High-weather-resistance waterproof exterior wall coating for buildings and preparation method thereof
An exterior wall coating, high weather resistance technology, applied in anti-corrosion coatings, coatings and other directions, can solve problems such as affecting the aesthetics of buildings, reducing the service life of buildings, and easily infiltrating into walls, etc., to achieve protection from damage and gloss. The effect of improving, enhancing strength and corrosion resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0059] The first high weather resistance waterproof exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:
[0060] Fluorosilicone modified acrylic emulsion 50 parts
[0061] Epoxy modified acrylic emulsion 25 parts
[0062] Fluorosilane 15 parts
[0063] 15 parts of organic bentonite
[0065] 25 parts of titanium dioxide
[0066] Auxiliary 5 parts
[0067] 25 parts of water.
[0068] Wherein: the solid content of fluorosilicon-modified acrylic emulsion and epoxy-modified acrylic emulsion is 50%-60%; the average particle diameter of the organic bentonite and silicon oxide is 200-400 mesh; the dispersant is sodium hexametaphosphate; The wetting agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.
Embodiment 2
[0070] The second high weather resistance waterproof exterior wall coating for buildings provided by this embodiment comprises the following components in parts by mass:
[0071] Fluorosilicone modified acrylic emulsion 50 parts
[0072] Epoxy modified acrylic emulsion 20 parts
[0073] Fluorosilane 20 parts
[0074] 20 parts of organic bentonite
[0075] Silicon oxide 20 parts
[0076] 30 parts of titanium dioxide
[0077] Auxiliary 8 parts
[0078] 35 parts of water.
[0079] Wherein: the solid content of fluorosilicon modified acrylic emulsion and epoxy modified acrylic emulsion is 50%-60%; the average particle diameter of described organic bentonite and silicon oxide is 200-400 mesh; dispersant is dispersant 5040; The wet agent includes CO-630; the thickener is hydroxyethyl cellulose; the defoamer is a silicone defoamer; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.
Embodiment 3
[0081] The third high weather resistance waterproof exterior wall coating for buildings provided in this embodiment comprises the following components in parts by mass:
[0082] Fluorosilicone modified acrylic emulsion 45 parts
[0083] Epoxy modified acrylic emulsion 15 parts
[0084] Fluorosilane 10 parts
[0085] 10 parts of organic bentonite
[0086] Silicon oxide 10 parts
[0087] 20 parts of titanium dioxide
[0088] Auxiliary 1 part
[0089] 15 parts of water.
[0090] Wherein: the solid content of fluorosilicon-modified acrylic emulsion and epoxy-modified acrylic emulsion is 50%-60%; the average particle diameter of the organic bentonite and silicon oxide is 200-400 mesh; the dispersant is sodium hexametaphosphate; The wetting agent is CO-630; the thickener is hydroxyethyl cellulose; the defoamer is mineral oil; the film-forming aid is lauryl alcohol ester; the antifreeze is ethylene glycol.
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com