Process for producing long-chain alkyl-phenyl modified silicone oil

A long-chain alkanephenyl and alkanephenyl technology, which is applied in the field of preparation of long-chain alkanephenyl modified silicone oil, can solve the problems of numerous steps, high cost, and low efficiency

Active Publication Date: 2009-04-08
NINGBO RUNHE HIGH TECH MATERIAL CO LTD
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation of long-chain alkylphenyl modified silicone oil in foreign prior art is obtained by modifying silicone oil by grafting phenyl gene on the basis of methyl silicone oil and long-c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing long-chain alkyl-phenyl modified silicone oil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Product Name: Long-chain alkylphenyl modified silicone oil (RH-1)

[0014] Catalyst: Dissolve 1g of chloroplatinic acid in 200g of isopropanol, take 2.5g;

[0015] Raw materials: Hydrogen-containing siloxane: 150g of 202 hydrogen-containing silicone oil;

[0016] Long-chain carbon olefins: 400g of α-dodecene, purity 99-99.9%;

[0017] Styryl hydrocarbons: α-methylstyrene 78g;

[0018] Process conditions: a reactor with a stirrer, thermometer, heating, cooling, and vacuum device, with a volume of 1000ml; addition reaction process: under an atmospheric pressure, add styrene-based hydrocarbons to the reactor, raise the temperature to 50 ° C, drop The catalyst is added, and after 5 minutes, the hydrogen-containing siloxane is added dropwise. After the dropwise addition, the long-chain carbon olefin is added dropwise. The temperature is controlled at 100° C., and the reaction is carried out for 6 hours. After testing the residual hydrogen content to be qualified, lower th...

Embodiment 2

[0024] Product Name: Long chain alkyl phenyl modified silicone oil (RH-2)

[0025] Catalyst: Dissolve 1g of chloroplatinic acid in 200g of isopropanol, take 2.6g;

[0026] Raw material: Hydrogen-containing siloxane: 200g of 202 hydrogen-containing silicone oil;

[0027] Long-chain carbon olefins: α-dodecene, a total of 500g divided into two parts of 200g and 300g, with a purity of 99-99.9%;

[0028] Styryl hydrocarbons: styrene 100g;

[0029] Process conditions: a reactor with a stirrer, thermometer, heating, cooling, and vacuum device, with a volume of 1000ml; addition reaction process: 200g of long-chain carbon olefins and styrene-based hydrocarbons are added to the reactor at an atmospheric pressure , the temperature was raised to 70°C, the catalyst was added dropwise, the temperature was raised to 90°C, the hydrogen-containing siloxane was added dropwise, and the temperature was controlled at 130°C. After the dropwise addition, 300g parts of long-chain carbon olefins wer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of long-chain alkyl phenyl modified silicone oil including a catalyst, raw materials, technological conditions and an addition reaction technology. In the preparation method, Pt is taken as the catalyst, the technical proposal that hydrogen siloxane, long-chain carbon olefin and styryl hydrocarbon are taken as raw materials for the addition reaction is adopted, and the problems and defects existing in the preparation method in the prior art such as numerous steps, complex process, low efficiency, high cost, long period and unsuitability for mass production are overcome. The preparation method of long-chain alkyl phenyl modified silicone oil realizes the simplification of steps and process for preparing long-chain alkyl phenyl modified silicone oil and achieves the improvement of efficiency, reduction of cost and shortening of period, thus meeting the objective required for mass production.

Description

technical field [0001] The invention relates to the preparation of a lubricating grease base oil, in particular to a preparation method of a long-chain alkylphenyl modified silicone oil used as a release agent, a lubricant and a lubricating additive. Background technique [0002] Long-chain alkyl phenyl modified silicone oil is a new type of advanced mold release agent, lubricant, and lubricating additive. Compared with long-chain alkyl silicone oil, it has higher temperature resistance, higher refractive index, better transparency, and better lubricity. Good, the workpiece can be directly coated and printed without cleaning. It has good compatibility with petroleum hydrocarbons and resins. It is used in occasions that require higher mold release and lubrication performance. It has a wide range of uses. There is no long-chain alkanes in China Experiment or production process of phenyl modified silicone oil. The preparation of long-chain alkylphenyl modified silicone oil in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G77/38C10M107/50C10M155/02C10N40/36
Inventor 易有彬
Owner NINGBO RUNHE HIGH TECH MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap