Biodegradable polyester and preparation method thereof

A biodegradable polyester and esterification technology, applied in the preparation of carboxylate, the preparation of organic compounds, chemical instruments and methods, etc., can solve the problems of increasing production costs, complex catalyst preparation processes, and small molecule residues.

Active Publication Date: 2021-03-19
FUHAI (DONGYING) ADVANCED MATERIAL TECH CO LTD
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] To sum up, the method of reducing the acid value of PBAT products in the prior art is mainly to add expensive carboxyl-terminated scavengers and carbodiimide anti-hydrolysis agents, which not only increases the production cost, but also has the precipitation of small molecules, and the product application is affected. limit problem
In addition, by preparing a highly efficient hydrolysis-resistant catalyst to reduce the amount of the catalyst, this method has

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biodegradable polyester and preparation method thereof
  • Biodegradable polyester and preparation method thereof
  • Biodegradable polyester and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0057] The invention provides a kind of preparation method of biodegradable polyester, it comprises the steps:

[0058] First carry out esterification-precondensation, then carry out copolycondensation and final polycondensation.

[0059] Specifically, esterification-precondensation includes: using methanesulfonic acid as an esterification catalyst, catalyzing the esterification reaction of terephthalic acid (PTA) and 1,4-butanediol (BDO), removing methyl After sulfonic acid, add a titanium-based catalyst for pre-condensation to obtain oligoesterification (BHBT) of terephthalic acid and 1,4-butanediol;

[0060] Use methanesulfonic acid as the catalyst for esterification reaction to catalyze the esterification reaction of 1,6-adipic acid (AA) and 1,4-butanediol. After removing methanesulfonic acid, add titanium catalyst for precondensation , to obtain the oligoesterification of 1,6-adipic acid and 1,4-butanediol (BHBA);

[0061] Co-polycondensation includes: co-condensation o...

Embodiment 1

[0110] Table 1 The feed list of Example 1.

[0111]

[0112] The present embodiment provides a kind of preparation method of biodegradable polyester, comprises following steps carried out in sequence:

[0113] (1) Esterification-precondensation:

[0114] Weighed 1661.7g of terephthalic acid (wt%≥99.90%), 994.3g of 1,4-butanediol (wt%≥99.70%) and 67.1g of methanesulfonic acid (wt%≥99.00%) ) into 10L esterification kettle 1, turn on the heating, stir evenly, raise the temperature to 180°C, carry out the esterification and dehydration reaction, and react for 2 hours. , Reaction 0.5h, removal of methanesulfonic acid.

[0115] Then adjust the temperature, add 0.54g tetrabutyl titanate, the reaction temperature is 200°C, the reaction pressure is 100KPa, pre-condensation is carried out, the reaction is 0.6h, and the molecular weight is measured by sampling.

[0116] Weighed 1789.4g of 1,6-hexanedioic acid (wt%≥99.80%), 1213.0g of 1,4-butanediol (wt%≥99.70%) and 105g of methanes...

Embodiment 2

[0121] Table 2 Feeding table of Example 2.

[0122]

[0123] The present embodiment provides a kind of preparation method of biodegradable polyester, comprises following steps carried out in sequence:

[0124] (1) Esterification-precondensation:

[0125] Weighed 1661.7g of terephthalic acid (wt%≥99.90%), 994.3g of 1,4-butanediol (wt%≥99.70%) and 67.1g of methanesulfonic acid (wt%≥99.00%) ) into 10L esterification kettle 1, turn on the heating, stir evenly, raise the temperature to 180°C, carry out the esterification and dehydration reaction, and react for 2 hours. , Reaction 0.5h, removal of methanesulfonic acid.

[0126] Then adjust the temperature, add 0.66g of tetrabutyl titanate, the reaction temperature is 200°C, the reaction pressure is 100KPa, carry out pre-polycondensation, react for 0.5h, and take samples for molecular weight detection.

[0127] Weighed 1789.4g of 1,6-hexanedioic acid (wt%≥99.80%), 1213.0g of 1,4-butanediol (wt%≥99.70%) and 105g of methanesulfon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses biodegradable polyester and a preparation method thereof, and relates to the technical field of biodegradable materials. According to the method, methanesulfonic acid replacestitanate which is easy to hydrolyze to serve as the catalyst in the esterification reaction stage for generating a large amount of water, then the titanate catalyst is added in batches during pre-polycondensation and copolycondensation reaction without generating water, catalyst hydrolysis is avoided, the use amount of the catalyst is reduced, and therefore PBAT thermal degradation reaction is effectively inhibited, the acid value of the product is reduced, and the acid value of the prepared PBAT is smaller than 15mol/t. The block copolymer with a longer BHBT and BHBA chain segment structure can be obtained by firstly carrying out pre-polycondensation after esterification and then carrying out co-polycondensation, the regularity of the molecular chain structure is higher than that of PBATprepared by a traditional random copolymerization method, and the mechanical property of PBAT resin is better due to the BHBT chain segment with a longer hard segment structure in the molecular structure.

Description

technical field [0001] The invention relates to the technical field of biodegradable materials, in particular to a biodegradable polyester and a preparation method thereof. Background technique [0002] With the increasing white pollution, biodegradable polyester has become one of the most effective solutions to the problem of plastic pollution. Biodegradable polyester can be degraded into environmentally harmless carbon dioxide and water under composting conditions or natural conditions. Among biodegradable polyesters, polybutylene terephthalate-co-polybutylene adipate (PBAT) is a combination of butylene adipate (PBA) and butylene terephthalate (PBT) copolymer, the structure of the copolymer has both rigid and flexible segments, not only has high ductility and elongation at break, but also has good heat resistance and impact resistance, and blown film Good, good biodegradability, is one of the current research hotspots. [0003] There are water-sensitive ester groups in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G63/85C08G63/183C07C67/08C07C69/82C07C69/44B01J31/02
CPCB01J31/0225B01J2231/49C07C67/08C08G63/183C08G63/85C08G2230/00C07C69/82C07C69/44
Inventor 王敏岳林黄森彪廖广明
Owner FUHAI (DONGYING) ADVANCED MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka