A kind of modification method of proton exchange membrane for all-vanadium redox flow battery

An all-vanadium redox flow battery and proton exchange membrane technology, applied in fuel cells, regenerative fuel cells, circuits, etc., can solve the problems affecting the electrochemical performance of all-vanadium redox flow batteries, poor vanadium resistance performance, etc., and achieve vanadium ion permeation. The effect of reduced rate, good bonding, uniform cross-section

Inactive Publication Date: 2019-03-19
HARBIN INST OF TECH SHENZHEN GRADUATE SCHOOL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Among them, the proton exchange membrane is one of the most important components of the system. DuPont's product Nafion (perfluorinated ion exchange resin) membrane has excellent electrochemical performance and good chemical stability. Therefore, its It is currently the most widely used proton exchange membrane in the field of vanadium redox flow batteries. However, the vanadium resistance of Nafion proton exchange membrane is poor, and the poor performance of vanadium resistance will directly affect the improvement of the comprehensive performance of proton exchange membrane, so as to affect the performance of all vanadium liquid. Electrochemical performance of flow batteries

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modification method of proton exchange membrane for all-vanadium redox flow battery
  • A kind of modification method of proton exchange membrane for all-vanadium redox flow battery
  • A kind of modification method of proton exchange membrane for all-vanadium redox flow battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Such as figure 1 As shown, embodiment 1 provides a kind of modification method for the proton exchange membrane of all-vanadium redox flow battery, and it comprises the following steps:

[0042] S1. Preparation of submicron ZSM-5 zeolite: first weigh 2.185g of deionized water, add it to 5.463g (the mass ratio of deionized water to tetrapropylammonium hydroxide is 1:2.5) and the concentration is 1.0 mol / L tetrapropylammonium hydroxide (TPAOH) aqueous solution, stirring to form a uniform solution; then weigh 1.093g of silicic acid (that is, the mass ratio of silicic acid to TPAOH is 1:5), and add silicic acid to the above uniform solution; then add 0.044g of sodium metaaluminate (that is, the mass ratio of sodium metaaluminate to silicic acid is 1:25) powder into the above solution, and stir evenly to obtain a milky white solution; then the obtained milky white The solution was stirred for 24 hours to obtain a homogeneous solution, which was transferred to a 100mL Teflon...

Embodiment 2

[0051] The difference between the modification method of a proton exchange membrane used in an all-vanadium redox flow battery provided in Example 2 and the modification method described in Example 1 is that the quality of TPAOH in Step S1 of Example 1 is 5.463 g is replaced by: the mass of TPAOH is 6.555g, that is to say, the mass ratio of deionized water to TPAOH is 1:3, and at the same time, according to the mass ratio of silicic acid to TPAOH is 1:5, sodium metaaluminate and silicic acid The mass ratio is 1:25, add 1.311g silicic acid and 0.052g sodium metaaluminate, other content is all the same as embodiment 1, repeats no more here. The composite proton exchange membrane prepared in Example 2 is numbered A2.

Embodiment 3

[0053] The difference between the modification method of a proton exchange membrane used in an all-vanadium redox flow battery provided in Example 3 and the modification method described in Example 1 is that the quality of TPAOH in step S1 of Example 1 is 5.463 g is replaced by: the mass of TPAOH is 7.648g, that is to say, the mass ratio of deionized water to TPAOH is 1:3.5, and at the same time, according to the mass ratio of silicic acid to TPAOH is 1:5, sodium metaaluminate and silicic acid The mass ratio is 1:25, add 1.530g silicic acid and 0.061g sodium metaaluminate, other content is all the same as embodiment 1, repeats no more here. The composite proton exchange membrane prepared in Example 3 is numbered A3.

[0054] Comparing the properties of the composite proton exchange membranes prepared in Examples 1-3, it was found that the performance of the composite proton exchange membrane prepared in Example 2 was the best. In other words, the performance of the composite ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a modification method of a proton exchange membrane for an all-vanadium redox flow battery, relating to the technical field of batteries. The modification method comprises the following steps: S1, preparation of submicron order ZSM-5 type zeolite: evenly mixing deionized water, tetrapropylammonium hydroxide, silicic acid and sodium metaaluminate, performing a hydrothermal synthesis method to the mixed solution, and then performing centrifugal cleaning and drying, so as to prepare the submicron order ZSM-5 type zeolite; and S2, preparation of a composite proton exchange membrane: preparing the composite proton exchange membrane from the submicron order ZSM-5 type zeolite obtained in the step 1 and a proton exchange membrane solution. The water-absorbing property, ion exchange capacity, proton conductivity and vanadium ion permeability of the composite proton exchange membrane prepared by adopting the modification method are superior to those of an unmodified proton exchange membrane. Compared with the unmodified proton exchange membrane, the vanadium ion permeability of the composite proton exchange membrane is reduced by 11%, and the proton conductivity is improved by 20%.

Description

technical field [0001] The invention relates to a method for modifying a proton exchange membrane used in an all-vanadium redox flow battery, and relates to the technical field of batteries. Background technique [0002] All-vanadium redox flow battery is an electrochemical energy storage system for electric energy storage, which has the advantages of good electrochemical performance, reasonable cost, convenient operation, good safety, and low pollution. The vanadium redox flow battery has a simple structure, mainly composed of positive and negative electrodes, proton exchange membrane, electrolyte storage system and pump system. [0003] Among them, the proton exchange membrane is one of the most important components of the system. DuPont's product Nafion (perfluorinated ion exchange resin) membrane has excellent electrochemical properties and good chemical stability. Therefore, its It is currently the most widely used proton exchange membrane in the field of vanadium redo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01M8/0243H01M8/18
CPCH01M8/0243H01M8/188Y02E60/50
Inventor 武俊伟刘彦辰安德鲁·贝克崔传敏崔彦辉
Owner HARBIN INST OF TECH SHENZHEN GRADUATE SCHOOL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka