Fluorescent artificial fish island reef and preparation method thereof

A technology of artificial fish and island reefs, applied in fish farming, sustainable waste treatment, animal husbandry, etc., to achieve the effect of improving economic attributes, good durability, and good economy

Inactive Publication Date: 2021-12-21
广西源盛矿渣综合利用有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to propose a new fluorescent artificial fish island and its preparation method in view of the problems existing in the above-mentioned existing artificial fish islands and reefs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorescent artificial fish island reef and preparation method thereof
  • Fluorescent artificial fish island reef and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Artificial reef fish fluorescent Example 1 of the present invention, the use of raw materials comprising: a steel slag, slag powder, cement, stone made fluorescent resin, 0-5mm aggregate particle size slag, steel slag aggregate particle diameter of 0-10mm and water, wherein the components and their mass per unit volume is: steel slag 50kg / m 3 , Slag powder, 350kg / m 3 Cement 50kg / m 3 , Made fluorite resin 300kg / m 3 , 0-5mm aggregate particle size slag 500kg / m 3 , 0-10mm diameter slag aggregate 1300kg / m 3 , Water 210kg / m 3 The total density of 2760kg / m 3 .

[0037] The present inventors, for the artificial fish reef fluorescent Example 1 were tested for their compressive strength in the case of 7 and 28 days, the results show that the compressive strength of 25MPa 7 days, 28 days anti compressive strength of 35MPa.

Embodiment 2

[0039] Artificial reef fish fluorescent Example 2 of the present invention, the use of raw materials comprising: a steel slag, slag powder, cement, stone made fluorescent resin, 0-5mm aggregate particle size slag, steel slag aggregate particle diameter of 0-10mm and water, specifically, the components and their mass per unit volume is: steel slag 50kg / m 3 , Slag powder, 350kg / m 3 Cement 50kg / m 3 , Made fluorite resin 300kg / m 3 , 0-5mm aggregate particle size slag 600kg / m 3 , 0-10mm diameter slag aggregate 1200kg / m 3 , Water 210kg / m 3 The total density of 2760kg / m 3 .

[0040]The present inventors, for the artificial fish reef fluorescent Example 2 were tested for their compressive strength in the case of 7 and 28 days, the results show that the compressive strength of 26MPa 7 days, 28 days anti compressive strength of 35MPa.

Embodiment 3

[0042] Artificial reef fish fluorescent Example 3 of the present invention, the use of raw materials comprising: a steel slag, slag powder, cement, stone made fluorescent resin, 0-5mm aggregate particle size slag, steel slag aggregate particle diameter of 0-10mm and water, specifically, the components and their mass per unit volume is: steel slag 50kg / m 3 , Slag powder, 340kg / m 3 Cement 50kg / m 3 , Made fluorite resin 400kg / m 3 , 0-5mm aggregate particle size slag 500kg / m 3 , 0-10mm diameter slag aggregate 1200kg / m 3 , Water 210kg / m 3 The total density of 2750kg / m 3 .

[0043] The present inventors, for the artificial fish reef fluorescent Example 3 were tested for their compressive strength in the case of 7 and 28 days, the results show that the compressive strength of 25MPa 7 days, 28 days anti compressive strength of 36MPa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fluorescent artificial fish island reef and a preparation method thereof. The fluorescent artificial fish island reef comprises the following components: 50-70kg / m <3> of steel slag powder, 300-350kg / m <3> of slag powder, 30-50kg / m <3> of cement, 300-500kg / m < 3 > of self-made fluorescent stone resin, 500-600kg / m < 3 > of steel slag aggregate with the particle size of 0-5mm, 1,200-1,300kg / m <3> of steel slag aggregate with the particle size of 0-10mm and 190-210kg / m <3> of water. The preparation method comprises the following steps: uniformly mixing the fluorescent stone resin and the steel slag aggregate to form a mixture A, pouring the steel slag powder and the slag powder into the mixture A to form a uniform mixture B, finally pouring water into the mixture B to form uniform slurry C, pouring the slurry C into a mold with a corresponding shape, and removing the mold after one day to obtain the fluorescent artificial fish island reef. The artificial fish island reef is high in strength, good in durability and good in economical efficiency, fluorescence emitted at the seabed has certain guidance quality, fishes are attracted to lay eggs, and the economic attribute of the artificial fish island reef is improved.

Description

Technical field [0001] Preparation of industrial waste and resource utilization FIELD The present invention relates to a fluorescent artificial fish reefs, particularly to a phosphor and a preparation method of artificial reef fish. Background technique [0002] Artificial reefs are artificial structures set up in the sea, which aims to improve the marine ecological environment, and create a favorable environment for marine habitats, such as to provide for fish breeding, growing, feeding and shelter enemy place, to protect, and proliferation the purpose of improving catches. At home and abroad have carried out extensive artificial reef construction, repair coastal marine habitat and fisheries, and achieved good results. [0003] However, the prior art, there is now an artificial fish reefs two issues: first, most of the artificial fish reefs cementitious material is cement, natural sand and gravel aggregate is not only costly, and hydration products of cement CSH gel in addition,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): C04B28/00A01K61/70C04B18/14C04B111/74
CPCC04B28/00A01K61/70C04B18/142C04B18/141C04B2111/74C04B2111/807C04B2111/00758C04B2201/20C04B2201/50C04B20/1033Y02A40/81Y02W30/91
Inventor李端乐刘传胜段崇国崔勇
Owner广西源盛矿渣综合利用有限公司