Single-component waterproof high-hardness water-based floor paint and preparation method thereof

A high-hardness, floor paint technology, applied in the field of floor paint, can solve the problems of poor water resistance, low hardness, poor wear resistance, etc., and achieve the effect of reducing the possibility of efflorescence, improving weather resistance, and promoting emulsion cross-linking

Inactive Publication Date: 2020-09-11
SHANGHAI BAOLIJIA NEW MATERIAL CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of poor water resistance, low hardness and poor wear resistance in existing floor paints

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component waterproof high-hardness water-based floor paint and preparation method thereof
  • Single-component waterproof high-hardness water-based floor paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Refer to the attached figure 1 , a one-component waterproof high-hardness water-based floor paint of the present embodiment includes the following components:

[0035] 10-25 parts of modified pure acrylic emulsion, 15-25 parts of modified silicone-acrylic emulsion, 0.7-1 part of film-forming aid, 20-30 parts of lithium water glass, 5-7 parts of calcined kaolin and 7-10 parts of precipitated barium sulfate share.

[0036] It also includes 0.1-0.3 part of lithium hydroxide, 1.5-2 part of polycarbodiimide, 0.1-0.2 part of wetting and dispersing agent and 0.1-0.2 part of rheology aid.

[0037] It also includes 0.2-0.4 parts of defoamer, 0.2-0.4 parts of preservatives, 3-5 parts of nano-zinc oxide and 10-15 parts of nano-titanium dioxide.

[0038] Also included are 0.1-0.3 parts of water glass stabilizer, 1-1.5 parts of fumed silica and 1-1.5 parts of modified bentonite.

[0039] A preparation method of one-component waterproof high-hardness water-based floor paint, speci...

Embodiment 2

[0055] A one-component waterproof high-hardness water-based floor paint and a preparation method thereof of the present embodiment specifically include the following steps:

[0056] S100, prepare materials, prepare materials according to the mass fraction of the required components;

[0057] S200, one-time mixing, adding modified pure acrylic emulsion and modified silicone-acrylic emulsion to the high-speed dispersing machine and then dispersing;

[0058] S300, secondary mixing, add film-forming aids and defoamer to the high-speed disperser, and disperse for 15 minutes;

[0059] S400, disperse three times, slowly add preservative solution to the high-speed disperser, and disperse for 10min;

[0060] S500, four times of dispersion, add dropwise carbodiimide and lithium hydroxide to the high-speed disperser, and continue to disperse for 15min during the dropwise addition;

[0061] S600, five times of dispersion, add wetting and dispersing agent and rheology aid to the high-spe...

Embodiment 3

[0071] A one-component waterproof high-hardness water-based floor paint and a preparation method thereof of the present embodiment specifically include the following steps:

[0072] S100, prepare materials, prepare materials according to the mass fraction of the required components;

[0073] S200, one-time mixing, adding modified pure acrylic emulsion and modified silicone-acrylic emulsion to the high-speed dispersing machine and then dispersing;

[0074] S300, secondary mixing, add film-forming aids and defoamer to the high-speed disperser, and disperse for 15 minutes;

[0075] S400, disperse three times, slowly add preservative solution to the high-speed disperser, and disperse for 10min;

[0076] S500, four times of dispersion, add dropwise carbodiimide and lithium hydroxide to the high-speed disperser, and continue to disperse for 15min during the dropwise addition;

[0077] S600, five times of dispersion, add wetting and dispersing agent and rheology aid to the high-spe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to single-component waterproof high-hardness water-based floor paint and a preparation method thereof. With the combination of a modified pure acrylic emulsion and a modified silicone acrylic emulsion, not only can the weather resistance be improved, but also certain hardness can be enhanced; a good waterproof effect is also achieved; secondly, polycarbodiimide is also introduced into the formula, so that emulsion crosslinking is effectively promoted, drying rate is accelerated, and adhesive force is improved; and thirdly, the materials are different from sodium silicateor potassium silicate used by common floor paint. The lithium silicate adopted by the invention has the advantages that the modulus is 3.5, the possibility of efflorescence is reduced to the maximum extent, the stability is better, and most importantly, the overall strength and wear resistance are improved. And finally, in order to solve the problem of storage stability of a traditional silicate system, the water glass stability is introduced, so that the reaction of the water glass and the emulsion can be effectively prevented, the coexistence effect is achieved, and the problem of storage stability of the system is effectively solved.

Description

technical field [0001] The invention belongs to the technical field of floor paint, in particular to a one-component waterproof high-hardness water-based floor paint and a preparation method thereof. Background technique [0002] The existing floor paints are mainly oil-based, and the oil-based paints are divided into epoxy, polyurethane and polyurea. These floor paints all contain harmful substances and do not meet the current environmental protection requirements. Poor weather resistance, not suitable for outdoor use. So the water-based floor paint was born, but the current water-based floor paint has the disadvantages of low hardness, poor wear resistance, poor weather resistance, easy to efflorescence, and water resistance. Compounding various additives can effectively solve the problems of poor water resistance, low hardness and poor wear resistance. SUMMARY OF THE INVENTION [0003] 1. The technical problem to be solved by the invention [0004] The purpose of the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D179/00C09D7/61C09D7/62C09D1/04C09D7/65
CPCC09D143/04C09D133/04C09D7/61C09D7/70C09D7/62C09D1/04C09D7/65C08L2312/00C08L2205/03C08K2201/011C08K2003/2296C08K2003/3045C08K2003/2241C08L79/00C08L33/04C08K13/06C08K3/346C08K7/26C08K3/22C08K3/34C08L43/04
Inventor 房迎春
Owner SHANGHAI BAOLIJIA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap