Block polyimide, block polyamide acid imide and use thereof

a technology of block polyamide and imide, which is applied in the field of block polyimide and block polyamic acid imide, can solve the problems of high cost of cyclohexanediamine, inability to maintain precise mount, and likely warpage of circuit substrate, and achieves low cte, high transparency, and moderate solubility.

Inactive Publication Date: 2016-03-17
MITSUI CHEM INC
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0024]According to the present invention, it is possible to provide a block polyamic acid imide having moderate solubility in an aqueous alkaline solution, and a block polyimide obtained by using the same which has high transparency and low CTE.

Problems solved by technology

The substrate is a metal substrate or a substrate having a circuit pattern; and when the difference in coefficient of linear thermal expansion (CTE) between the substrate and the polyimide resin layer becomes large, warpage of the circuit substrate is likely to occur by heat or the like generated in its usage environment.
Such warped circuit substrate is incapable of maintaining precise mount and, thus, there is a demand for reduction of warpage of the circuit substrate caused by heat or the like.
On the other hand, cyclohexanediamine is generally expensive, and thus cost reduction is achieved by combining with other diamines, such as norbornene diamine (NBDA) (see PTLs 2 and 5).

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Block polyimide, block polyamide acid imide and use thereof
  • Block polyimide, block polyamide acid imide and use thereof
  • Block polyimide, block polyamide acid imide and use thereof

Examples

Experimental program
Comparison scheme
Effect test

synthesis example 1

[0124]1,4-Diaminocyclohexane (CHDA (trans ratio>99%), 22.6 g, 0.198 mol) and N-methyl-2-pyrrolidone (NMP, 371 g) as an organic solvent were charged into a 500 mL five-necked separable flask equipped with a thermometer, a stirrer and a nitrogen inlet tube, to thereby dissolve CHDA, followed by stirring. 3,3′,4,4′-Biphenyltetracarboxylic dianhydride (BPDA, 58.8 g, 0.200 mol) in a powdery form was added to this stirred mixture, and the resultant solution was allowed to react while keeping the separable flask in an oil bath kept at 90° C. for 1 hour. The solution was initially heterogeneous, but in accordance with the progress of the reaction, the solution changed to an almost colorless transparent solution, thereby forming a viscous amic acid oligomer solution.

synthesis example 2

[0125]An amic acid oligomer was synthesized in substantially the same manner as in Synthesis Example 1 except that the charged amounts of CHDA and BPDA were changed to: CHDA / BPDA (weight: 22.8 g / 57.7 g, molar ratio: 1.00 / 0.98), and that the charged amount of NMP was changed to 36.7 g.

synthesis example 3

[0126]An amic acid oligomer was synthesized in substantially the same manner as in Synthesis Example 1 except that the charged amounts of CHDA and BPDA were changed to: CHDA / BPDA (weight: 22.8 g / 57.1 g, molar ratio: 1.00 / 0.97), and that the charged amount of NMP was changed to 36.4 g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
temperatureaaaaaaaaaa
Tgaaaaaaaaaa
Login to view more

Abstract

The purpose of the present invention is to provide a block polyamide acid imide having an appropriate solubility in aqueous alkaline solutions, and block polyimides that are obtained using same and have high transparency and a low coefficient of linear thermal expansion (low CTE). This block polyimide comprises blocks configured from repeating structural units represented by formula (1A) and blocks configured from repeating structural units represented by formula (1B).

Description

TECHNICAL FIELD[0001]The present invention relates to a block polyimide and a block polyamic acid imide, and a use thereof.BACKGROUND ART[0002]Polyimides generally have excellent heat resistance, mechanical properties and electrical properties, compared with other general purpose resins or engineering plastics. Therefore, polyimides are widely used for various applications as molding materials, composite materials, electrical / electronic materials, optical materials, and the like.[0003]For example, a circuit substrate, such as an HDD suspension substrate or a semiconductor package substrate, typically has a substrate and a patterned polyimide resin layer. The substrate is a metal substrate or a substrate having a circuit pattern; and when the difference in coefficient of linear thermal expansion (CTE) between the substrate and the polyimide resin layer becomes large, warpage of the circuit substrate is likely to occur by heat or the like generated in its usage environment. Such warpe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(United States)
IPC IPC(8): C08G73/10B32B15/088C08L79/08C09D179/08G03F7/20H05K1/02H05K1/03
CPCC08G73/10C09D179/08C08L79/08B32B15/088G03F7/20H05K2201/0154H05K1/0296B32B2457/08B32B2551/00B32B2457/20B32B2307/206H05K1/0346B32B15/08B32B27/281B32B2307/412C08G73/1042C08J5/18C08J2379/08G03F7/037H01B3/306H05K1/0393H05K3/281C08G73/1082G03F7/11G03F7/322H05K1/0353H05K3/0017
Inventor FUKUKAWA, KENICHIOKAZAKI, MASAKISAKATA, YOSHIHIROURAKAMI, TATSUHIROOKUBO, ATSUSHI
Owner MITSUI CHEM INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap