A kind of high weather resistance waterproof exterior wall paint for building and preparation method thereof

An exterior wall coating, high weather resistance technology, used in anti-corrosion coatings, coatings and other directions, can solve problems such as reducing the service life of buildings, affecting the aesthetics of buildings, and easily infiltrating into walls, etc., to improve gloss and protect against Destruction, strength and corrosion resistance effects

Active Publication Date: 2021-09-21
徐洪涛
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-based acrylic paints on the market tend to be hot, sticky and brittle. In the dry environment below 0 ℃ for a long time in northern my country, they are prone to cracking. In the warm and humid environment of southern my country, water vapor and rainwater are easy to seep into the wall. surface and corrode the wall, which not only affects the aesthetics of the building, but also reduces the service life of the building

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] The first high weather resistance waterproof exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:

[0060] Fluorosilicone modified acrylic emulsion 50 parts

[0061] Epoxy modified acrylic emulsion 25 parts

[0062] Fluorosilane 15 parts

[0063] 15 parts of organic bentonite

[0064] Silicon oxide 15 parts

[0065] 25 parts of titanium dioxide

[0066] Auxiliary 5 parts

[0067] 25 parts of water.

[0068] Wherein: the solid content of fluorosilicon-modified acrylic emulsion and epoxy-modified acrylic emulsion is 50%-60%; the average particle diameter of the organic bentonite and silicon oxide is 200-400 mesh; the dispersant is sodium hexametaphosphate; The wetting agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.

Embodiment 2

[0070] The second high weather resistance waterproof exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:

[0071] Fluorosilicone modified acrylic emulsion 50 parts

[0072] Epoxy modified acrylic emulsion 20 parts

[0073] Fluorosilane 20 parts

[0074] 20 parts of organic bentonite

[0075] Silicon oxide 20 parts

[0076] 30 parts of titanium dioxide

[0077] Auxiliary 8 parts

[0078] 35 parts of water.

[0079] Wherein: the solid content of fluorosilicon modified acrylic emulsion and epoxy modified acrylic emulsion is 50%-60%; the average particle diameter of described organic bentonite and silicon oxide is 200-400 mesh; dispersant is dispersant 5040; The wet agent includes CO-630; the thickener is hydroxyethyl cellulose; the defoamer is a silicone defoamer; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.

Embodiment 3

[0081] The third high weather resistance waterproof exterior wall coating for buildings provided in this embodiment comprises the following components in parts by mass:

[0082] Fluorosilicone modified acrylic emulsion 45 parts

[0083] Epoxy modified acrylic emulsion 15 parts

[0084] Fluorosilane 10 parts

[0085] 10 parts of organic bentonite

[0086] Silicon oxide 10 parts

[0087] 20 parts of titanium dioxide

[0088] Auxiliary 1 part

[0089] 15 parts of water.

[0090] Wherein: the solid content of fluorosilicon-modified acrylic emulsion and epoxy-modified acrylic emulsion is 50%-60%; the average particle diameter of the organic bentonite and silicon oxide is 200-400 mesh; the dispersant is sodium hexametaphosphate; The wetting agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a highly weather-resistant waterproof exterior wall coating for buildings and a preparation method thereof, which comprises the following components: fluorine-silicon modified acrylic emulsion, epoxy-modified acrylic emulsion, fluorosilane, organic bentonite, silicon oxide, and titanium dioxide And auxiliary agent, wherein, described auxiliary agent comprises dispersant, wetting agent, thickener, defoamer, film-forming auxiliary agent and antifreezing agent. The preparation method includes the following steps: firstly mix organic bentonite, silicon oxide and titanium dioxide, then add fluorosilicon modified acrylic emulsion and epoxy modified acrylic emulsion to mix, then add additives and mix, and finally add fluorosilane . The highly weather-resistant waterproof exterior wall coating for buildings and the preparation method thereof have excellent waterproof performance, self-cleaning and washability, and are suitable for various external environments.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a highly weather-resistant waterproof exterior wall coating for buildings and a preparation method thereof. Background technique [0002] Architectural exterior wall coatings are coatings that are applied to the entire exterior wall of a building. Its main function is to decorate and protect the exterior wall, making the building look flat and beautiful, and at the same time protecting the building. Exterior wall paint needs to be exposed to the outdoor environment. Compared with interior wall paint, it faces a harsher environment, especially in some humid areas in the south, where the waterproof function of exterior wall paint is more demanding. [0003] In the prior art, acrylic emulsion is often used as the base material, and the prepared water-based acrylic paint has the advantages of moderate cost and good adjustability. However, the water-based acrylic paints on the marke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D151/08C09D7/61C09D7/63C09D7/62C09D5/08C09D7/20
CPCC09D133/04C09D7/61C09D7/63C09D7/62C09D5/08C09D7/70C09D7/20C08K2003/2241C08L51/08C08K13/06C08K5/5419C08K9/04C08K3/346C08K3/36C08K3/22C08K7/24
Inventor 徐洪涛
Owner 徐洪涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com