A kind of alloy tool steel with corrosion resistance, high strength and high toughness, heat treatment method and production method thereof

A technology of alloy tool steel and heat treatment method, which is applied in the field of alloy tool steel with corrosion resistance, high strength and high toughness and its heat treatment, and can solve the problem that alloy tool steel wire rods do not have toughness, products and achievements are blank, and high strength and high toughness materials are few. problem, to achieve the effect of excellent wear resistance, good wear resistance, good strength and plastic toughness

Active Publication Date: 2022-04-01
MAANSHAN IRON & STEEL CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The shortcoming of this method is that the final structure of the wire rod produced is martensite with poor plasticity, and the alloy tool steel wire rod does not have good toughness
[0006] To sum up, although there are many studies on alloy tool steel products in my country and the products are relatively mature, there are few high-strength and high-toughness materials that take into account corrosion resistance, and their products and achievements are almost blank

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of alloy tool steel with corrosion resistance, high strength and high toughness, heat treatment method and production method thereof
  • A kind of alloy tool steel with corrosion resistance, high strength and high toughness, heat treatment method and production method thereof
  • A kind of alloy tool steel with corrosion resistance, high strength and high toughness, heat treatment method and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0048] The corrosion-resistant, high-strength and high-toughness alloy tool steel provided by the invention contains the following chemical components by weight percentage: C 0.70%-1.00%, Si 0.80%-1.10%, Mn 0.50%-0.80%, Cr 0.50%-0.80%, Mo0.30%~0.50%, V 0.20%~0.40%, Nb 0.020%~0.040%, Ti 0.030%~0.050%, Ni0.15%~0.35%, Cu 0.15%~0.35%, Re 0.05%~0.25% , P trace ~0.015%, S trace ~0.015%, O≤0.0015%, N≤0.006%. The rest is Fe and other unavoidable impurities; among them, 0.50W+0.50Mo+0.26Cr+V+Nb≤1.5C.

[0049] The production method of alloy tool steel with corrosion resistance, high strength and high toughness includes the following steps: electric furnace smelting → LF furnace refining → RH or VD vacuum degassing → bloom continuous casting → billet rolling → finishing peeling → heating → high-speed wire rod controlled rolling Manufacturing→Stelmore cooling by wire controlled cooling→Finished wire rod and wire rod→Spheroidizing annealing→Quenching→Tempering;

[0050] Among them, in th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
fatigue strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a corrosion-resistant, high-strength and high-toughness alloy tool steel and a heat treatment method and production method thereof. %, Cr 0.50% to 0.80%, Mo 0.30% to 0.50%, V 0.20% to 0.40%, Nb 0.020% to 0.040%, Ti 0.030% to 0.050%, Ni 0.15% to 0.35%, Cu 0.15% to 0.35% , Re 0.05%~0.25%, traces of P, S, O, N, the rest are Fe and other inevitable impurities; 0.50W+0.50Mo+0.26Cr+V+Nb≤1.5C; it has good strength , plastic toughness, wear resistance, impact resistance and corrosion resistance, can meet the requirements of use.

Description

technical field [0001] The invention belongs to the technical field of tool steel, and in particular relates to a corrosion-resistant, high-strength, high-toughness alloy tool steel, a heat treatment method and a production method thereof. Background technique [0002] Tool steel is a type of steel used to manufacture various cutting tools, measuring tools, molds and wear-resistant tools, and is widely used in various industries such as machinery manufacturing. Due to its use characteristics, tool steel is required to have high strength, high hardness, high red hardness, high toughness, high wear resistance, high fatigue performance, etc. after heat treatment. According to the chemical composition, tool steel can be divided into carbon tool steel, alloy tool steel and high-speed tool steel. Alloy tool steel has better hardenability than carbon tool steel due to the addition of alloy elements such as Cr, Mo, W, V, etc. Hardenability, wear resistance and toughness have a wide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50C22C38/42C21D1/18C21D1/32C21D8/06
CPCC22C38/02C22C38/04C22C38/44C22C38/46C22C38/48C22C38/50C22C38/42C22C38/005C21D1/18C21D1/32C21D8/065C21D2211/008
Inventor 张晓瑞汪开忠于同仁姜婷尹德福龚梦强郭湛丁雷余良其孙凯许文喜
Owner MAANSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com