Target directivity adsorption type activated carbon fiber material and preparation method and bolt shape products
A technology of activated carbon fiber and products, which is applied in the field of targeted adsorption activated carbon fiber materials and its preparation and suppository products, can solve the problems of toxic side effects, stillbirth, neonatal mental retardation, etc., and achieve good biocompatibility, high absorption Effect of desorption speed and high adsorption capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] Embodiment 1: take viscose-based fiber as raw material hydrophilic activated carbon fiber and preparation method thereof
[0033] The 1000-denier viscose-based fiber is spun into a cloth with a density of 40 (yarn longitude) and 2 up and 2 down (double-sided weaving) by special machinery. Fully wash the non-woven felt with hot water or boiling water at 40-100°C for 30 minutes, then impregnate copper oxide and zinc chloride catalysts and dry. Under the condition of air medium and 200°C, pre-oxidize for 100 minutes; under the protection of inert gas, carbonize continuously at 850°C for 100 minutes to obtain carbon fibers; activated into hydrophilic activated carbon fibers. Control the pore structure by controlling the activation speed and activation time, that is, control the amount of water vapor during activation to about 50Nm 3 / h (Note: m 3 / h is the unit of the amount of water vapor, N represents the water vapor under the protection of nitrogen, the general writin...
Embodiment 2
[0035] Embodiment 2: take polyacrylonitrile fiber as the hydrophilic active carbon fiber of raw material and preparation method thereof
[0036] The same method as in Example 1 was used to prepare the hydrophilic activated carbon fibers of the present invention, except that the viscose-based fiber filaments were replaced with polyacrylonitrile fiber filaments. Its C weight percentage content is determined to be 92%, and the specific surface area of activated carbon fiber is 1250m 2 / g, the pore volume is 0.75ml / g. Its pore structure and surface properties are shown in Table 2 below.
[0037] Diameter range ()
Embodiment 3
[0038] Embodiment 3: the preparation of tampon product of the present invention:
[0039] Select a piece of hydrophilic activated carbon fiber (cloth shape) of the present invention prepared by the method of Example 1, which is similar in size to an ordinary sanitary napkin, and compress and fold it according to the female physiological structure, and its specification is the diameter Between (12-15) mm (diameter) - length (45-55) mm.
PUM
Property | Measurement | Unit |
---|---|---|
iodine adsorption value | aaaaa | aaaaa |
specific surface area | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com