Self-crosslinked aqueous traffic paint and method for using same

A self-crosslinking and road marking technology, applied to road signs, roads, roads, etc., can solve the problems of affecting the service life of road markings, insufficient non-ionization, microcoagulation, etc., and achieve good calcium ion stability and good mechanical stability , Improve the effect of drying speed

Active Publication Date: 2006-01-18
阿克苏诺贝尔功能涂料(常州)有限公司
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the insufficient deionization of amine-containing polymers in the coating preparation process, phenomena such as increased viscosity, microcoagulation, and agglomeration are prone to occur during paint production or storage. Poor water resistance and stain resistance, the paint film becomes soft in rain or high temperature, causing the paint film to fall off and affecting the service life of road signs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1、 Embodiment 2 and Embodiment 3

[0026] 1. See Table 1 for the formula of self-crosslinking water-based road marking paint

[0027] raw material name

Dosage (parts by weight)

raw material name

Dosage (parts by weight)

implement

example 1

implement

Example 2

implement

Example 3

implement

example 1

implement

Example 2

implement

Example 3

R-252

/

34.69

/

HX-6050

0.16

0.16

0.24

R-262

/

/

33.30

SN-defoamer

318

0.32

0.32

0.42

R-242

34.69

/

/

distilled water

2.0

2.0

2.0

HF-100

0.35

0.35

0.32

Methanol

1.59

1.59

1.59

Tioxide TR92

7.95

7.95

7.95

Alcohol Ester-12

1.30

1.30

1.30

wollastonite

34.62

34.62

31.21

Rhodoline DP-270

1.56

1.56

1.72

Silica powder

4.88

14.88

19.55

Hydropalat 436

0.58

0.58 ...

Embodiment 4

[0050] 1. The formula of special two-component water-based epoxy paint is shown in Table 2

[0051] A component

B component

raw material name

Dosage (parts by weight)

raw material name

Dosage (parts by weight)

R-262

32.8

GCA01

20

GEM01

49.2

distilled water

80

Alcohol Ester-12

1.64

distilled water

16.36

[0052] Note ① R-262 self-crosslinking silicone acrylic emulsion, solid content 49%, Wenzhou Tiancheng Chemical Co., Ltd.

[0053] product;

[0054] ②GEM01 epoxy emulsion, product of Shanghai Lujia Water-based Coatings Co., Ltd.;

[0055] ③Alcohol ester-12 coalescence aid, product of Tianjin Beihui Chemical Co., Ltd.;

[0056] ④ GCA01 curing agent, product of Shanghai Lujia Water-based Coatings Co., Ltd.

[0057] 2. Preparation of special two-component water-based epoxy paint

[0058] Component A: According to the formula in Table 2, under high-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is self-linking water thinned road mark paint and its preparation and usage. The road mark paint is storage stable and has solid content of at least 75 %, and anionic self-linking silicone propylene emulsion as main material. Specifically, it consists of anionic self-linking silicone propylene emulsion 20-50 weight portions, distilled water 1-5 weight portions, methanol 1-5 weight portions, filming assistant 1-5 weight portions, dispersant 1-3 weight portions, moistener 0.1-1 weight portions, disinfecting mildew inhibitor 0.1-0.5 weight portions, defoaming agent 0.1-0.5 weight portions, and pigment and stuffing 20-80 weight portions. It may be painted to road directly or on primer, and may be used widely for different kinds of road.

Description

technical field [0001] The invention relates to a self-crosslinking water-based road marking paint and its preparation and application method. Background technique [0002] With the development of the national economy, the total mileage of my country's highways has reached 1.25 million kilometers in the 21st century. The vigorous development of road construction has promoted the development of road marking paint. About 90% of road marking paints currently used are solvent-based paints that dry at room temperature. This type of road marking paint contains volatile organic compounds (hereinafter referred to as VOC) as high as 650g / l. In the process of making paint or drawing road signs, the volatilization of VOC will cause harm to operators and the environment; there is also a kind of hot-melt road marking paint. Although the VOC content is low and the durability is good, it needs to be heated and melted during construction. It is very difficult, and the old coating must be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/00E01F9/04
Inventor 包启宇王雄戴红艳陈鲍芬曹剑科
Owner 阿克苏诺贝尔功能涂料(常州)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com