UV light-cured wood coating and preparation method thereof

A technology of wood coatings and mixtures, applied in the field of coatings, which can solve problems such as strong odor and damage, and achieve the effect of good viscosity and fast curing speed

Pending Publication Date: 2022-04-08
濮阳展辰新材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Combined with market feedback, higher requirements are put forward for the additional effects of UV-curable coatings, especially for odor; the existing UV-curable coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • UV light-cured wood coating and preparation method thereof
  • UV light-cured wood coating and preparation method thereof
  • UV light-cured wood coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0038] Example 1

[0039] The present embodiment provides a kind of woodware coating, by weight, its formula is as follows:

[0040]

[0041] The present embodiment simultaneously provides the preparation method of the above-mentioned woodware coating, comprising the following steps:

[0042] (1) Epoxy acrylate 621-100, TMPTA, TPGDA, TPO and active amine are dispersed for 15min at 1500r / min to obtain mixture I;

[0043] (2) Disperse the mixture I, dispersant and defoamer for 8min at 1200r / min to obtain mixture II;

[0044] (3) Disperse the mixture II and talc at 1200 r / min for 20 min to obtain.

Example Embodiment

[0045] Example 2

[0046] The present embodiment provides a kind of woodware coating, by weight, its formula is as follows:

[0047]

[0048] The present embodiment simultaneously provides the preparation method of the above-mentioned woodware coating, comprising the following steps:

[0049] (1) disperse modified bisphenol A epoxy acrylate 6100D-85, TMPTA, TPGDA, PBZ and active amine for 15min at 1500r / min to obtain mixture I;

[0050] (2) Disperse the mixture I, dispersant and defoamer for 8min at 1200r / min to obtain mixture II;

[0051] (3) Disperse the mixture II and talc at 1200 r / min for 20 min to obtain.

Example Embodiment

[0052] Example 3

[0053] The present embodiment provides a kind of woodware coating, by weight, its formula is as follows:

[0054]

[0055]

[0056] The present embodiment simultaneously provides the preparation method of the above-mentioned woodware coating, comprising the following steps:

[0057] (1) Epoxy acrylate 621-100, TMPTA, TPGDA, OMBB and active amine are dispersed for 15min at 1500r / min to obtain mixture I;

[0058] (2) Disperse the mixture I, dispersant and defoamer for 8min at 1200r / min to obtain mixture II;

[0059] (3) Disperse the mixture II and talc at 1200 r / min for 20 min to obtain.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of coatings, in particular to a UV light-cured wood coating and a preparation method thereof. The wood coating comprises the following components in parts by weight: 20-50 parts of resin, 20-40 parts of a monomer and 3-7 parts of an initiator, wherein the resin is epoxy acrylate or modified bisphenol A epoxy acrylate; the monomer is a mixture of trimethylolpropane triacrylate and diethylene glycol diacrylate; the initiator is a mixture of active amine and one or more of TPO, PBZ and OMBB. The wood coating provided by the invention can be cured under UV light, and the wood coating can realize complete odor removal; meanwhile, the wood coating has good viscosity, heat resistance, stability, leveling property and adhesive force, and relatively high curing speed.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a UV light-cured wood coating and a preparation method thereof. Background technique [0002] In recent years, UV-curable coatings have been rapidly developed and widely used in wood furniture and other fields. Combined with market feedback, higher requirements are put forward for the additional effects of UV-curable coatings, especially for odor; the existing UV-curable coatings have a relatively strong odor, so apply them to children's study tables, wardrobe interior panels, etc. When entering the field, it will cause certain damage to the human body. Therefore, it is a technical problem that those skilled in the art urgently need to solve to develop a low-odor or even clean-taste UV-curable coating. [0003] In view of this, the present invention is proposed. Contents of the invention [0004] The object of the present invention is to provide a kind of wood coating, the residual s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/10
Inventor 范学庆陈寿生罗先平
Owner 濮阳展辰新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap