Corrosion-resistant and wear-resistant silicon carbide composite material protective agent and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A kind of wear-resistant silicon carbide, composite material technology
Inactive Publication Date: 2021-12-28
林存华
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The purpose of the present invention is to provide an anti-corrosion and wear-resistant silicon carbide composite protective agent and its preparation method, aiming to solve the problem in the prior art that in the domestic industrial production process, there are generally strong acids and alkalis plus the influence of temperature, extreme The operating environment leads to the problem that the life of related equipment is greatly reduced
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0027] The invention provides the following technical solutions:
[0028] An anti-corrosion and wear-resistant silicon carbide composite protective agent, the coating agent includes the following raw material formula in parts by weight: 20 parts of vinyl resin, 1 part of curing agent, 160 parts of silicon carbide, 20 parts of aluminum oxide, sepiolite mineral 15 parts of fiber, 1 part of emulsifier, 20 parts of filler, 3 parts of viscosifier.
[0029] In a specific embodiment of the present invention, samples are taken in parts by weight, and the surfaces of 160 parts of silicon carbide, 20 parts of aluminum oxide, and 20 parts of filler are cleaned with a dry cleaning cloth for use; after cleaning, 160 parts of carbonized Put silicon, 20 parts of aluminum oxide, and 20 parts of filler into a mixer and mix evenly; put 160 parts of silicon carbide, 20 parts of aluminum oxide, and 20 parts of filler into a ball mill for grinding, and grind the powder Put it into the sieving mac...
Embodiment 2
[0049] An anti-corrosion and wear-resistant silicon carbide composite protective agent, the coating agent includes the following raw material formula in parts by weight: 35 parts of vinyl resin, 10 parts of curing agent, 280 parts of silicon carbide, 50 parts of aluminum oxide, sepiolite mineral 20 parts of fiber, 8 parts of emulsifier, 35 parts of filler, 7 parts of viscosifier.
[0050] The preparation method of Example 2 is the same as that of Example 1, except that the weight parts of the raw materials are different, and will not be repeated here.
Embodiment 3
[0052] An anti-corrosion and wear-resistant silicon carbide composite protective agent, the coating agent includes the following raw material formula in parts by weight: 25 parts of vinyl resin, 2 parts of curing agent, 240 parts of silicon carbide, 30 parts of aluminum oxide, sepiolite mineral 17 parts of fiber, 2 parts of emulsifier, 23 parts of filler, 4 parts of viscosifier.
[0053] The preparation method of Example 3 is the same as that of Example 1, except that the weight parts of the raw materials are different, and will not be repeated here.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention provides a corrosion-resistant and wear-resistant silicon carbide composite material protective agent and a preparation method thereof, and belongs to the technical field of wear-resistant protective agents. The corrosion-resistant and wear-resistant silicon carbide composite material protective agent is prepared from the following raw materials in parts by weight: 20 to 35 parts of vinyl resin, 1 to 10 parts of curing agent, 160 to 280 parts of silicon carbide, 20 to 50 parts of aluminum oxide, 15 to 20 parts of sepiolite mineral fiber, 1 to 8 parts of emulsifier, 20 to 35 parts of filler and 3 to 7 parts of tackifier. The protective agent contains vinyl resin, aluminum oxide, silicon carbide, sepiolite mineral fibers and the like, and when the protective agent is applied to a surface needing to be protected, the effect of prolonging the service life of equipment can be achieved, and the problem that in the industrial production process, the service life of related equipment is greatly shortened due to the influence of strong acid, strong alkali and temperature and the extreme operating environment is solved.
Description
technical field [0001] The invention belongs to the technical field of anti-wear protective agents, and in particular relates to an anti-corrosion and wear-resistant silicon carbide composite material protective agent and a preparation method thereof. Background technique [0002] Anti-wear protective agent, widely used in the repair of various wear parts and the preparation of wear-resistant and anti-corrosion coatings on the surface of various parts that require wear resistance and corrosion resistance, such as pump bodies, impellers, Repair and pre-protection of fan casings, pipe elbows, pipe augers, etc. [0003] In the domestic industrial production process, strong acid and strong alkali are common, coupled with the influence of temperature, and the extreme operating environment has greatly shortened the life of related equipment. Contents of the invention [0004] The purpose of the present invention is to provide an anti-corrosion and wear-resistant silicon carbide...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.