Repairing type lubricant additive and its preparation method

A lubricating oil additive and additive technology, which is used in lubricating compositions, thickeners, petroleum industry, etc., can solve the problems of lubricating oil body deterioration, body corrosion, aggravating friction and wear, etc.

Inactive Publication Date: 2002-11-20
TIANJIN UNIV
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the added copper and nickel are high-energy metals without any protection on the surface (otherwise it does not need to be operated in a vacuum), they are often used as catalysts in the petrochemical industry. Therefore, during use, the lubricating oil body will deteriorate and the acidity will increase. cause corrosion
Unprotected agglomerated particles will form large hard agglomerates that cannot be dispersed in the oil, which not only cannot ensure suspension but also aggravate friction and wear

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Repairing type lubricant additive and its preparation method
  • Repairing type lubricant additive and its preparation method
  • Repairing type lubricant additive and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Embodiment 1. take by weighing aluminum 0.55g, titanium 0.25g of 10-200nm: zinc 0.05g: tin 0.15g, base oil or 98g; dispersing additive T154 1g, put into same container, carry out mechanical stirring and mixing 20 minutes; put the mixture together with the container into an ultrasonic oscillator for 20 minutes of ultrasonic vibration, and obtain the repairing lubricant additive.

Embodiment 2

[0025] Embodiment 2. take by weighing aluminum 2.6g, titanium 1g: zinc 0.2g: tin 0.2g, finished lubricating oil 94g that particle size scale is 10-200nm; Dispersing additive T202 2g, put into same container, carry out mechanical stirring and mixing 30 Minutes; put the mixture together with the container into an ultrasonic oscillator for 30 minutes of ultrasonic oscillation to obtain a repairing lubricating oil additive.

Embodiment 3

[0026] Embodiment 3. take by weighing aluminum 6.5g, titanium 1.5g: zinc 1.5g: tin 0.5g, finished lubricating oil 88g that particle size scale is 10-200nm; Dispersing additive T101 2g is put into same container, carries out mechanical stirring and mixing After 40 minutes, put the mixture together with the container into an ultrasonic oscillator for 40 minutes of ultrasonic vibration to obtain a repairing lubricating oil additive.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The present invention discloses a repairing type lubricating oil additive and its preparation method. Its composition includes 1-10% of aluminium, titanium, zinc and tin granules whose grain size is 10-200 nm, their weight ratio of 5.5-6.5:1.5-2.5:0.5-1.5:0.5-1.5, 88-98% of basis oil for finished product lubricating oil and 1-2% of dispersing additive. Its preparation method incldues the following steps: placing the above-mentioned all the materials into same container, mechanically-stirring and mixing for 20-40 min., placing the mixture and said container into an ultrasonic oscillator to make ultrasonic oscillation for 20-40 min. so as to obtain the invented lubricating oil additive with good repairing effects.

Description

technical field [0001] The invention relates to a lubricating oil additive, in particular to a repairing lubricating oil additive based on nanometer metal particles and a preparation method thereof. Background technique [0002] In mechanical equipment, where there is relative movement, such as various friction pairs, friction will occur, and the accumulation of friction will cause wear on the surface of the friction pairs. The existence of friction consumes extra energy and reduces mechanical efficiency. The occurrence of wear and tear will gradually cause the parts to lose their dimensional accuracy and fail, resulting in the scrapping of equipment. For internal combustion engines, the occurrence of wear and tear will also lead to a decrease in the sealing of the cylinder, resulting in insufficient fuel combustion, which will pollute the environment when it is discharged into the air. Therefore, in the operation of mechanical equipment, vari...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M113/06
Inventor 柳刚秦伯雄范荣焕孙月海封云
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap