Transmutation glaze ground coat, preparation method thereof and porcelain

A kiln-changing glaze and bottom glaze technology, which is applied in the field of ceramics, can solve problems such as poor viscosity, affecting the quality of the kiln-changing glaze porcelain glaze surface, and restricting promotion, and achieve the effect of changing textures, rich colors, and less environmental pollution

Inactive Publication Date: 2020-08-14
潮州市荣嘉陶瓷有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor viscosity of the existing kiln-changing glaze bottom glaze, it affects the glaze quality of the kiln-ch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transmutation glaze ground coat, preparation method thereof and porcelain
  • Transmutation glaze ground coat, preparation method thereof and porcelain
  • Transmutation glaze ground coat, preparation method thereof and porcelain

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example one

[0025] The embodiment of the present invention provides a kiln variable glaze base glaze, the components and the mass percentages of each component are: frit 70%~75%, kaolin 5%~8%, zinc oxide 4%~7%, barium carbonate 1 %~2%, iron trioxide 10%~13%.

[0026] The base glaze prepared according to the base glaze formula of this embodiment, its chemical composition includes: SiO 2 , Fe 2 O 3 , Al 2 O 3 , B 2 O 3 , Na 2 O, ZnO, BaO, CaO, K 2 O, Cl, SO 3 , P 2 O 5 , ZrO 2 , SrO, MnO, PbO, Li 2 O; The weight percentage of the chemical composition of the primer: SiO 2 45%~50%, Fe 2 O 3 10%~13%, Al 2 O 3 10%~12%, B 2 O 3 9%~11%, Na 2 O 6%~8%, ZnO 4%~7%, BaO1%~2%, CaO 1%~2%, K 2 O 0.4%~1.2%, Cl 0.05%~0.1%, SO 3 0.05%~0.1%, P 2 O 5 0.05%~0.1%, ZrO 2 0.05%~0.1%, SrO 0.01%~0.05%, MnO 0.01%~0.05%, PbO 0.01%~0.05%, Li 2 O <0.01%; the reduction rate is less than 1.50%.

[0027] figure 1 It is a schematic diagram of the preparation method of the kiln variable glaze base glaze of the...

Example Embodiment

[0033] Example two

[0034] The embodiment of the present invention provides a kiln variable glaze base glaze, the components and the mass percentages of each component are: frit 73.9%, kaolin 8.0%, zinc oxide 5.0%, barium carbonate 1.9%, and iron trioxide 11.2%.

[0035] The base glaze prepared according to the above-mentioned base glaze formula, the weight percentage of its chemical composition: SiO 2 49.66%, Fe 2 O 3 11.20%, Al 2 O 3 10.95%, B 2 O 3 10.02%, Na 2 O 7.53%, ZnO 5.00%, BaO 1.85%, CaO 1.28%, K 2 O0.93%, Cl 0.08%, SO 3 0.06%, P 2 O 5 0.05%, ZrO 2 0.05%, SrO 0.04%, MnO 0.03%, PbO 0.01%, Li 2 O <0.01%; its discretionary reduction rate is less than 1.26%

[0036] The preparation method of the base glaze of this embodiment includes the steps:

[0037] Proportioning weighing: according to the base glaze raw material formula for proportioning weighing;

[0038] Raw material ball milling: Put the prepared base glaze raw materials into a ball mill and perform wet ball milling. T...

Example Embodiment

[0043] Example three

[0044] The embodiment of the present invention provides a kiln-varying glaze base glaze, the components and the mass percentages of each component are: frit 72.00%, kaolin 8.00%, zinc oxide 5.74%, barium carbonate 1.96%, and iron trioxide 12.30%.

[0045] The base glaze prepared according to the above-mentioned base glaze formula, the weight percentage of its chemical composition: SiO 2 48.76%, Fe 2 O 3 12.30%, Al 2 O 3 10.2%, B 2 O 3 10.02%, Na 2 O 7.25%, ZnO 5.74%, BaO 1.96%, CaO 1.32%, K 2 O0.93%, Cl 0.08%, SO 3 0.06%, P 2 O 5 0.04%, ZrO 2 0.05%, SrO 0.03%, MnO 0.02%, PbO 0.01%, Li 2 O <0.01%; the reduction rate is less than 1.25%.

[0046] The preparation method of the base glaze of this embodiment includes the steps:

[0047] Proportioning weighing: according to the base glaze raw material formula for proportioning weighing;

[0048] Raw material ball milling: Put the prepared base glaze raw materials into a ball mill and perform wet ball milling. The milli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a transmutation glaze ground coat which comprises the following components in percentage by mass: 70%-75% of frit, 5%-8% of kaolin, 4%-7% of zinc oxide, 1%-2% of barium carbonate and 10%-13% of ferric oxide. The invention further discloses a preparation method of the transmutation glaze ground coat and porcelain. According to the transmutation glaze ground coat, the preparation method thereof and the porcelain, a unique ground coat formula is adopted, good application of the transmutation glaze ground coat to the porcelain is achieved through mutual cooperation and combined action of all the components and the content of all the components, the porcelain rich in hue and variable in texture is obtained, and the glaze is resistant to abrasion, not prone to falling offand little in environmental pollution. The transmutation glaze ground coat is applicable to the technical field of ceramics.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a kiln-transformed underglaze, a preparation method thereof, and porcelain. Background technique [0002] Kiln-changing glaze is a general term for art glazes that produce kiln-changing effects during the firing process of ceramic glazes. The invention belongs to the technical field of ceramic glazes of inorganic non-metallic materials, and is used for the entire glaze surface and partial decoration of daily-use ceramics and art ceramics. Due to the poor viscosity of the existing kiln-changing glaze bottom glaze, the quality of the glazed surface of the kiln-changing glaze porcelain is affected, and the popularization of this kind of bottom glaze kiln-changing glaze on daily-use ceramics is limited. Therefore, it is very necessary to develop a kind of bottom glaze with wide applicability, make it adapt to the use of daily ceramics, enrich the decoration of ceramic glazes, and b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/14C04B41/89
CPCC03C8/14C04B41/009C04B41/52C04B41/89C04B33/00C04B35/00C04B41/5022C04B41/4535C04B41/522C04B41/4543
Inventor 吴作明吴岱迅许腾曾利鹏蔡钊杰
Owner 潮州市荣嘉陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap