Dye for anisotropic dye film, dye composition for anisotropic dye film, anisotropic dye film, and polarizing device

A dye composition, anisotropic technology, applied in polarizing elements, azo dyes, organic dyes, etc., can solve the problems of poor yield of bonding anisotropic dye films, insufficient heat resistance or light resistance, etc.

Active Publication Date: 2008-06-18
MITSUBISHI RAYON CO LTD
View PDF10 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the conventional anisotropic dye film produced in this way has problems of insufficient heat resistance or light resistance depending on the dye or polymer material used; Membrane yield is poor
[0017] However, the above-mentioned compound is a disazo compound, and a halogen atom is bonded to the triazine ring, so it is easy to decompose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dye for anisotropic dye film, dye composition for anisotropic dye film, anisotropic dye film, and polarizing device
  • Dye for anisotropic dye film, dye composition for anisotropic dye film, anisotropic dye film, and polarizing device
  • Dye for anisotropic dye film, dye composition for anisotropic dye film, anisotropic dye film, and polarizing device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0279] Under stirring, 10 parts of dyes (I-31) exemplified below and 0.2 parts of nonionic surfactant EMULGEN 109P (produced by Kao Corporation) were dissolved in 89.8 parts of water to obtain a dye composition for anisotropic dye film:

[0280]

[0281] On the other hand, prepare a base material, this base material comprises glass base material (75mm * 25mm, thickness 1mm) and polyimide alignment film (polyimide film thickness: about 800 Ȧ) formed on it by silk printing , and pre-rubbed with a cloth. On the substrate thus prepared, the aforementioned dye composition for anisotropic dye film was coated with a bar coater ("No. 3" manufactured by Tester Sangyo Co., Ltd.), followed by natural drying to obtain a film thickness of about An anisotropic dye film of 0.4 μm.

[0282] The X-ray diffraction curve and the in-plane vibration curve of the obtained anisotropic dye film are shown in Figs. 4 and 5, respectively. Fig. 4 shows the results of in-plane measurement from two di...

Embodiment 2

[0286] Under stirring, 10 parts of the following exemplified dye (II-15) were dissolved in 90 parts of water to obtain a dye composition for anisotropic dye film:

[0287]

[0288] In the same manner as in Example 1 except using a bar coater (“No. 2” produced by Tester Sangyo Co., Ltd.), the glass substrate on which the polyimide alignment film was formed was coated with The dye composition for the anisotropic dye film was spread, followed by natural drying to obtain an anisotropic dye film.

[0289] The obtained anisotropic dye film was tested for its molecular lamination period, lamination length, orientation degree of molecular lamination axis, and dichromatic ratio, and the results are shown in Table 1.

[0290] Table 1 demonstrates that the anisotropic dye film of this example has a molecular arrangement suitable for expressing a dichroic ratio and has a high dichroic ratio.

Embodiment 3

[0292] Under stirring, 8 parts of the following exemplified dye (I-1) were dissolved in 92 parts of water to obtain a dye composition for anisotropic dye film:

[0293]

[0294] The anisotropic dye was coated on a glass substrate on which a polyimide alignment film was formed in the same manner as in Example 1, except that a coater (manufactured by Imoto Manufacturing Co., Ltd.) with a gap of 10 μm was used. The dye composition for the film, followed by natural drying, thereby obtaining an anisotropic dye film.

[0295] The obtained anisotropic dye film was tested for its molecular lamination period, lamination length, orientation degree of molecular lamination axis, and dichromatic ratio, and the results are shown in Table 1.

[0296] Table 1 demonstrates that the anisotropic dye film of this example has a molecular arrangement suitable for expressing a dichroic ratio and has a high dichroic ratio.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
absorption wavelengthaaaaaaaaaa
absorption wavelengthaaaaaaaaaa
absorption wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a dye for anisotropic dye film, a dye composition for anisotropic dye film, anisotropic dye film and a polarizing element. The molecular stacking of the anisotropic dye produces a period d of at most 3.445 and a stacking length of at least 105. It is preferable that the anisotropic dye film has a molecular lamination axis orientation degree of at least 85%, a film thickness of at most 30 μm, and is formed by a wet film-forming method. Since it has a molecular orientation suitable for expressing dichroic ratio, it can provide high dichroism. A polarizing element having the anisotropic dye film has excellent heat resistance, light resistance, and polarization performance.

Description

[0001] This application is a divisional application. The international application number of the original application is PCT / JP2004 / 015450, the Chinese national application number is 200480029954.X, and the application date is October 13, 2004. Dyes, Dye Compositions for Anisotropic Dye Films, Anisotropic Dye Films, and Polarizing Elements". technical field [0002] The present invention relates to an anisotropic dye film having high dichroism, such as a polarizer used in a light control device, a liquid crystal device, and a display device of an organic electroluminescent device (OLED), the present invention It also relates to a polarizing element using the anisotropic dye film and a dye composition for an anisotropic dye film for obtaining the anisotropic dye film. In addition, the present invention relates to novel azo dyes for use in anisotropic dye films. Background technique [0003] For LCDs (Liquid Crystal Displays), linear polarizers or circular polarizers are used...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09B31/20C09B31/18C09B67/36G02B5/30
Inventor 米山富雄长谷川龙一佐野秀雄大泉淳一西村政昭门脇雅美
Owner MITSUBISHI RAYON CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com