Jewelry and surface treatment method thereof

A surface treatment and jewelry technology, applied in clothing, application, jewelry and other directions, can solve the problems of increasing the complexity of surface treatment of jewelry products, unable to enameled metal surface effect or texture rendering, etc., to achieve the effect of colorful and colorful

Pending Publication Date: 2021-11-02
广东顺德周大福珠宝制造有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The enamel color of existing jewelry products is usually relatively flat, and the metal surface effect or texture under the enamel cannot be clearly presented
Furthermore, if enamel is fired at high temperature on the surface of existing jewelry items, the processing temperature is usually around 1000°C (Celsius), which increases the complexity of the surface treatment of jewelry items

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Jewelry and surface treatment method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described below with reference to the embodiments shown in the drawings.

[0023] like figure 1 As shown, the surface treatment method of the jewelry proposed by the present invention includes the following steps:

[0024] (1) After mixing the transparent low temperature enamel and the curing agent, the first heating and drying treatment are performed to obtain an initial glaze. Among them, the role of the curing agent is to promote the solidification and hardening of the target glaze in the subsequent step. If the curing agent is lacking, the target glaze is applied to the surface of the jewelry and cannot be solidified and hardened. The role of the first heating and drying process is to increase the fluidity of the target glaze, thereby easy to glaze in the subsequent steps.

[0025] (2) Treatment of the initial glaze to obtain a target glaze. Among them, a vacuum bubble within the glaze can be discharged by vacuum processing of the i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses jewelry and a surface treatment method thereof. The surface treatment method of the jewelry comprises the following steps: mixing transparent low-temperature enamel glaze and a curing agent and then performing first heating and drying treatment, and obtaining initial glaze; performing vacuum treatment on the initial glaze to obtain a target glaze; coating the target glaze on the surface of the jewelry; and carrying out second heating and drying treatment or air drying treatment on the coated jewelry. The jewelry is obtained by adopting the surface treatment method. The surface effect or texture of the jewelry under the enamel can be clearly presented, the unique effect of the surface of the jewelry can be reserved, and clear and colorful colors are added.

Description

Technical field [0001] The present invention belongs to the field of jewelry processing, and more particularly to a jewelery and a surface treatment method thereof. Background technique [0002] Existing jewelry types, its enamel color is usually relatively flat, and it is unable to show the metal surface effect or texture under the enamel. Further, if enamel is high temperature on the surface of the existing jewelry type, the processing temperature is usually around 1000 ° C (degrees Celsius), thereby increasing the complexity of the surface treatment of the jewelry type. Inventive content [0003] It is an object of the present invention to provide a jewelery and a surface treatment method, which can clearly presented the jewelry surface effect or texture under the enamel, not only to retain the unique effect of the jewelry surface, but also Add a colorful color of the clear. [0004] In order to solve the above technical problem, the present invention adopts the surface treat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A44C27/00
CPCA44C27/007
Inventor 廖娟娟
Owner 广东顺德周大福珠宝制造有限公司