Polyurethane elastomer material as well as preparation method and application thereof

A polyurethane elastomer and modified technology, applied in the field of wear-resistant materials, can solve the problems of wear of soles, unsuitable wear, and poor slip resistance, so as to improve wear resistance, strengthen connection, and prolong storage period and service life. Effect

Pending Publication Date: 2022-06-28
锋特(福建)新材料科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] But generally speaking, the soles made of conventional polyurethane elastomer materials will be severely worn and the slip resistance will deteriorate after two or three years of use, which is not suitable for wearing.
[0005] For the related technologies mentioned above, the inventors found that the wear resistance of polyurethane elastomer materials needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane elastomer material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0047] A preparation method of modified montmorillonite, comprising the following steps:

[0048] Add 10kg of common montmorillonite to 90kg of water while stirring to obtain a suspension, heat the suspension to 80°C, add 50kg of acrylamide to the suspension while stirring under heating conditions, continue stirring for 30min, and filter to obtain modified montmorillonite earth.

preparation example 2

[0050] A preparation method of modified montmorillonite, comprising the following steps:

[0051]Add ordinary montmorillonite to 105kg of water while stirring to obtain a suspension, heat the suspension to 90°C, add 75kg of acrylamide to the suspension while stirring under heating conditions, continue stirring for 40min, and filter to obtain modified montmorillonite .

preparation example 3

[0053] A preparation method of modified montmorillonite, comprising the following steps:

[0054] Add 11kg of common montmorillonite to 100kg of water while stirring to obtain a suspension, heat the suspension to 85°C, add 55kg of acrylamide to the suspension while stirring under heating conditions, continue stirring for 35min, and filter to obtain modified montmorillonite earth.

[0055] Preparation example of surface-modified silicon nitride

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of wear-resistant materials, and particularly discloses a polyurethane elastomer material as well as a preparation method and application thereof. The polyurethane elastomer material is prepared from the following raw materials: polyester polyol and / or polyether polyol, isocyanate, a foaming agent, a chain extender, silicon nitride and modified montmorillonite, the modified montmorillonite is obtained by organically modifying common montmorillonite with acrylamide; the preparation method comprises the following steps: mixing and stirring the polyester polyol and / or polyether polyol and isocyanate to obtain a mixture, mixing and stirring the remaining raw materials to obtain a mixture, adding the mixture into the mixture while stirring to obtain a base material, banburying the base material at 150-200 DEG C for 5-10 minutes to obtain a sizing material, and carrying out compression molding on the sizing material to obtain the polyurethane elastomer material. The polyurethane elastomer material provided by the invention has excellent wear resistance.

Description

technical field [0001] The present application relates to the field of wear-resistant materials, and more particularly, to a polyurethane elastomer material and its preparation method and application. Background technique [0002] Polyurethane elastomer materials have many excellent properties, such as high modulus, high strength, excellent abrasion resistance, chemical resistance, hydrolysis resistance, high and low temperature resistance and mildew resistance. These good properties make polyurethane materials widely used in many fields such as shoe materials, cables, clothing, automobiles, medicine and health, pipes, films and sheets. [0003] And the performance of polyurethane elastomer material is between plastic and rubber, oil resistance, wear resistance, low temperature resistance, aging resistance, high hardness, elasticity, usually used as the raw material of wear-resistant soles and often used as the raw materials of wear-resistant soles. [0004] But generally s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/06C08L75/04C08L83/04C08K9/04C08K3/34C08K9/06C08K3/22C08J9/04A43B13/04
CPCC08J9/009C08J9/0066C08J9/04C08J9/0061A43B13/04C08J2375/06C08J2375/04C08J2483/04
Inventor 陈金水陈杉培陈贵强陈一木陈碧梅陈文锋陈文平
Owner 锋特(福建)新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com