A kind of waterproof and thermal insulation exterior wall paint for building and preparation method thereof

A technology for thermal insulation of exterior walls and buildings, applied in the direction of coating, etc., can solve the problems of reducing the service life of buildings, affecting the aesthetics of buildings, and easy penetration into walls, etc., to achieve increased gloss, more surface active sites, Overcome the hot sticky cold crisp effect

Active Publication Date: 2021-09-21
王洪磊
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-based acrylic paints on the market are often hot, sticky and brittle. In the dry environment below 0°C for a long time in northern my country, it is easy to crack, and the paint needs to play a certain role in heat preservation. In the warm and humid southern my country In the environment, water vapor, rainwater, etc. are easy to penetrate into the wall and corrode the wall, which not only affects the aesthetics of the building, but also reduces the service life of the building

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The first waterproof and thermal insulation exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:

[0034] Fluorosilicone modified acrylic emulsion 50 parts

[0035] Graphene-acrylic composite emulsion 25 parts

[0036] Fluorosilane 15 parts

[0037] 15 parts of silica sol

[0038] Activated carbon fiber powder 15 parts

[0039] 25 parts of titanium dioxide

[0040] Auxiliary 5 parts

[0041] 25 parts of water.

[0042] Wherein: the solid content of fluorosilicon modified acrylic acid emulsion and graphene-acrylic acid composite emulsion is 50%-60%; the average particle diameter of described activated carbon fiber powder is 200-400 mesh; dispersant is sodium hexametaphosphate; wetting The agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is dodecyl alcohol ester; the antifreeze is ethylene glycol.

Embodiment 2

[0044] The second waterproof and thermal insulation exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:

[0045] Fluorosilicone modified acrylic emulsion 50 parts

[0046] 20 parts of graphene-acrylic composite emulsion

[0047] Fluorosilane 20 parts

[0048] 20 parts of silica sol

[0049] Activated carbon fiber powder 20 parts

[0050] 30 parts of titanium dioxide

[0051] Auxiliary 8 parts

[0052] 35 parts of water.

[0053]Among them: the solid content of fluorosilicon modified acrylic emulsion and graphene-acrylic composite emulsion is 50%-60%; the average particle size of the activated carbon fiber powder is 200-400 mesh; the dispersant is dispersant 5040; the wetting agent Including CO-630; thickener is hydroxyethyl cellulose; defoamer is silicone defoamer; film-forming aid is dodecyl alcohol ester; antifreeze is ethylene glycol.

Embodiment 3

[0055] The third waterproof and thermal insulation exterior wall coating for buildings provided by this embodiment includes the following components in parts by mass:

[0056] Fluorosilicone modified acrylic emulsion 45 parts

[0057] 15 parts of graphene-acrylic composite emulsion

[0058] Fluorosilane 10 parts

[0059] 10 parts of silica sol

[0060] Activated carbon fiber powder 10 parts

[0061] 20 parts of titanium dioxide

[0062] Auxiliary 1 part

[0063] 15 parts of water.

[0064] Wherein: the solid content of fluorosilicon modified acrylic acid emulsion and graphene-acrylic acid composite emulsion is 50%-60%; the average particle diameter of described activated carbon fiber powder is 200-400 mesh; dispersant is sodium hexametaphosphate; wetting The agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is dodecyl alcohol ester; the antifreeze is ethylene glycol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a waterproof and thermal insulation exterior wall coating for buildings and a preparation method thereof. Auxiliaries, wherein the adjuvants include dispersants, wetting agents, thickeners, defoamers, film-forming aids and antifreezing agents. The preparation method of the waterproof and thermal insulation exterior wall coating for buildings comprises the following steps: firstly mix the silica sol, activated carbon fiber powder and titanium dioxide, then add the fluorosilicon modified acrylic emulsion and the graphene-acrylic composite emulsion to mix evenly, then add the auxiliary Agent mixing, and finally mixed with fluorosilane. The waterproof and thermal insulation exterior wall coating for buildings has excellent waterproof and thermal insulation properties, self-cleaning and washable, and is suitable for various external environments.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a waterproof and thermal insulation exterior wall coating for buildings and a preparation method thereof. Background technique [0002] Architectural exterior wall coatings are coatings that are applied to the entire exterior wall of a building. Its main function is to decorate and protect the exterior wall, making the building look flat and beautiful, and at the same time protecting the building. Exterior wall paint needs to be exposed to the outdoor environment. Compared with interior wall paint, it faces a harsher environment, especially in some humid areas in the south, where the waterproof function of exterior wall paint is more demanding. [0003] In the prior art, acrylic emulsion is often used as the base material, and the prepared water-based acrylic paint has the advantages of moderate cost and good adjustability. However, the water-based acrylic paints on the market ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/10C09D7/61C09D7/63
CPCC09D143/04C09D7/61C09D7/70C09D7/63C08K2201/005C08L2205/035C08L33/10C08K13/06C08K3/36C08K3/042C08K7/26C08K5/54
Inventor 王洪磊
Owner 王洪磊
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com