Water-retaining agent, preparation method thereof, ceramic tile adhesive and preparation method thereof

A technology of water-retaining agent and tile adhesive, which is applied in the field of building materials, and can solve problems such as increasing the adjustable time of tile laying, prolonging the drying time, and poor adhesion of tile laying

Active Publication Date: 2021-04-20
GUANGDONG BOZHILIN ROBOT CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding a very small amount of water-retaining agent can significantly prolong the airing time, increase the adjustable time of tile laying, and solve the problems of poor adhesion and hollowing of tiles due to insufficient airing time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-retaining agent, preparation method thereof, ceramic tile adhesive and preparation method thereof
  • Water-retaining agent, preparation method thereof, ceramic tile adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0103] The present invention also provides a preparation method of water retaining agent, comprising the following steps:

[0104] Mix active agent, hyaluronic acid, alcohol and water;

[0105] In parts by weight, the addition amount of active agent, hyaluronic acid, alcohol and water is:

[0106] Active agent 4-7 parts;

[0107] Hyaluronic acid 24-70 parts;

[0108] Alcohol 45-200 parts;

[0109] 40-100 parts of water;

[0110] The active agent is selected from fatty alcohol polyoxyethylene ether sulfate and / or alkylbenzene sulfonate.

[0111] Preferably, the preparation method of the water-retaining agent of the present invention comprises the following steps:

[0112] Mix alcohol and water evenly in proportion, dissolve the active agent in the mixture of alcohol and water, then mix in hyaluronic acid, stir evenly, cool, dry, slice, granulate and sieve to obtain a water-retaining agent, and dry The distilled alcohol can be reused after recovery.

[0113] The invention...

Embodiment 1

[0163] This embodiment provides a water-retaining agent and a method for preparing the water-retaining agent, and a tile adhesive and a method for preparing the tile adhesive.

[0164] (1) In parts by weight, the formula of water retaining agent A is as follows:

[0165] 5 parts aluminum dodecylbenzene sulfonate, 30 parts hyaluronic acid, 50 parts ethanol and 50 parts water.

[0166] (2) The preparation method of water retaining agent A is as follows:

[0167] Mix water and ethanol, then dissolve aluminum dodecylbenzenesulfonate in ethanol aqueous solution, then mix in hyaluronic acid, stir thoroughly, cool, dry, slice, granulate and sieve to obtain water retaining agent A .

[0168] (3) In parts by weight, the formula of tile adhesive A is as follows:

[0169] 350 parts of P.O 42.5 Portland cement; 250 parts of sand with a fineness of 22-40 mesh; 350 parts of sand with a fineness of 70-140 mesh; 12 parts of Wacker rubber powder 5010N; 0.1 part of water retaining agent A an...

Embodiment 2

[0174] This embodiment provides a water-retaining agent and a method for preparing the water-retaining agent, and a tile adhesive and a method for preparing the tile adhesive.

[0175] (1) In parts by weight, the formula of water retaining agent B is as follows:

[0176] 5 parts aluminum dodecylbenzene sulfonate, 30 parts hyaluronic acid, 50 parts ethanol and 50 parts water.

[0177] (2) The preparation method of water retaining agent B is as follows:

[0178] Mix water and ethanol, then dissolve aluminum dodecylbenzenesulfonate in ethanol aqueous solution, then mix in hyaluronic acid, stir thoroughly, cool, dry, slice, granulate and sieve to obtain water retaining agent B . The water-retaining agent B in this implementation is the same as the water-retaining agent A in Example 1.

[0179] (3) In parts by weight, the formula of tile adhesive B is as follows:

[0180] 350 parts of P.O 42.5 Portland cement; 250 parts of sand with a fineness of 22-40 mesh; 350 parts of sand w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a water-retaining agent, a preparation method thereof, a ceramic tile adhesive and a preparation method thereof. The invention belongs to the technical field of building materials. The water-retaining agent comprises the following components in parts by weight: 4-7 parts of active agent; 24-70 parts of hyaluronic acid; 45-200 parts of alcohol; and 40-100 parts of water. The active agent is selected from fatty alcohol-polyoxyethylene ether sulfate and / or alkylbenzene sulfonate. The water-retaining agent is good in water-retaining effect, long in airing time and good in moisture absorption effect. When the ceramic tile adhesive is prepared, a very small amount of the water-retaining agent is added, so that the airing time can be remarkably prolonged, the adjustable time during the paving of the ceramic tile is prolonged, and the problems of poor ceramic tile paving bonding force and ceramic tile hollowing caused by insufficient airing time are solved. And moreover, the hydration reaction degree of the ceramic tile adhesive can be enhanced, the setting time is not influenced, and the later strength is favorably improved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a water-retaining agent, a tile glue and a preparation method thereof. Background technique [0002] Tiles are one of the commonly used decorative materials for walls and floors in the construction industry. At present, tile adhesives are widely used as adhesives for pasting tiles. The largest amount of tile adhesives on the market is cement-based dry powder products with admixtures such as dispersible latex powder. The manual construction process of laying tiles with tile glue includes plastering and scraping teeth on the wall and floor, scraping the back of the tiles, and then laying tiles. However, in the process of laying tiles, in order to improve the efficiency of laying, the general construction personnel will apply the slurry on a large area before laying the tiles. The high water absorption will cause the tile adhesive to lose water, and the hydration in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/38C04B28/04C04B103/46
Inventor 蓝柳波唐振中向青云
Owner GUANGDONG BOZHILIN ROBOT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com