Flexible vinyl dedicated to wire and cable

A soft polyvinyl chloride, wire and cable technology, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of partial waste of antioxidants, influence on mechanical and physical properties, influence of tensile strength retention rate on thermal stability time, etc. Achieve the effects of easy processing, excellent heat resistance and low volatility

Active Publication Date: 2006-04-19
CHANGSHU ZHONGLIAN PHOTOELECTRICITY NEW STUFF +1
View PDF3 Cites 38 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Japanese patents JP2001-266649A and JP10-306185A and JP9-132689A all disclose polyvinyl chloride compositions with electric wires. In the compositions of the three documents, antioxidants seem to be partial, but the applicant believes that polyvinyl chloride as electric wires Whether the ethylene composition contains an antioxidant is related to the heat resistance of the product. Specifically, it will affect the retention rate of tensile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flexible vinyl dedicated to wire and cable

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0039] Example 1:

[0040] The degree of polymerization is 100 parts of 1300PVC resin;

[0041] 50 parts of tetraoctyl pyromellitic acid (TOPM);

[0042] 10 parts of lead cyanurate;

[0043] Antioxidant B225 0.8 parts;

[0044] 0.2 part of antioxidant DLTP;

[0045] 30 parts of calcium carbonate;

[0046] 1 part of barium stearate.

Example Embodiment

[0047] Example 2:

[0048] The degree of polymerization is 30 parts of 1300PVC resin;

[0049] The degree of polymerization is 70 parts of 2500PVC resin;

[0050] 90 parts of tetraoctyl pyromellitic acid (TOPM);

[0051] 10 parts of lead cyanurate;

[0052] Antioxidant B225 0.8 parts;

[0053] 0.2 parts of antioxidant DLTP;

[0054] 30 parts of calcium carbonate;

[0055] 1 part of barium stearate.

Example Embodiment

[0056] Example 3:

[0057] Antioxidant B225 0.5 parts;

[0058] 0.1 part of antioxidant DLTP;

[0059] The remaining amounts are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Polymerizationaaaaaaaaaa
Polymerizationaaaaaaaaaa
Elongation at breakaaaaaaaaaa
Login to view more

Abstract

A soft polyviny chloride plastic for electric transmission line or cable is proportionally prepared from PVC resin, refractory plasticizer, stabilizer, antioxidizing agent, filler and lubricant. Its advantages are high refractory class (120deg.C), long high-temp stabilizing duration (300 min), and low high-temp volatilization.

Description

technical field [0001] The invention belongs to the wire and cable insulating material among industrial polymer materials, and more specifically relates to a special heat-resistant soft polyvinyl chloride plastic used for wires and cables. Background technique [0002] The copper conductor of the wire and cable needs to transmit electric energy and load a certain amount of current, and at the same time, the copper wire generates a higher temperature during operation. When the cross-sectional area of ​​the copper conductor is constant, the larger the current transmitted, the higher the temperature generated, so there is a heat resistance requirement for the insulation material of the wire and cable; according to the size of the transmitted current, different temperatures are generated, so the insulation Materials have different heat resistance requirements, so that they can maintain good mechanical and physical properties under long-term high temperature to meet the requireme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08K5/56H01B3/30
Inventor 张尔梅王俊刚张国强计文龙朱俊张健
Owner CHANGSHU ZHONGLIAN PHOTOELECTRICITY NEW STUFF
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap