Water-based long-acting antirust agent

An antirust agent and long-acting technology, applied in the field of chemical treatment of the surface of metal materials, can solve the problems of many kinds of raw materials and complex preparation methods, etc., and achieve the effects of good solution stability, good protection effect, product and raw material safety

Inactive Publication Date: 2009-10-28
DALIAN SANDAAOKE CHEM
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The non-nitrite water-based antirust agent provided by CN 1530463 (application number 03111171) has got rid of nitrite, but it uses many kinds of raw materials and complicated preparation methods (divided into two components of A and B, heated and melted three times) , reaction), there are many inconveniences in actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0020] Carry out the preparation of antirust agent by following formula (W%):

[0021] Sodium isooctanoate 15.0

[0022] Triethanolamine 8.0

[0023] Boric acid 5.0

[0024] water 72.0

[0025] When preparing, mix the above raw materials at room temperature and stir evenly. The product is light yellow viscous liquid. Stored at 25-30°C for 5 months, no stratification or precipitation. The original color and luster of the metal surface is maintained after the anti-rust treatment of the carbon steel plate, and there is no change in the damp heat test cycle of 500h.

example 2

[0027] Carry out the preparation of antirust agent by following formula (W%):

[0028] Sodium caprate 25.0

[0029] Triethanolamine 12.0

[0030] Boric acid 4.0

[0031] water 59.0

[0032] The preparation is the same as the above example. The product is light yellow transparent liquid. Placed at 35-50°C for 3 months, no stratification or precipitation. The original color of the metal surface is maintained after the antirust treatment of the carbon steel plate, and there is no change in the damp heat test cycle for 4 weeks.

example 3

[0034] Carry out the preparation of antirust agent by following formula (W%):

[0035] Potassium nonanoate 8.0

[0036] Triethanolamine 4.0

[0037] Monoethanolamine: 4.0

[0038] Boric acid 4.0

[0039] water 80.0

[0040] The preparation is the same as the above example. The product is light yellow transparent liquid. Placed at 35-50°C for 3 months, no stratification or precipitation. The original color of the metal surface is maintained after the antirust treatment of the carbon steel plate, and there is no change in the damp heat test cycle for 4 weeks.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A water-based long-acting antirust agent, which is composed of C8~C10 carboxylate (sodium, potassium or ammonium salt, 5.0~30.0%), ethanolamine (one, two or triethanolamine, 5.0~15.0%), boric acid (boric acid or ammonium borate, 3.0-8.0%) polyethylene glycol (8-10 ethylene glycol polymerization degree, 0.0-5.0%). The product is light yellow transparent viscous liquid. The antirust agent can dissolve the raw material in water at normal temperature or under heating. The antirust agent has a good protective effect on general carbon steel and cast iron. When used, no white spots will be formed on the metal surface, no flow marks and the original color of the metal surface will be maintained; there will be no change in the damp heat test period of more than 4 weeks. The anti-rust agent has good stability and can remain stable under high and low temperature conditions without stratification or precipitation. The product and raw materials are safe, and it has no harm to the human body and no pollution to the environment when it is prepared and used. It is an environmentally friendly and pollution-free long-term metal rust inhibitor.

Description

Technical field: [0001] The present invention relates to the field of chemical treatment of the surface of metallic materials (iron and iron alloys). Background technique: [0002] At present, for the antirust treatment of the surface of metal materials (especially for steel), water-based antirust agents used in large quantities are compounded with nitrite as the main agent. Although its antirust effect is good and the price is low, this type of antirust agent has many disadvantages: First, this type of antirust agent has great toxicity, and nitrite is a strong carcinogen, which is harmful to the human body and the environment. There is great danger. In addition, because it is a salt-based substance, it is easy to form white spots on the metal surface after use, which will affect the appearance; it is very sensitive to acid and alkali, so we must pay great attention to the effective concentration of the working fluid used, otherwise it will have the opposite effect. Not on...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23F11/00
Inventor 王明望
Owner DALIAN SANDAAOKE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap