Zirconium oxide dispersion strengthening palladium-gold alloy and producing method thereof

A palladium-gold alloy and dispersion-strengthening technology, which is applied in the field of zirconia dispersion-strengthened palladium-gold alloy and its production, can solve the problems of high price, large loss of platinum and rhodium, and reduced strength, and achieve corrosion resistance to molten glass and good economical use , the effect of excellent high temperature characteristics

Active Publication Date: 2008-07-09
英特派铂业股份有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The high-temperature durable strength and load-bearing capacity of this alloy exceed Pt-40Rh, and it can be used under high-temperature oxidation conditions, but platinum-rhodium is volatile, the grains are coarsened, the strength is reduced and creep occurs, the service life is limited, and the price is expensive. Large loss of rhodium, high investment and use costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Embodiment one: Pd100%.

[0017] Technical performance: when subjected to the same stress at high temperature, the fracture life is about 0.005 times that of ZGSPt-5Rh.

Embodiment 2

[0018] Embodiment 2: Au1.5%, Pd96.4%, Pt2.0%, Zr0.1%.

[0019] Technical performance: when subjected to the same stress at high temperature, the fracture life is about 30 times that of ZGSPt-5Rh.

Embodiment 3

[0020] Embodiment 3: Au3.5%, Pd92.2%, Pt4.0%, Zr0.3%.

[0021] Technical performance: when subjected to the same stress at high temperature, the fracture life is about 48 times that of ZGSPt-5Rh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a precious metal alloy, in particular to zirconia dispersion strengthening polarium and a method for preparation. According to the technical scheme of the invention, the dispersion strengthening polarium comprises palladium, gold and zirconium, wherein the content of the gold is bigger than 0 and is equal or less than 7 percent, the content of the zirconium is bigger than 0 and is equal or less than 0.7 percent, the allowance is palladium, the zirconium is dispersed in the alloy in the mode of zirconia, and the unit is weight percent. The invention is capable of replacing zirconia dispersion strengthening platinum-rhodium alloy, thereby reducing the fund input and service wear of a production line, greatly reducing the production cost of glass, and increasing the economic benefit.

Description

technical field [0001] The invention relates to a precious metal alloy, in particular to a zirconia dispersion strengthened palladium-gold alloy and a production method thereof. Background technique [0002] This alloy is mainly used in the manufacture of key equipment in glass fiber, electronic glass (CRT, TFT), and optical glass industry. At present, ZGSPt-Rh (zirconia dispersion strengthened platinum-rhodium alloy) is used in these industries, and the composition is rhodium Rh5~10 %, platinum Pt is the balance, zirconium Zr content <0.5%. The high-temperature durable strength and load-bearing capacity of this alloy exceed Pt-40Rh, and it can be used under high-temperature oxidation conditions, but platinum-rhodium is volatile, the grains are coarsened, the strength is reduced and creep occurs, the service life is limited, and the price is expensive. The loss of rhodium is large, and the investment and use costs are high. Contents of the invention [0003] The purpo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C5/04C22C1/02C22F1/14
Inventor 吴显忠
Owner 英特派铂业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com