Road fire-resistant asphalt

A technology for road petroleum asphalt and asphalt, applied in the field of road flame retardant asphalt, achieves the effects of convenient use, less casualties and property losses, and less black smoke

Inactive Publication Date: 2010-07-14
SHENZHEN OCEAN POWER INDUSTRIAL CO LTD
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Domestic research on flame-retardant asphalt is mainly used for building linoleum, and it has not been used in roads.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Road fire-resistant asphalt
  • Road fire-resistant asphalt
  • Road fire-resistant asphalt

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh by weight: 60 parts of heavy traffic road petroleum asphalt AH-70; 8 parts of decabromodiphenyl ether; 20 parts of magnesium hydroxide; 20 parts of aluminum hydroxide; 0.6 parts of coupling agent; 1.5 parts of blending agent; modifier 0.5 servings.

[0030] First, the heavy traffic road petroleum asphalt AH-70 is melted at a constant temperature of 80 °C, and decabromodiphenyl ether, magnesium hydroxide, aluminum hydroxide, coupling agent and blending agent are added to the molten asphalt, and they are added while stirring, so that Each component can be evenly mixed in the asphalt, then add the modifier, while adding the modifier, use a high-speed shearing machine at 1000r / min for 10min to make the modifier melt and swell, and then continue at 5000~ High-speed shearing at 6000r / min for 30min, the modifier gradually becomes thinner under the action of shearing, and finally the fine particles are evenly distributed in the asphalt, thus making the flame retardant asp...

Embodiment 2

[0032] Weigh by weight: 80 parts of heavy traffic road petroleum asphalt AH-70; 3 parts of decabromodiphenyl ether; 5 parts of magnesium hydroxide; 10 parts of aluminum hydroxide; 0.45 parts of coupling agent; 2 parts of blending agent; modifier 1.5 servings. The preparation process is the same as in Example 1.

Embodiment 3

[0034] Weigh by weight: 65 parts of heavy traffic road petroleum asphalt AH-70; 6 parts of decabromodiphenyl ether; 10 parts of magnesium hydroxide; 5 parts of aluminum hydroxide; 0.3 part of coupling agent; 1 part of blending agent; modifier 0.8 servings. The preparation is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
oxygen indexaaaaaaaaaa
oxygen indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses road using inflaming retarding asphalt whose components part by weight are as follows: heavy traffic road petroleum asphalt 60-80, pentabromophenyl ether 3-8, magnesium hydroxide 5-20, aluminum hydroxide 5-20, coupling agent 0.3-0.7, tempering agent 1-3, and modifier 0.5-1.5. While burning it has high oxygen index to form stable charring layer to arise self extinguishing, little lamp black to reduce environment pollution. Thus it has wide application prospect, good socioeconomic performance. The preparing method is simple, effective, economic, convenient, and widely used.

Description

【Technical field】 [0001] The present invention relates to a kind of asphalt, more specifically, the present invention relates to a kind of road flame retardant asphalt. 【Background technique】 [0002] Asphalt is the final product of petroleum refining, and is a cheap and abundant building material widely used in construction for waterproof, moisture-proof, anti-corrosion, rust-proof, anti-leakage, etc. Some of its properties are unmatched by synthetic rubber and synthetic resin. However, asphalt is easy to burn, produces a large amount of black smoke, melts and flows when heated, and has a great fire hazard, and its application is also limited to a certain extent. Therefore, the research on the flame retardancy of asphalt has great practical significance. [0003] With the improvement of road users' requirements for road driving quality, smooth, wear-resistant and low-noise asphalt concrete pavement may replace cement concrete pavement and gradually become the mainstream o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E01C7/18C08K5/06C08L95/00
Inventor 高云龙廖克俭何唯平
Owner SHENZHEN OCEAN POWER INDUSTRIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap