed with a pulverizer, sieved to 40-80 mesh, and then dried for later use;

[0031] Weigh 13.5 g FeCl 3 ·6H 2 O and 11.85 gNiCl 2 ·6H 2 O solid was dissolved in 200 mL deionized water, weighed 20 g dry Sargassum powder and added FeCl 3 and NiCl 2 Mix the solution and stir it magnetically for 8 h at room temperature to make the Sargassum and FeCl 3 and NiCl 2 The mixed solution was fully contacted, and after the stirring was completed, it was dried in a drying oven at 105 °C for 24 h, and ground to obtain the SC@0.05Ni-Fe precursor;

[0032] Weigh 20 gSC@0.05Ni-Fe precursor and place it in a single temperature zone horizontal tube furnace, 2The gas flow rate was 500 mL / min, and the mixture was heated to 800 °C at a heating rate of 10 °C / min and kept for 60 min. After natural cooling was completed, a biomass honeycomb semi-coke supported nickel / iron nanoparticle ca...

Embodiment 2

[0035] Sargassum raw material was washed with deionized water, dried at 105 °C for 48 h, crushed with a pulverizer, sieved to 40-80 mesh, and then dried for later use;

[0036] Weigh 27 g FeCl 3 ·6H 2 O and 23.7 gNiCl 2 ·6H 2 O solid was dissolved in 200 mL deionized water, weighed 20 g dry Sargassum powder and added FeCl 3 and NiCl 2 Mix the solution and stir it magnetically for 8 h at room temperature to make the Sargassum and FeCl 3 and NiCl 2 The mixed solution was fully contacted, and after the stirring was completed, it was dried in a drying oven at 105 °C for 24 h, and ground to obtain the SC@0.1Ni-Fe precursor;

[0037] Weigh 20 gSC@0.1Ni-Fe precursor and place it in a single temperature zone horizontal tube furnace, 2 The gas flow rate is 300-700 mL / min, and the mixture is heated to 800-900 °C at a heating rate of 10-15 °C / min and maintained for 60-90 min. After natural cooling is completed, biomass honeycomb semi-coke loaded nickel / iron is prepared Nanopartic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method and an application of a biomass honeycomb semicoke loaded nickel-iron nanoparticle catalyst. According to the method, gulfweed is used as a raw material, feCl3.6H2O and NiCl2.6H2O are introduced to serve as a chemical activating agent and a metal endowing substance, gulfweed is mixed with a mixed solution of FeCl3.6H2O and NiCl2.6H2O according to a certain ratio for dipping, carrier gas N2 is introduced into a tubular furnace for heat treatment to directly convert the gulfweed raw material into an excellent catalyst with a high specific surface area, multiple active sites and a special honeycomb structure, and the catalyst is applied to the catalytic cracking process of biomass pyrolysis tar. The waste seaweed biomass is used for treating biomass pyrolysis tar, waste is treated with waste, the biomass growth cycle is short, the preparation process is simple, the cost is low, environmental pollution is small, and the prepared gulfweed carbon-based honeycomb catalyst achieves a stable and ideal effect in biomass tar catalytic cracking.

Description

technical field [0001] The invention belongs to the technical field of energy and chemical industry for environmental protection and utilization of biomass solid waste, and specifically relates to a preparation method and application of a biomass honeycomb semi-coke loaded nickel-iron nano particle catalyst. Background technique [0002] In the production process of modern society, a large amount of waste biomass will be produced. Composting and incineration are mainly used for the treatment of waste biomass, but this method will generate a lot of smoke and waste energy. At present, various thermochemical technologies (such as pyrolysis and gasification) convert biomass into high-value products, but in this process, the key problem of tar is inevitably generated. At present, the treatment of tar includes two methods of physical cleaning and chemical conversion. Among them, the physical cleaning method is easy to cause environmental pollution and energy waste, and the chemic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/755B01J35/00B01J35/04B01J35/10B01J37/08B01J37/16C10B53/02C10B57/18C10B57/04
CPCB01J23/755B01J35/006B01J35/04B01J35/1019B01J37/084B01J37/16C10B53/02C10B57/04C10B57/18Y02E50/10
Inventor 郭飞强梁爽贾小芃田倍乐董亦琛杜世麟钱琳
Owner CHINA UNIV OF MINING & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap