Antioxidative method for superfine chemical nickel powder

An ultra-fine chemical and anti-oxidation technology, which is applied in the field of anti-oxidation, can solve problems such as spontaneous combustion, and achieve good effect and simple operation

Inactive Publication Date: 2006-08-16
JINCHUAN GROUP LIMITED
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the anti-oxidation technology of powder in the existing technology is generally post-processing of powder output, such as follow-up anti-oxidation technology of copper powder and copper coated powder, silver powder and silver coated powder, etc., due to ultrafine chemical nickel powder The activity of the powder is ver

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Heating to the specified temperature in the closed system reduction furnace, and then reducing with hydrogen, after the reduction is completed, start to cool down, when the temperature drops to 160°C, open the valve of the nitrogen cylinder, adjust the valves of the hydrogen and nitrogen cylinders, and use the flow meter to indicate When the flow ratio of nitrogen and hydrogen is 4:1, continue to cool down to 80°C, close the valve of the hydrogen cylinder, and only pass nitrogen. When the temperature in the closed system drops to 45°C, stop nitrogen flow, open the closed system, and take out the The reduced ultra-fine nickel powder is quickly put into a sealed bag, filled with nitrogen and sealed, and taken out after 24 hours of storage. The appearance of the ultra-fine nickel powder is a loose black powder, and the hydrogen loss value is less than 2.0%.

Embodiment 2

[0014] Heating to the specified temperature in the reduction furnace of the closed system, and then reducing with hydrogen, after the reduction is completed, start to cool down, when the temperature drops to 140°C, open the valve of the nitrogen cylinder, adjust the valves of the hydrogen and nitrogen cylinders, and use the flow meter It is indicated that the flow ratio of nitrogen and hydrogen is 5:1, continue to cool down to 75°C, close the valve of the hydrogen cylinder, and only pass nitrogen, and when the temperature in the closed system drops to 50°C, stop nitrogen, open the closed system, and take out the The reduced ultra-fine nickel powder is quickly put into a sealed bag, filled with nitrogen and sealed, and taken out after 24 hours of storage. The appearance of the ultra-fine nickel powder is a loose black powder, and the hydrogen loss value is less than 2.0%.

[0015] Example 2

[0016] Heating to the specified temperature in the reduction furnace of the closed sys...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An antioxidizing process for the superfine chemical Ni powder includes such steps as preparing superfine chemical Ni powder by using H2 to reduce superfine nickel oxalate in a sealed system, continuously filling H2 to lower temp to 130-160 deg.C, beginning to fill N2 or inertial gas, increasing the flow of N2 or inertial gas while decreasing the flow of H2 until their volume-flow ratio is (4-6):1, cooling to 70-80 deg.C, and continuously increasing the flow of N2 or inertial gas until the flow of H2 is zero. The N2 or inertial gas is adsorbed by the surface of Ni particle to generate a layer of passivated film.

Description

technical field [0001] The invention relates to an anti-oxidation method of superfine chemical nickel powder, which relates to a method for producing superfine nickel powder by a chemical method, in particular to an anti-oxidation method thereof. Background technique [0002] With the rapid development of modern electronics, magnetic materials, conductive paste, catalysts, parts, high-capacity batteries, organic synthesis, aerospace devices and other major industries, the requirements for powder products are getting higher and higher, not only the relative purification of chemical components, Higher requirements are put forward for some physical properties of powder products. With the further development of the modern new material industry, the particle size of the powder tends to be more and more refined. Using nickel salt as raw material, the ultrafine chemical nickel powder with a particle size of less than 10um is produced after reduction with very high activity. In the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F9/22
Inventor 陈自江汪锦瑞段建军陈泞来颜智宏
Owner JINCHUAN GROUP LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap