Biologic waterproof glue and usage

A waterproof adhesive and biological technology, applied in adhesives, natural rubber adhesives, acidic copolymer adhesives, etc., can solve the problems of no waterproof coating, etc., and achieve good alkali corrosion resistance, good water impermeability, and high fracture The effect of elongation

Inactive Publication Date: 2006-02-01
赵春发 +1
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But looking at the existing waterproof coatings as a whole, no matter how the formula changes, there is no waterproof coating based on biological materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biologic waterproof glue and usage

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] 40 kg of water, 5 kg of glutinous rice, 6.5 kg of polyvinyl alcohol, 0.5 kg of dioctyl phthalate, and 48 kg of ethylene-vinyl acetate emulsion.

[0057] Put glutinous rice and water into the reaction kettle and stir, add polyvinyl alcohol to boil and dissolve, stir to form a paste, add ethylene-vinyl acetate emulsion when the temperature is cooled to normal temperature, stir evenly, and finally filter to obtain biological waterproof glue.

[0058] The biological waterproof glue of the invention can be used for waterproofing, moisture-proofing and anticorrosion of wood; for anticorrosion of metal; and as a bonding agent for ceramics, glass and plastic products.

Embodiment 2

[0060] 16 kg of water, 1.5 kg of glutinous rice, 35 kg of acrylic acid emulsion, 7 kg of dioctyl phthalate, 15 kg of light calcium carbonate, 1.3 kg of polyvinyl alcohol, and 24.2 kg of ethylene-vinyl acetate emulsion.

[0061] Put glutinous rice and water into the reaction kettle and stir, add polyvinyl alcohol to boil and dissolve, stir to form a paste, add ethylene-vinyl acetate emulsion, dioctyl phthalate, acrylic acid emulsion and light The calcium carbonate raw material is stirred evenly at high speed, and finally filtered to obtain biological waterproof glue.

[0062] The biological waterproof glue of the present invention can be used for waterproofing of cement roofs, exterior walls, bathrooms, and basements in houses; for wood waterproofing, moisture-proofing, and anticorrosion; for repairing cracks in ointment, asphalt, and cement surfaces.

Embodiment 3

[0064] 40 kg of water, 5 kg of glutinous rice, 6.5 kg of polyvinyl alcohol, 0.5 kg of dioctyl phthalate, 35 kg of natural rubber powder, and 13 kg of ethylene-vinyl acetate emulsion.

[0065] Put the glutinous rice and water into the reaction kettle and stir, add polyvinyl alcohol and boil to dissolve, stir for about 5 hours to get a paste, add natural rubber powder when the temperature drops to about 30°C, stir at high speed for about 30 minutes, then add ethylene - Vinyl acetate emulsion, dioctyl phthalate, stirred evenly at high speed, and finally filtered to obtain biological waterproof glue.

[0066] The biological waterproof glue of the present invention can be used for waterproofing of cement roofs, exterior walls, bathrooms, and basements in houses.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A biologic water-proof adhesive for building, wood, metal, ceramic, glass, etc is prepared from glutinous rice, water, ethene-vinyl acetate emulsion, dioctyl phthalate, PVC, tung oil, acrylic emulsion and natural rubber. Its advantages are high weatherability, adhesion, tension strength, elongation percentage for breaking and resistance to water, acid and alkali.

Description

technical field [0001] The invention belongs to the field of waterproof coatings, in particular to biological waterproof glue and its application. Background technique [0002] At present, ointment and asphalt materials are mostly used to repair cracks on cement pavement in China, but from the perspective of use effect, their waterproof effect is poor, so that the roadbed cannot be protected for a long time; waterproof membranes used for roof waterproofing include LHG, APP, SBS, ZYP, etc., paint waterproof series include LIP, IS, BR, JS, etc., but these waterproof materials are not easy to construct and difficult to operate in the complex parts of the construction, and there are natural weathering of waterproof materials, cracks are not durable, and water resistance is poor. Due to the large temperature changes, after several freeze-thaw cycles, the substrate and the substrate are easily separated, resulting in hollowing, joints are easy to crack, and there are many water ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J133/02C09J107/00C09J9/00
Inventor 赵春发俞胤合
Owner 赵春发
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap