Orthopedic casting articles containing backings having water soluble binders

A water-soluble adhesive and backing technology, applied in bandages, absorbent pads, medical science, etc., can solve the problems of expensive manufacturing costs, and achieve the effects of excellent specific strength, excellent tactility, and low tensile elongation

Inactive Publication Date: 2001-01-31
3M CO
View PDF16 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these materials are not as compressible as plaster, can coat fin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Orthopedic casting articles containing backings having water soluble binders
  • Orthopedic casting articles containing backings having water soluble binders

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Carded nonwoven fibrous backing containing water-soluble binder

[0043] A non-oriented double doffer card (Dulmen, Germany, Hergeth Hollingsworth, model WZM / K5-d2-R2) was used to convert different types of fiber materials into various fiber fabric backings of non-woven fabric structure. The fibers were weighed in batches and mixed by hand before being placed in the fiber opening unit located ahead of the Hergeth card. The resulting backing consists of a uniform mat of loose fibers highly oriented in the machine direction with little or no dimensional stability or tensile strength. The fiber materials used, varying in composition, structure, denier, fiber length and basis weight, are listed in Table 1A. High tenacity (HT) straight Minifiber polyester (PET) was passed through a Cadette 500 fiber opener (Laroche Co., France) before being fed into the fiber opening unit.

[0044] Following the carding step, the aqueous binder solution was applied to the nonwoven fabric b...

Embodiment 2

[0050] Microcreped nonwoven and knitted backings with water soluble binder

[0051] Table 2A

[0052]As shown in the results in Tables 2B and 2C, all microcreped nonwoven and knitted fabric backing samples (with and without PVP binder) imparted high dry tensile strength to the material (force at break greater than about 4200 gf / cm width) and high wet tensile strength (force at break greater than about 2900 gf / cm). Additionally, the addition of PVP to the backing samples greatly increased the force required to stretch the fabric, based on the dry tensile strength results. For example, it was measured that the micro-creped SONTARA 8043 backing without PVP adhesive required a force of 17.2 grams per centimeter width when the extensibility was 4%, while that with PVP adhesive increased to 172. 3 gf / cm. Thus, in subsequent processing, such as winding and unwinding of rolls of the backing during resin application, it is expected that the elongation of the fabric backin...

Embodiment 3

[0054] Fabric backing with adhesive and hardenable resin

[0055] (Orthopedic casts and casts)

[0056] table 3

Polyurethane prepolymer resin composition

components

Element

Parts (weight)

Isocyanate

Component A

ISONATE 2134L Polyisocyanate (Dow Chemical)

58．91

Benzoyl chloride (stabilizer)

0．05

Subtotal

58．96

Polyol

Component B

NIAX PPG 725 Polypropylene Oxide Polyol (Pennsylvania,

Newton Square, Arco Chemical Co. ,)

24．99

NIAX PPG 425 Polypropylene Oxide Polyol (Pennsylvania,

Newton Square, Arco Chemical Co. ,)

9．90

DB-100 defoamer (Dow Chemical)

0．18

Arno Antioxidant (Shell Chemical Co.)

0．48

Pluronic F-108(BASF)

3．99

2,2'-Dimorpholinodiethyl ether catalyst (Texas,

Austin, Huntsman Chemical)

1．50

Subtotal

41．04

total

100．0

[0057] A dry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention describes an orthopedic casting article containing a fibrous backing stabilized with a water soluble binder and having a hardenable material applied thereto. The present invention also describes methods of making and using such orthopedic casting articles.

Description

field of invention [0001] This invention relates to materials for orthopedic castings, and more particularly to orthopedic castings such as belts and splints comprising a fibrous backing set by a water-soluble binder, wherein the fibrous backing comprises a hardenable material. background of the invention [0002] A number of orthopedic casting materials are known in the art for immobilizing broken or injured limbs. Among them, the first material developed for this purpose was the plaster of Paris bandage, which has good formability and palpability for fine bone structures, but it has many disadvantages, including low specific strength, and slow formation of strength. The cast material was recently developed to solve the problems associated with plaster of paris bandages. For example, knitted fiberglass fabrics coated with water-curable polyisocyanate prepolymer resins have been developed, which have greater specific strength and improved air permeability. However, these m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/07A61L15/12
CPCA61L15/12C08L29/04C08L33/26C08L75/04
Inventor M·D·德尔莫P·E·汉森
Owner 3M CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap