A kind of cobalt-chromium alloy biological material and preparation method thereof

A biomaterial, cobalt-chromium alloy technology, applied in drug delivery, pharmaceutical formulations, prostheses, etc., can solve the difficulty of ensuring the service life of the alloy, the difficulty of ensuring the high hardness and high wear resistance of the alloy, the mechanical properties of coarse grains and the durability Abrasion and other issues, to achieve high service life, improve tensile strength and wear resistance, good biocompatibility effect

Active Publication Date: 2021-04-27
中怡(深圳)医疗科技集团有限公司
View PDF25 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the surface grains of the alloy prepared by casting are relatively coarse, the mechanical properties and wear resistance are low, and it is difficult to ensure the high hardness and high wear resistance characteristics of the alloy as materials for artificial joints and surgical instruments, and it is difficult to ensure the service life of the alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A cobalt-chromium alloy biological material, calculated by weight percentage, includes the following components: Mo 22.0%, Cr 18.5%, Si 2.0%, ZrO 2 3.0%, Fe 0.5%, C 0.6%, N 0.2%, Co 53.2%.

Embodiment 2

[0029] A cobalt-chromium alloy biological material, calculated by weight percentage, includes the following components: Mo 28.0%, Cr7.5%, Si 4.0%, ZrO 2 1.0%, Fe 1.2%, C 0.3%, N 0.3%, Co 57.7%.

Embodiment 3

[0031] A cobalt-chromium alloy biological material, calculated by weight percentage, includes the following components: Mo 24.0%, Cr16.5%, Si 3.0%, ZrO 2 2.2%, Fe 0.7%, C 0.5%, N 0.2%, Co 62.9%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a cobalt-chromium alloy biological material and a preparation method thereof, which comprises the following components in terms of weight percentage: the balance is Co. The preparation method of the material is to weigh the raw materials in proportion, mix and smelt Co, Mo, Cr, Si, Fe, C, N, homogenize and cast according to biological requirements; spray ZrO on the surface of the cast and uncooled product. 2 , and then cooled naturally to obtain a cobalt-chromium alloy biomaterial; this scheme improves the composition of the alloy material, effectively improves the mechanical properties and biocompatibility of the material, and modifies the surface of the alloy material by spraying, causing a phase change on the surface to enhance The strength of the alloy surface while maintaining the toughness inside the alloy makes the surface of the material more wear-resistant, thereby ensuring its high service life.

Description

technical field [0001] The invention relates to the technical field of alloy materials, in particular to a cobalt-chromium alloy biological material and a preparation method thereof. Background technique [0002] With the continuous development of modern science and technology, the level of medical treatment is becoming more and more developed. Biomaterials are the most important field of life science research. Most organs of the human body can be replaced by artificial organs and other medical devices implanted in the body, such as the human body. Human hard tissues such as bones and cardiac pacemakers can be replaced by metal titanium alloys and chromium alloys. Since medical devices, alloys, or alloys are implanted in living organisms or are in direct contact with the surface of living organisms, these medical devices are required to have high corrosion resistance and biocompatibility. In addition, when these medical devices are used as artificial joint materials, they a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C19/07C22C30/00C22C1/02C23C24/04A61L27/04A61L27/50
CPCA61L27/045A61L27/50A61L2400/18C22C1/02C22C19/07C22C30/00C23C24/04
Inventor 俞光锋
Owner 中怡(深圳)医疗科技集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com