Separator plate felt for plumbous acid battery and preparation method thereof

A lead-acid battery and separator technology, applied in the field of lead-acid battery separator felt, can solve the problems of unsatisfactory mechanical strength and vibration resistance of the lead-acid battery separator, and achieve good acid resistance, uniform thickness, and strong starting ability Effect

Inactive Publication Date: 2007-08-22
SINOMA SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is the unsatisfactory mechanical strength and vibration resistance of the existing lead-acid battery separator, and it provides a new type of lead-acid battery separator felt and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] 1. Wire drawing process section: first set the running speed of the wire drawing furnace at 2 to 3 m / s, and the rotational speed of the drum at 24 to 30 m / s; meanwhile, mix the polyacrylate solution with a solid content of 50% and water at 1 : The ratio of 1.2 is made into solution 40kg;

[0019] Fiberglass consists of 5 # The medium-alkali glass balls are melted and drawn to form glass fibers, and the diameter of the fibers is between 10-15mm; the final fiber weight is about 55-60kg.

[0020] While forming fibers, the polyacrylate solution is evenly sprayed on the glass fibers. After the amount of fibers is reached, a concentrated felt is formed. At this time, the concentrated felt is cut along the axial direction of the roller and spread on a platform. superior.

[0021] 2. Drafting process section: stretch the concentrated felt on the platform horizontally along the cutting direction, and the width of the felt after drafting reaches 1.8-2.3 meters wide.

[0022] 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a baffle plate felt of a lead storage battery, characterized in that it is made by continuous glass fiber and adhesive through large roller process, where the continuous glass fiber content is 85-90 (mass)% and the adhesive content is 10-15 (mass)%. The steps are as follows: (1) making basic glass balls in a glass fiber state through a fusing-wiredrawing device, and at the same of forming fiber by wiredrawing, uniformly spraying polyacrylate solution on the glass fiber; and after forming a condensed felt, slicing off the condensed felt along the axis of the roller and spreading it on a platform; (2) transversely drawing the condensed felt on the platform in the cutting direction; (3) at the same time of drawing, drying the drawn felt between 180 deg.C and 200 deg.C; (4) after all the felt is dried, rolling the felt and cutting it into parts. The baffle felt can make the baffle posses the characters of flat surface, strong absorbing ability, good acid resistance, uniform thickness, fewer potassium permanganate reducing matter, etc.

Description

technical field [0001] The invention relates to a base material of a lead-acid battery separator, in particular to a novel lead-acid battery separator felt. Background technique [0002] The base material of the traditional lead-acid battery separator is ultrafine microfiber, which has poor mechanical strength. In addition, the separator will cause the active material to fall off due to vibration during use, so the shock resistance is also poor, which affects the lead-acid battery. lifespan. [0003] At present, there is a kind of lead-acid battery composite separator, which is made of fixed-length glass fiber as the base material and PVC or rubber. Its mechanical and shock resistance performance is improved compared with ultra-fine fiber separator. The service life of the plate-assembled lead-acid battery is 15%-20% higher than that of the ultrafine microfiber separator plate-assembled lead-acid battery. Contents of the invention [0004] The technical problem to be sol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/14C09J133/08C03B37/01D04H17/00H01M50/44H01M50/446H01M50/489
CPCY02E60/12Y02E60/10
Inventor 徐赟宋煜
Owner SINOMA SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com