Catalyst for hydrorefining petroleum waxes and its prep.

A hydrofining and catalyst technology, which is applied in petroleum wax refining, etc., can solve the problems of insufficient metal dispersion and low hydrofining activity, achieve high hydrofining reaction activity, improve hydrofining activity, and high concentration Effect

Inactive Publication Date: 2003-10-15
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this method is that the amount of metal dispersed on the carrier is not high enough, only 12.5-19.1w% (based on MoO 3 count), so the activity of hydrofining is not high
This method has the same disadvantages as USP 4,186,078

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1(1), γ-Al 2 o 3 Preparation of vector

[0033] Weigh 200g of alumina monohydrate dry rubber powder (containing 2w% alumina trihydrate), add 3.0g KCl, 4.0ml H 3 PO 4 , 155ml 3% HNO 3 and a moderate amount of H 2 O. Mix well, knead into a plastic shape and extrude into clover strips. After air drying overnight, it was dried at 110°C for 2 hours.

[0034] Place the dried sample in a high-temperature furnace, raise the temperature to 200°C at a rate of 3°C per minute, and roast at this temperature for 1.0 hour. Then, the temperature was raised to 488° C. at a rate of 3° C. per minute, and was roasted at a constant temperature at this temperature for 2.0 hours, and then the temperature was raised to 600° C. at a rate of 3° C. per minute, and roasted at a constant temperature at this temperature for 2.0 hours. (2), preparation of Mo-Ni-P solution

[0035] Dissolve 15ml of phosphoric acid (85%) in 600ml of water. The solution was a...

Embodiment 2

[0039] Same step as Example 1, but γ-Al 2 o 3 The final firing temperature was changed from 600°C to 720°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The preparation process of petroleum wax hydrorefining Mo-Ni-P / Al2O3 catalyst includes preparing new-type gamma-Al2O3, on the surface of which, the chemical metal dispersing amount is 60-120 % higherthan on the surface of gamma-Al2O3 prepared via common process; introducing two kinds of additives to increase the specific surface area and pore size of the gamma-Al2O3; preparing Mo-Ni-P solution with high metal concentration and high stability; soaking gamma-Al2O3 with the solution at room temperature, filtering, stoving, roasting and other steps.

Description

1. Technical field [0001] The invention relates to a hydrofinishing catalyst and a preparation method thereof, in particular to a highly active petroleum wax hydrofinishing catalyst and a preparation method thereof. 2. Background technology [0002] Petroleum wax usually contains a small amount of harmful substances, such as certain aromatic compounds harmful to the human body and certain colored and unstable components. The main purpose of petroleum wax hydrofining is to remove the colored, unstable and harmful substances contained in petroleum wax by hydrogenation. Therefore, there is a need for an efficient catalyst. The catalyst is required to have both high hydrogenation saturation performance and high ability to remove aromatic organic compounds. [0003] Petroleum wax hydrorefining catalysts mainly use metal elements of Group VIII (Ni or Co) and Group VIB (Mo or W) as active components, and γ-Al 2 o 3 or SiO 2 -Al 2 o 3 as the carrier. It is generally believed...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10G73/44
Inventor 罗锡辉何金海
Owner CHINA PETROLEUM & CHEM CORP