A method for preparing poly(ether-ether-ketone) rod bar

A technology of polyether ether ketone and polyetherether ketone resin, which is applied in the field of plastic products and profiles, can solve the problems of high mold production costs, etc., and achieve the effects of high dimensional stability, uniform cross-section, and high strength

Active Publication Date: 2009-10-28
长春吉大特塑工程研究有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Polyether ether ketone products used in the above fields are generally manufactured by injection molding, but some products are subject to many molds and high production costs due to their large size and different shapes. However, many users need to use semi-finished products such as polyether ether ketone rods, profiles, plates and sheets to manufacture the required parts and products through mechanical processing. The purpose of this invention is to meet the needs of different users. Out-of-molding method for manufacturing polyether ether ketone rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing poly(ether-ether-ketone) rod bar
  • A method for preparing poly(ether-ether-ketone) rod bar
  • A method for preparing poly(ether-ether-ketone) rod bar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Such as figure 1 In the extrusion production line shown, the polyether ether ketone resin of natural color is melted at 400°C in a single-screw extruder, and the melt is extruded into the mouth die through the head of the extruder, and then directly enters the two-stage cooling and sizing The length of each sizing sleeve is 300mm. As mentioned above, the heat transfer oil is high temperature resistant dibenzyltoluene. The resin density is evenly filled with the die and the sizing sleeve in turn, and in the process of moving forward at a constant speed (corresponding to the rotation speed of the extruder screw, the extrusion speed of the rod is 3-6mm / min), at the first Cooling and sizing at 200°C in the first sizing sleeve, and then cooling and sizing at 120°C in the second sizing sleeve to obtain polyether ether ketone rods with a diameter of D51±1mm.

[0031] After the polyetheretherketone rod is crystallized by gradient cooling and sizing, it is introduced by the tra...

Embodiment 2

[0039] As in Example 1, only the natural color PEEK resin was replaced with black PEEK resin (adding 0.2% by weight carbon black for coloring), and the same method and process were used to obtain black PEEK rods.

[0040] With the method of Example 1, the roundness of the bar prepared in this embodiment is studied, for this reason, the diameter of the bar is measured at 5 different points on the cross section of the bar, and the results are as follows:

[0041] Table 3: Diameter data of polyetheretherketone rods prepared in Example 2:

[0042]

[0043] The data in the table shows that the roundness of the prepared black rod is better and the diameter is more uniform.

Embodiment 3

[0045] As in Example 1, only the natural color polyetheretherketone resin was replaced with green polyether ether ketone resin (adding 0.2% by weight of chrome green for coloring), and the same method and process were used to obtain green polyetheretherketone rods.

[0046] With the method of Example 1, the roundness of the bar prepared in this embodiment is studied, for this reason, the diameter of the bar is measured at 5 different points on the cross section of the bar, and the results are as follows:

[0047] Table 4: Diameter data of polyetheretherketone rods prepared in Example 3:

[0048]

[0049] The data in the table shows that the roundness of the prepared green rod is better and the diameter is more uniform.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention pertains to the plastic product and the profile field thereof, and in particular relates to a method to prepare a PEEK bar by means of extrusion molding. PEEK is put into the feed hopper of an extruder, and is fused to plasticize in the extruder barrel below the degree of 360-400 DEG C, so as to form PEEK melt, which is extruded out by the nose and rod dies. Under the role of back pressure rods with constantly reverse pressure, the melt enters into and permeates the Rod Dies, and then enters into the sizing sets linking with the Rod Dies; The melt goes on formation of products by echelon cooling gradually in the sizing sets, thus the PEEK bar is made. Then the bar is treated by the way of echelon annealing in a tube-type annealing furnace, at last the good crystallized PEEK bar with excellent size stability and against bending is obtained. The PEEK bar produced by the invention is used to the fields of aerospace, electronic and electrical engineering, cars, chemicals, as well as machine, etc., and is used to process all kinds of parts and products needed in these fields.

Description

technical field [0001] The invention belongs to the field of plastic products and profiles thereof, and in particular relates to a method for preparing a polyether ether ketone resin rod through an extrusion molding method. Background technique [0002] Polyether ether ketone resin has the characteristics of high heat resistance, radiation resistance, high impact strength, good wear resistance and fatigue resistance, flame retardancy, and excellent electrical properties. Since its commercialization, it has been widely used in aerospace, automotive, electrical and electronic, chemical, mechanical and medical fields. Polyether ether ketone products used in the above fields are generally manufactured by injection molding, but some products are subject to many molds and high production costs due to their large size and different shapes. However, many users need to use semi-finished products such as polyether ether ketone rods, profiles, plates and sheets to manufacture the requ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C47/12B29C47/90B29C47/92B29C71/02B29K71/00B29C48/30B29C48/90B29C48/92
CPCB29C47/92B29C48/92B29C2948/92704B29C2948/92895
Inventor 姜振华王贵宾吴忠文
Owner 长春吉大特塑工程研究有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap