Exposed wall elastic anti-crack putty

An anti-cracking putty and elastic technology, which is applied in the field of elastic anti-cracking putty for external walls, to achieve the effect of good filling batch scraping and excellent adhesion performance

Inactive Publication Date: 2007-06-13
南通甜港材料科技有限公司
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a kind of elastic anti-crack putty for outer wall which has good dynamic crack resistance and is easy to scrape and coat. many deficiencies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] An elastic anti-crack putty for external walls is prepared by mixing 20kg of base material, 65kg of filler and 15kg of auxiliary agent.

[0012] Among them, 20kg of base material contains 15kg of acrylic flexible emulsion and 5kg of EVA emulsion.

[0013] 65kg filler contains 25kg heavy calcium, 25kg cement, 15kg quartz powder.

[0014] 15kg additives include 2kg dioctyl phthalate, 1kg defoamer, 2.1kg thickener, 0.9kg C-12 coalescent, 2.5kg hydroxypropyl methylcellulose, 3kg wood fiber, 3kg polypropylene Fiber, 0.5kg antifungal agent.

[0015] The ratio of the above-mentioned components is not unique, and various elastic anti-cracking putties can be made by adjusting the ratio of the components.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention is related to a kind of elastic crack-resistant putty exterior walls composed by mixing base of 20-30% part, filler of 60-70% part and assistant of 8-20% part by weight. The said base contains flexible acrylic acid emulsion of 12-25% part and EVA emulsion of 5-10% part by weight. The said filler contains heavy calcium of 25-30% part, 25-30% cement and silica flour of 10-20 part by weight. The said assistant contains the following componentsby weight: dioctyl phthalate of 1-3% part, defoaming agent of 1-1.5% part, thickening agent of 2-5% part, emulsive filmogen of 3-5% part, hydroxypropyl methylcellulose of 2.5-3.0% part, woody fiber of 2-5% part, polypropylene fiber of 3-5% part, and mildew preventive of 0.5-1% part. The said putty can be used as the exterior wall coatings of both regular buildings and buildings with higher crack-resistant requirements and its dynamic crack property exceeds the national standard. The said putty can adjust the viscosity of the paste and other workabilities according to different operating requirements by selecting the variety and thickness scale of the filler, adjusting the matched ratios, and also adding proper quantities of water and assistants which satisfy different constructing requirements.

Description

technical field [0001] The invention relates to a putty, in particular to an exterior wall putty, in particular to an exterior wall elastic anti-crack putty. Background technique [0002] A large number of buildings have to do cement mortar plastering layer. Due to the unavoidable hydration and shrinkage of cementitious materials, it will cause cracks in the plaster layer, which will lead to cracks in the decorative coating made by it, which generally directly affects the decorative effect and the life of the coating. Especially if the exterior wall is serious, it will cause rainwater leakage, which is an extremely troublesome problem in the construction industry. In order to solve the above problems, a large amount of paper lime lime mixed with cement mortar has been used in the past for a long time to make the plastering surface layer, but due to the material difference between it and the cement concrete base, the adhesion is not good, and it is prone to hollowing and pee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
Inventor 杨生凤冯金海
Owner 南通甜港材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products